Preparation method of thermal conductive film based on graphene polyimide composite sponge precursor

A polyimide precursor, ene polyimide technology, which is applied in the field of preparation of thermal conductive films based on graphene-polyimide composite sponge precursors, achieves perfect thermal conductivity and electrical conductivity, improved mechanical properties, and good electrical conductivity. Effect

Active Publication Date: 2022-01-11
SHENZHEN STRONG ADVANCED MATERIALS RES INST CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above technical problems, the present invention discloses a method for preparing a thermally conductive film based on a graphene polyimide composite sponge precursor, which solves the problems existing in the existing graphene composite film in terms of mechanical properties and electrical and thermal conductivity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of thermal conductive film based on graphene polyimide composite sponge precursor
  • Preparation method of thermal conductive film based on graphene polyimide composite sponge precursor
  • Preparation method of thermal conductive film based on graphene polyimide composite sponge precursor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] A thermally conductive film based on graphene / polyimide composite sponge precursor is prepared by the following steps, and the schematic diagram of the preparation process is as follows: figure 1 Shown:

[0060] 1. Preparation of graphene oxide aqueous solution: measure 20mL graphene oxide slurry, add deionized water; under the condition of stirring speed of 700r / min, after stirring for 60min; and at a frequency of 100KHz, perform ultrasonic treatment for 30min to obtain Graphene oxide aqueous solution.

[0061] Wherein, the concentration of the graphene oxide slurry is 20 mg / mL; the concentration of graphene oxide in the graphene oxide aqueous solution is 5 mg / mL.

[0062] 2. Preparation of polyimide precursor solution:

[0063] Using an electromagnetic stirrer, 1.98g of monomeric diamine diaminodiphenyl ether (ODA) powder was uniformly dispersed in 83mL of polar solvent dimethylacetamide (DMAc) solution; 2.18g of dianhydride was continuously added to the mixed solut...

Embodiment 2

[0083]A thermally conductive film based on graphene / polyimide composite sponge precursor is prepared by the following steps:

[0084] 1. Preparation of graphene oxide aqueous solution:

[0085] Measure 20 mL of graphene oxide slurry, add deionized water; stir for 60 min at a stirring speed of 700 r / min; and perform ultrasonic treatment for 30 min at a frequency of 100 KHz to obtain a graphene oxide aqueous solution.

[0086] Wherein, the concentration of the graphene oxide slurry is 20 mg / mL; the concentration of graphene oxide in the graphene oxide aqueous solution is 5 mg / mL.

[0087] 2. Preparation of polyimide precursor solution:

[0088] Using an electromagnetic stirrer, 1.98g of monomeric diamine diaminodiphenyl ether (ODA) powder was uniformly dispersed in 83mL of polar solvent dimethylacetamide (DMAc) solution; 2.18g of dianhydride was continuously added to the mixed solution in small amounts Pyromellitic anhydride (PMDA) powder, stirred for 5h to make it fully react...

Embodiment 3

[0106] A thermally conductive film based on graphene / polyimide composite sponge precursor is prepared by the following steps:

[0107] 1. Preparation of graphene oxide aqueous solution:

[0108] Measure 20 mL of graphene oxide slurry, add deionized water; stir for 120 min at a stirring speed of 100 r / min; and perform ultrasonic treatment for 60 min at a frequency of 10 KHz to obtain a graphene oxide aqueous solution.

[0109] Wherein, the concentration of the graphene oxide slurry is 20 mg / mL; the concentration of graphene oxide in the graphene oxide aqueous solution is 4 mg / mL.

[0110] 2. Preparation of polyimide precursor solution:

[0111] Using an electromagnetic stirrer, 1.98g of monomeric diamine diaminodiphenyl ether (ODA) powder was uniformly dispersed in 83mL of polar solvent dimethylacetamide (DMAc) solution; 2.18g of dianhydride was continuously added to the mixed solution in small amounts Pyromellitic anhydride (PMDA) powder, after stirring 5h to make it fully r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing a thermally conductive film based on graphene polyimide composite sponge precursor, which comprises the following steps: mixing graphene oxide aqueous solution with polyimide precursor solution to obtain graphene oxide / polyamide acid mixed solution, and then it is frozen to obtain graphene oxide / polyamic acid frozen sponge, which is dried by freeze-drying method to obtain graphene oxide / polyamic acid composite sponge, which is placed in a hot-press reaction furnace and heated by hot-pressing Oxidation pretreatment and mechanical pressure to obtain reduced graphene oxide / polyimide composite film, then vacuum heat treatment and mechanical pressure to obtain graphene / polyimide carbon film, and then placed in a high-temperature graphitization furnace , the graphitization of carbon films was achieved by gradient temperature rise method. By adopting the technical solution of the present invention, the dispersion problem of graphene is improved, and the obtained film has certain flexibility, high mechanical strength, and better electrical and thermal conductivity, and the preparation process is simple.

Description

technical field [0001] The invention belongs to the technical field of composite materials, and in particular relates to a method for preparing a thermally conductive film based on a graphene-polyimide composite sponge precursor. Background technique [0002] Today, with the advancement of science and technology, the lightweight and highly integrated development of modern military equipment is facing increasingly severe thermal management challenges. For example, in electronic weapons, ultra-high-speed aircraft, remote sensing satellites, radars and other equipment, large-scale The high integration of high-power electronic components will cause serious heat concentration problems, which poses a fatal threat to the working stability, safety and reliability of key components of military equipment. At the same time, the complex thermal interface in highly integrated equipment also puts forward unique requirements on the flexibility of thermal management materials. [0003] Wit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/524C04B35/622
CPCC04B35/524C04B35/522C04B35/622C04B2235/6562C04B2235/6567C04B2235/96C04B2235/9607
Inventor 彭庆宇祝越赫晓东
Owner SHENZHEN STRONG ADVANCED MATERIALS RES INST CO LTD