Fireproof paint for wooden furniture
A technology for fire-resistant paint and wooden furniture, applied in the field of paint, can solve the problems that are difficult to make up, high cost, and the fire-proof effect of fire-proof paint needs to be strengthened, and achieve the effects of convenient use, improved flame-retardant effect, and environmentally friendly raw materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0019] Example 1:
[0020] A fire-resistant paint for wooden furniture, consisting of the following components by weight percentage: epoxy resin 12%, phthalic anhydride 3%, polyacrylamide 5%, high temperature resistant non-gelling egg liquid 1.5%, petroleum 15% %, fatty acid sodium 0.8%, aluminum hydroxide powder 22%, silane coupling agent 0.5, dispersant 1.2%, defoamer 1.5%, thickener 0.6%, pigment 2%, thinner 5%, alkyd resin 4%, loose water margin.
[0021] The particle size of the aluminum hydroxide powder is 400 mesh;
[0022] The method for preparing the high temperature resistant non-gel egg liquid includes the following steps: after adjusting the pH of the egg yolk liquid to alkalescence, adding a neutral protease for enzymatic reaction, then adjusting the pH to acidity, adding carboxypeptidase, and continuing After the reaction, adjust the pH again to alkalescence, add xylose, and finally add enzyme inactivation and carry out Maillard reaction. The specific preparation met...
Example Embodiment
[0030] Example 2:
[0031] A fire-resistant paint for wooden furniture, consisting of the following components by weight percentage: 15% epoxy resin, 2% phthalic anhydride, 8% polyacrylamide, 1% high-temperature non-gelling egg liquid, 18 petroleum %, fatty acid sodium 0.5%, aluminum hydroxide powder 15%, silane coupling agent 0.2%, dispersant 2%, defoamer 1%, thickener 1%, pigment 1%, thinner 8%, alkyd Resin 3%, turpentine water balance.
[0032] The particle size of the aluminum hydroxide powder is 400 mesh;
[0033] The method for preparing the high temperature resistant non-gel egg liquid includes the following steps: after adjusting the pH of the egg yolk liquid to alkalescence, adding a neutral protease for enzymatic reaction, then adjusting the pH to acidity, adding carboxypeptidase, and continuing After the reaction, adjust the pH to alkalescence again, add xylose, and finally add the enzyme inactivation and carry out Maillard reaction. The specific preparation method refe...
Example Embodiment
[0041] Example 3:
[0042] A fire-resistant paint for wooden furniture, consisting of the following components by weight percentage: epoxy resin 8%, phthalic anhydride 5%, polyacrylamide 3%, high temperature resistant non-gelling egg liquid 3%, petroleum 12% %, fatty acid sodium 1%, aluminum hydroxide powder 25%, silane coupling agent 1%, dispersant 0.5%, defoamer 3%, thickener 0.5%, pigment 3%, thinner 3%, alkyd Resin 5%, turpentine water balance.
[0043] The particle size of the aluminum hydroxide powder is 400 mesh;
[0044] The method for preparing the high temperature resistant non-gel egg liquid includes the following steps: after adjusting the pH of the egg yolk liquid to alkalescence, adding a neutral protease for enzymatic reaction, then adjusting the pH to acidity, adding carboxypeptidase, and continuing After the reaction, adjust the pH to alkalescence again, add xylose, and finally add the enzyme inactivation and carry out Maillard reaction. The specific preparation m...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap