A technology of tempered glass and a manufacturing method, applied in the field of glass processing, can solve the problems of unsatisfactory surface strength and hardness of glass fiber reinforced plastics, easy occurrence of scratches, etc., and achieve the effects of improving hardness, enhancing scratch resistance, and improving mechanical strength

Inactive Publication Date: 2020-02-04
正安鑫旺钢化玻璃有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the surface strength and hardness of glass tempering are not ideal, and it is prone to scratches

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A method for producing scratch-resistant tempered glass with a surface coating, comprising the following steps:

[0034] (1) Put the glass into the tempering furnace and keep it warm for 20-30 minutes at 580°C-600°C, then lower the temperature in the furnace evenly to 200-220°C within 30 minutes, and keep it warm for 10-15 minutes after dropping to 200-220°C ;

[0035] (2) Take the glass out of the furnace and apply a layer of paint, the paint is made of the following raw materials,

[0036] Metasilicate 5-10kg, TMPTA 15-25kg,

[0037] Alumina 1-4kg, polyethyl acrylate 18-30kg,

[0038] 5-12kg pyrosilicic acid, 85-90kg glycerol,

[0039] PETA 15-25kg, calcium oxide 2-5kg,

[0040] Carbon fiber 0.5-3kg.

[0041] (3) Put the glass coated with paint in step (2) into molten potassium nitrate salt for 15-20 minutes;

[0042] (4) Immerse the glass in step (2) in hot water at 80-90°C for 8-10 minutes;

[0043] (5) Take out step (4) and let it cool naturally.

[0044] P...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing method of anti-scraping toughened glass. The manufacturing method comprises the following steps: (1) conveying glass into a tempering furnace, keeping the temperature at 580-600 DEG C for 20-30 minutes, uniformly reducing the temperature in the furnace to 200-220 DEG C within 30 minutes, and keeping the temperature for 10-15 minutes after the temperature isreduced to 200-220 DEG C; (2) taking out the glass from the furnace, and then coating the glass with a layer of a coating, wherein the coating is prepared from the following raw materials: 5-10 partsof metasilicic acid, 15-25 parts of trimethylolpropane triacrylate (TMPTA), 1-4 parts of aluminum oxide, 18-30 parts of poly(ethyl acrylate), 5-12 parts of pyrosilicic acid, 85-90 parts of glycerol, 15-25 parts of pentaerythritol triacrylate (PETA), 2-5 parts of calcium oxide and 0.5-3 parts of carbon fibers; (3) putting the glass coated with the coating in the step (2) into potassium nitrate molten salt for reacting for 15-20min; (4) putting the glass in the step (2) into hot water with a temperature of 80-90 DEG C for immersion for 8-10min; and (5) taking out the glass obtained in the step (4), and carrying out natural cooling to obtain the toughened glass. The manufacturing method has the characteristic of enhancing anti-scraping performance of glass.

Description

technical field [0001] The invention relates to the field of glass processing, in particular to a method for manufacturing scratch-resistant tempered glass. [0002] technical background [0003] Tempered glass has been widely used due to its advantages such as high mechanical strength, excellent thermal shock resistance, and good safety. Most of the existing tempered glass production processes adopt the tempering process using air as the cooling medium, so that the heated glass is subjected to chilling treatment in a short period of time through a large amount of air, thereby completing the tempering process. In order to ensure the performance of tempered glass, it is usually necessary to provide a large flow of air in a short period of time, especially when tempering thin glass. Usually, a high-power fan with high wind pressure and large flow is used to blow air at the same time. [0004] At present, the surface strength and hardness of glass tempering are not ideal, and i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C17/00C03C21/00
CPCC03C17/007C03C17/009C03C21/001
Inventor 旺正齐
Owner 正安鑫旺钢化玻璃有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap