A kind of glass fiber sizing agent for polyurethane pultrusion composite material and preparation method thereof

A composite material and glass fiber technology, which is applied in the field of glass fiber sizing for polyurethane pultrusion composite materials and its preparation, can solve the problems of large hairiness and poor stability, and achieve low hairiness, high compatibility, biophase good capacitive effect

Active Publication Date: 2022-01-11
NEIJIANG HUAYUAN ELECTRONICS MATERIALS
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a glass fiber sizing for polyurethane pultrusion composite materials and its preparation method to solve the problems of poor stability and large amount of hairiness in the existing glass fiber sizing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of glass fiber sizing agent for polyurethane pultrusion composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The glass fiber sizing agent for polyurethane pultrusion composites in this embodiment includes: by percentage, silane coupling agent A 0.2wt%, silane coupling agent B 0.4wt%, film forming agent 6.2wt%, lubricant A0. 3wt%, lubricant B 0.2wt%, auxiliary agent 0.2wt%, pH regulator 0.2wt%, and the rest is water;

[0029] Wherein, silane coupling agent A is 3-aminopropyltriethoxysilane; silane coupling agent B is 3-(2-aminoethylamino)propyltrimethoxysilane; film-forming agent is modified epoxy Emulsion; lubricant A is polyethylene glycol; lubricant B is octadecyltrimethylammonium chloride; pH regulator is glacial acetic acid; auxiliary agent includes starch nanocrystal modified epoxy resin.

[0030] Wherein, the preparation method of modified epoxy emulsion comprises the following steps:

[0031] (1) Chitosan is added to water, and citric acid is added, after being heated to 30 ℃, the chitosan aqueous solution is obtained after stirring until completely dissolved; wherein,...

Embodiment 2

[0042] The glass fiber sizing agent for polyurethane pultrusion composites in this embodiment includes: by percentage, silane coupling agent A 0.3wt%, silane coupling agent B 0.5wt%, film forming agent 6.5wt%, lubricant A0. 4wt%, lubricant B 0.4wt%, auxiliary agent 0.3wt%, pH regulator 0.25wt%, and the rest is water;

[0043] Wherein, silane coupling agent A is 3-aminopropyltriethoxysilane; silane coupling agent B is 3-(2-aminoethylamino)propyltrimethoxysilane; film-forming agent is modified epoxy Emulsion; lubricant A is polyethylene glycol; lubricant B is octadecyltrimethylammonium chloride; pH regulator is glacial acetic acid; auxiliary agent includes starch nanocrystal modified epoxy resin.

[0044] Wherein, the preparation method of modified epoxy emulsion comprises the following steps:

[0045] (1) Chitosan is added to water, and citric acid is added, after being heated to 40°C, the chitosan aqueous solution is obtained after stirring until completely dissolved; wherein, ...

Embodiment 3

[0056] The glass fiber sizing agent for polyurethane pultrusion composites in this embodiment includes: by percentage, silane coupling agent A 0.4wt%, silane coupling agent B 0.6wt%, film forming agent 7.0wt%, lubricant A0. 5wt%, lubricant B 0.5wt%, auxiliary agent 0.4wt%, pH regulator 0.3wt%, and the rest is water;

[0057] Wherein, silane coupling agent A is 3-aminopropyltriethoxysilane; silane coupling agent B is 3-(2-aminoethylamino)propyltrimethoxysilane; film-forming agent is modified epoxy Emulsion; lubricant A is polyethylene glycol; lubricant B is octadecyltrimethylammonium chloride; pH regulator is glacial acetic acid; auxiliary agent includes starch nanocrystal modified epoxy resin.

[0058] Wherein, the preparation method of modified epoxy emulsion comprises the following steps:

[0059] (1) Chitosan is added to water, and citric acid is added, after being heated to 40 ℃, after stirring until fully dissolved, an aqueous solution of chitosan is obtained; wherein, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass fiber sizing agent for polyurethane pultrusion composite materials, which belongs to the technical field of polyurethane pultrusion technology. It includes: by percentage, silane coupling agent A 0.2-0.6wt%, silane coupling agent B 0.4-0.8wt%, film-forming agent 6.2-8.2wt%, lubricant A 0.3-0.7wt%, lubricant B 0.2-0.8wt%, auxiliary agent 0.2-0.6wt%, pH regulator 0.2-0.4wt%, and the balance is water. The glass fiber sizing agent of the invention has high compatibility with the polyurethane pultrusion composite material, and can make the glass fiber yarn have good bundling property and less hairiness, and can improve the mechanical properties of the glass fiber reinforced polyurethane composite material.

Description

technical field [0001] The invention relates to the technical field of polyurethane pultrusion technology, in particular to a glass fiber sizing agent for polyurethane pultrusion composite materials and a preparation method thereof. Background technique [0002] In recent years, polyurethane resin-reinforced composite materials made by polyurethane pultrusion molding process stand out for their advantages such as good toughness, fast curing, and no styrene smoke. In the polyurethane pultrusion process, reinforced glass fibers are used to obtain high-strength, high-modulus, lightweight polymer composites. At the same time, due to the excellent impact strength, tensile strength and interlayer shear strength of polyurethane itself, the products can be made thinner and lighter. Polyurethane pultrusion products include profiles, rods and plates, such as doors and windows, ladder poles, tool handles, utility pole crossarms, poles, hockey sticks, dock piles, container plates, etc....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C25/465
CPCC03C25/465
Inventor 刘钢刘术明李尚勇孟凡荣何文黄令奇
Owner NEIJIANG HUAYUAN ELECTRONICS MATERIALS