Composition for preparing PVC board and preparation method of composition

A PVC board and composition technology, applied in the field of boards, can solve the problems of excessive formaldehyde emission, waste of manpower and material resources, and influence on normal use of finished advertising boards, and achieve the effects of improving surface finish, maintaining chemical balance, and preventing cracking

Inactive Publication Date: 2020-04-21
刘奇
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing advertising boards are made of non-woven fabric or cardboard, which are easy to change color in the outdoor environment, affecting normal use, and waste manpower and material resources when replacing
Moreover, in the production process of many existing advertising boards, organic spraying agents, printing agents and adhesives are usually used, resulting in excessive formaldehyde emission from the finished advertising boards and endangering the environment.
Moreover, most of the existing advertising boards are flammable and prone to fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] This embodiment provides a composition for preparing PVC boards, including 500 parts by weight of PVC resin, 400 parts of calcium powder, 4 parts of oxidized polyethylene, 20 parts of stabilizer, 4 parts of surface lubrication aids, wax 3 parts, 6 parts of internal lubrication aid, 3 parts of lubricant, 2 parts of zinc oxide, 20 parts of 100 regulator, 0.1 part of toner and 15 parts of toughening agent.

[0028] A kind of preparation method for the composition that is used to prepare PVC plate of present embodiment, comprises the steps:

[0029] S1. Raw material mixing: Add PVC resin, calcium powder, oxidized polyethylene, stabilizer, surface lubrication aid, wax, internal lubrication aid, lubricant, zinc oxide, regulator, toner and toughening agent to the mixture In the device, mix at 10-130 degrees Celsius and then add to the cooler to cool to 30-50 degrees Celsius;

[0030] S2. Raw material reaction: Add the cooled raw materials into the mixing tank, then use the au...

Embodiment 2

[0035] This embodiment provides a composition for preparing PVC boards, including 1000 parts by weight of PVC resin, 600 parts of calcium powder, 8 parts of oxidized polyethylene, 50 parts of stabilizer, 8 parts of surface lubrication aids, wax 8 parts, 10 parts of internal lubrication aid, 7 parts of lubricant, 6 parts of zinc oxide, 40 parts of 100 regulator, 0.5 parts of toner and 40 parts of toughening agent.

[0036] A kind of preparation method for the composition that is used to prepare PVC plate of present embodiment, comprises the steps:

[0037] S1. Raw material mixing: Add PVC resin, calcium powder, oxidized polyethylene, stabilizer, surface lubrication aid, wax, internal lubrication aid, lubricant, zinc oxide, regulator, toner and toughening agent to the mixture In the device, mix at 10-130 degrees Celsius and then add to the cooler to cool to 30-50 degrees Celsius;

[0038] S2. Raw material reaction: Add the cooled raw materials into the mixing tank, then use the...

Embodiment 3

[0043] This embodiment provides a composition for preparing PVC boards, including 800 parts by weight of PVC resin, 450 parts of calcium powder, 5 parts of oxidized polyethylene, 30 parts of stabilizer, 5 parts of surface lubrication aids, wax 5 parts, 7 parts of internal lubrication aid, 4 parts of lubricant, 3 parts of zinc oxide, 25 parts of 100 regulator, 0.1 part of toner and 20 parts of toughening agent.

[0044] A kind of preparation method for the composition that is used to prepare PVC plate of present embodiment, comprises the steps:

[0045] S1. Mixing of raw materials: Add raw materials to the mixing device, heat up to 125 degrees Celsius, and then add them to the cooler to cool to 42 degrees Celsius;

[0046]S2. Raw material reaction: Add the cooled raw materials into the mixing tank, then use the automatic feeder to add the raw materials into the hopper of the plastic machine, flow into the screw barrel through the hopper and heat up to 170 degrees Celsius, and s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of plates, and discloses a composition for preparing a PVC board and a preparation method of the composition. The composition comprises the following components in parts by weight: 500-1000 parts of PVC resin, 400-600 parts of calcium powder, 4-8 parts of oxidized polyethylene, 20-50 parts of a stabilizer, 4-8 parts of a surface lubricating auxiliary agent, 3-8 parts of wax, 6-10 parts of an internal lubricating auxiliary agent, 3-7 parts of a lubricant, 2-6 parts of zinc oxide, 20-120 parts of a regulator, 0.1-0.5 part of toner and 15-40 parts of atoughening agent. The finished board material is prepared through the steps of raw material mixing, raw material reaction, plate shaping, film covering of a plate material, obtainment of the finishedboard material, etc. The PVC board prepared by using the preparation method provided by the invention has good waterproof and mildew-proof properties, is not easy to deform, has good oil stain-proofeffect, does not contain radioactive elements, does not release harmful substances, has good environmental protection performance, is non-flammable, and can be used for advertisement boards, cupboardsand the like.

Description

technical field [0001] The invention belongs to the technical field of boards, and in particular relates to a composition for preparing PVC boards and a preparation method thereof. Background technique [0002] Modern society has entered the information age, especially under the conditions of commodity market economy, a large amount of information is displayed by advertisements. Advertising boards are billboards used to attract customers to come to consume, and can also be used to promote policies and regulations, or to remind attention. Existing advertising boards are made of non-woven fabric or cardboard, and are prone to discoloration in the outdoor environment, affecting normal use and wasting manpower and material resources when replacing them. Moreover, in the production process of many existing advertising boards, organic spraying agents, printing agents and adhesives are usually used, resulting in excessive formaldehyde emission from the finished advertising boards ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/30C08L91/06C08K3/26C08K3/22C08J9/00
CPCC08J9/0061C08J9/0066C08J2327/06C08J2423/30C08J2491/06
Inventor 刘奇
Owner 刘奇
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com