PBT composite material reinforced by modified flat glass fibers, and preparation method of PBT composite material

A flat glass fiber and composite material technology, which is applied in the field of polyester polymer material preparation, can solve the problem of low thermal deformation temperature, poor compatibility between inorganic materials and organic polymers, and the problem of stickiness of glass fiber reinforced PBT compositions. Conjunctive profile warpage and other issues

Active Publication Date: 2020-02-18
福建华塑新材料有限公司
View PDF13 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is limited to PVC co-extruded profiles, and cannot solve the adhesion between glass fiber reinforced PBT compositions and other materials and the degree of warping of profiles
[0013] In summary, polybutylene terephthalate, as an engineering plastic, is a semi-crystalline thermoplastic with excellent performance. In order to overcome the defects of the material itself, PBT composite materials such as PET / PBT have appeared in the prior art, but PET / PBT PBT composite materials cannot effectively improve the defects of low notched impact strength, low heat distortion temperature and large shrinkage rate
Even if the means of adding inorganic fillers is adopted, the existing composite materials cannot effectively improve the defects of poor compatibility between inorganic materials and organic polymers, and thus cannot make the composite materials improve the inherent defects such as PBT brittleness and new materials on the basis of obtaining balanced mechanical properties. Defects, such as the floating fiber problem of long glass fiber reinforced PBT materials and the low notched impact strength and low heat distortion temperature of short glass fiber reinforced materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PBT composite material reinforced by modified flat glass fibers, and preparation method of PBT composite material
  • PBT composite material reinforced by modified flat glass fibers, and preparation method of PBT composite material

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0081] Preparation of doped modified PBT polyester

[0082] In a reactor with stirring, condensing and splitting and decompression devices, add 0.7kg terephthalic acid, 0.65kg 1,4-butanediol, 1.2g tetraisopropyl titanate and 18g mesoporous silica Nanoparticles; after reacting for 2 hours under normal pressure and 240°C, gradually reduce the pressure to 0.08-0.09KPa (total depressurization time 0.6h), and continue the polycondensation reaction for 1.5h; the intrinsic viscosity of the synthesized PBT is 0.82dL / g, Dry and set aside.

preparation example 2

[0084] Preparation of PET-ABS compound composition

[0085] (1) After drying the PET and ABS resin raw materials at a temperature of 100° C. for 4 hours according to the mass ratio of 1:0.3, they were pulverized with an engineering plastic grinder and passed through a 200-mesh sieve, and dried to obtain a PET-ABS mixed raw material;

[0086] (2) Weigh 60 parts of PET-ABS mixture after drying in the above steps, 10 parts of ethylene-methyl acrylate copolymer, 3 parts of butadiene-styrene-methyl methacrylate, 5 parts of surface-treated hollow Glass beads and 2 parts of mesoporous silica treated with silane coupling agent were stirred in a high-speed mixer for 5 minutes until uniform;

[0087] (3) Add the above-mentioned uniformly mixed materials into the feeding port of the twin-screw extruder, melt and extrude through the twin-screw extruder, granulate, and dry in an oven, then pulverize with a pulverizer and pass through a 200-mesh sieve to obtain PET-ABS Mixing composition; ...

preparation example 3

[0089] Preparation of surface-modified flat glass fibers

[0090] Configure isocyanate group propyl triethoxysilane-ethanol solution 1.2kg, so that the isocyanate group propyl triethoxysilane content is 12wt%; Glass fibers, which have a length of 500-600 μm, a width of 20-25 μm, and a thickness of 3-5 μm) are uniformly sprayed, wherein the weight ratio of glass fibers to isocyanate-propyltriethoxysilane-ethanol solution is 1:1; The treated glass fiber is placed in a drying oven, dried at 90°C to remove the solvent, and the surface-treated flat glass fiber is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Lengthaaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a PBT composite material. The composite material comprises the following preparation raw materials in parts by weight: 70-80 parts of PBT composite resin, 10-30 parts of a PET-ABS mixed material composition, 20-30 parts of composite glass fibers, 5-20 parts of a compatible toughening agent, 3-5 parts of surface-treated hollow glass micro-beads, 1-5 parts of mesoporous silica nanoparticles treated by a silane coupling agent and 0-3 parts of an auxiliary agent. According to the prepared PBT composite material, the defect of poor compatibility of an inorganic material andan organic polymer is effectively improved, and the composite material can obtain balanced mechanical properties on the basis of good notch impact strength, thermal deformation temperature and shrinkage rate.

Description

technical field [0001] The invention relates to the field of polyester polymer material preparation, in particular to a modified flat glass fiber reinforced PBT composite material and a preparation method thereof. Background technique [0002] PBT (polybutylene terephthalate) is a polyester polymer prepared by polycondensation of terephthalic acid and butanediol. It belongs to thermoplastic engineering plastics and has low water absorption, good electrical insulation, and aging resistance. However, the disadvantages of large molding shrinkage, low notched impact strength, and poor rigidity at high temperatures limit its application. PBT / PET alloy has high temperature resistance, humidity resistance, chemical corrosion resistance, good electrical insulation performance and good mechanical properties, and is used more and more widely. However, the strength of pure PBT resin is average, it is sensitive to notch, and its heat resistance and deformation temperature are low. [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L67/02C08L55/02C08K13/06C08K9/06C08K7/14C08K7/28C08K7/26C08J5/08C08J3/20
CPCC08J3/201C08J5/08C08J2367/02C08J2455/02C08J2467/02C08K2201/003C08K2201/004C08K2201/011C08K2201/014C08K2201/016
Inventor 林建民蔡鹏飞
Owner 福建华塑新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com