Safe and harmless ceramic tile anti-skid agent and preparation method thereof

An anti-slip agent and ceramic tile technology, applied in chemical instruments and methods, other chemical processes, coatings, etc., can solve the problems of poor thermal cycle resistance, low anti-slip coefficient of anti-slip agent, ground corrosion, etc., to enhance the stability of the system , high anti-skid coefficient, good environmental protection effect

Inactive Publication Date: 2020-04-21
佛山市善益科技有限公司
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the anti-slip agent has a low anti-slip coefficient, is dull, and has poor stability against hot and cold cycles, and cracks will appear after a long time; at the same time, the raw materials of the anti-slip agent are toxic substances such as oxalic acid and hydrofluoric acid, which will not only corrode the ground, And it will cause environmental pollution, poor environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Safe and harmless ceramic tile anti-skid agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0112] The preparation of the B component comprises the following steps:

[0113] (1) Heat deionized water to 70-75°C, add acid and stir;

[0114] (2) adding defoamer, anti-aging agent and surfactant in the mixed solution that step (1) obtains successively, and stir;

[0115] (3) Add industrial glue to the mixed solution obtained in the step (2), stir evenly, and cool to normal temperature to obtain component B, which is packaged independently.

[0116] In a preferred embodiment, the preparation method of the safe and harmless ceramic tile anti-slip agent, the A component and the B component are prepared separately and packaged independently;

[0117] Wherein, the preparation of described A component comprises the following steps:

[0118] (1) Dissolve the corrosion inhibitor in water and stir evenly;

[0119] (2) adding the dispersant to the mixed solution obtained in the step (1), and stirring evenly;

[0120] (3) Add the moisturizing agent into the mixed solution obtain...

Embodiment 1

[0130] Embodiment 1 provides a safe and harmless anti-slip agent for tiles, the anti-slip agent for tiles includes component A and component B; the volume ratio of component A and component B is 1:1.5;

[0131] In parts by weight, the A component includes 3 parts of corrosion inhibitor, 0.5 part of dispersant, 0.1 part of moisturizing agent, and 70 parts of water;

[0132] The corrosion inhibitor is ammonium fluoride;

[0133] The dispersant is a water-based acrylic polyol, the trade mark is Akuapol AL 4500, and the hydroxyl content of the water-based acrylic polyol is 4.3wt%, purchased from T&L Co., Ltd. Polymer Technology Center;

[0134] The humectant is a mixture of glycerol and epoxy polyether modified silicone oil KF1002, and the mass ratio of glycerin and epoxy polyether modified silicone oil KF1002 is 1:4; the epoxy polyether Modified silicone oil KF1002 was purchased from Suzhou Jiandao Electronics Co., Ltd.;

[0135] In parts by weight, the B component includes 2 p...

Embodiment 2

[0150] Example 2 provides a safe and harmless anti-slip agent for tiles, the anti-slip agent for tiles includes component A and component B; the volume ratio of component A and component B is 1:3;

[0151] In parts by weight, the A component includes 15 parts of a corrosion inhibitor, 2 parts of a dispersant, 1 part of a moisturizing agent, and 85 parts of water;

[0152] The corrosion inhibitor is ammonium fluoride;

[0153] The dispersant is a water-based acrylic polyol, the trade mark is Akuapol AL 2300, and the hydroxyl content of the water-based acrylic polyol is 3.9wt%, purchased from T&L Co., Ltd. Polymer Technology Center;

[0154] Described humectant is with embodiment 1;

[0155] In parts by weight, the B component includes 10 parts of surfactant, 1 part of defoamer, 30 parts of acid, 1 part of anti-aging agent, and 80 parts of deionized water;

[0156] The surfactant is a mixture of triethanolamine dodecylbenzenesulfonate and sodium isooctyl sulfate, and the mass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of ceramic tile skid resistance, in particular to a safe and harmless ceramic tile skid resistance agent and a preparation method thereof. The ceramic tileskid resistance agent comprises a component A and a component B according to a volume ratio of the component A to the component B of 1: (1.5-3), the component A comprises a corrosion inhibitor, a dispersing agent, a humectant and water, and the component B comprises a surfactant, a defoaming agent, an acid, an anti-aging agent and deionized water. Tartaric acid is used for replacing oxalic acid and other harmful substances used in a traditional anti-skid agent, the tartaric acid is harmless and environmentally friendly, corrosion of the anti-skid agent to ceramic tiles and pollution to the environment can be reduced, and environmental friendliness is good, the used high-molecular water-based polymer has hydrophilicity, has excellent dispersibility in a system, can enhance the stability ofan antiskid coefficient, glossiness and cold and hot cycle resistance, is safe and harmless, has a high antiskid coefficient and good durability, and has good decontamination performance.

Description

technical field [0001] The invention relates to the technical field of ceramic tile anti-skid, in particular to a safe and harmless ceramic tile anti-skid agent and a preparation method thereof. Background technique [0002] With the needs of urbanized buildings, more and more buildings use bright hard materials such as marble, tiles, and mosaics. These materials are suitable for large buildings such as exhibition halls, hotels, supermarkets, shopping centers, restaurants, gymnasiums, swimming pools, Bathrooms and residential buildings are indispensable. But the ensuing problem is that some slipping accidents continue to occur due to the smoothness of the ground, and even cause human disability. According to statistics, in daily life, the number of casualties caused by slipping accidents every year is second only to car accidents, among which young children, the elderly, pregnant women and people with limited mobility are the most serious, so the ground slip resistance has ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/00C09D7/61C09D7/63C09D7/65C04B41/85C09K3/14
CPCC04B41/5018C04B41/85C09D5/00C09D7/61C09D7/63C09D7/65C09K3/149C04B41/501C04B41/46C04B41/4961C04B41/4539
Inventor 刘宏键林家荣
Owner 佛山市善益科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka