A kind of medium temperature curing high toughness epoxy adhesive and preparation method thereof

An epoxy adhesive and high toughness technology, which is applied in the direction of adhesives, epoxy resin glue, polymer adhesive additives, etc., can solve the problems of high brittleness, poor impact toughness, and limitations of epoxy resin, and achieve the effect of rapid delivery

Active Publication Date: 2022-02-25
康达新材料(集团)股份有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the shortcomings of epoxy resin itself, such as high brittleness and poor impact toughness, limit its application in the field of automobile lightweight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of medium temperature curing high toughness epoxy adhesive and preparation method thereof
  • A kind of medium temperature curing high toughness epoxy adhesive and preparation method thereof
  • A kind of medium temperature curing high toughness epoxy adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] 1. The preparation method of the toughening agent:

[0057] React 100 parts of N330, 80 parts of N220 and 30 parts of TDI at 80°C to prepare an isocyanate-terminated prepolymer; weigh 100 parts of isocyanate-terminated prepolymer, 12 parts of KH550 and 10 parts of KH560 and mix them in the reactor, React for 60 minutes under stirring at a speed of 200-500 rev / min, and discharge the material to obtain a siloxane hybrid polyurethane elastomer.

[0058] 2. The preparation method of medium temperature curing high toughness epoxy adhesive:

[0059] 1) Preparation of component A: 50 parts of E-51 resin, 50 parts of E-44 resin, 8 parts of 636 reactive diluent, 5 parts of siloxane hybrid polyurethane elastomer, 10 parts of talc powder, silicon micropowder Put 60 parts and 6 parts of hydrophobic fumed silica into the planetary stirring tank, control the rotation speed at 200-500 rpm for stirring and mixing, and the mixing time is 2 hours. After vacuum defoaming, filter, discharge...

Embodiment 2

[0062] 1. The preparation method of the toughening agent:

[0063] React 100 parts of N330, 80 parts of N220 and 30 parts of TDI at 80°C to prepare an isocyanate-terminated prepolymer; weigh 100 parts of isocyanate-terminated prepolymer, 12 parts of KH550 and 10 parts of KH560 and mix them in the reactor, React for 60 minutes under stirring at a speed of 200-500 rev / min, and discharge the material to obtain a silicone hybrid polyurethane elastomer.

[0064] 2. The preparation method of medium temperature curing high toughness epoxy adhesive:

[0065] 1) Preparation of component A: 50 parts of E-51 resin, 50 parts of E-44 resin, 8 parts of 636 reactive diluent, 10 parts of siloxane hybrid polyurethane elastomer, 10 parts of talcum powder, and microsilica powder Put 55 parts and 6 parts of hydrophobic fumed silica into a planetary stirring tank, control the rotation speed at 200-500 rpm for stirring and mixing, and the mixing time is 2 hours. After vacuum defoaming, filter, dis...

Embodiment 3

[0068] 1. The preparation method of the toughening agent:

[0069] React 100 parts of N330, 80 parts of N220 and 30 parts of TDI at 80°C to prepare an isocyanate-terminated prepolymer; weigh 100 parts of isocyanate-terminated prepolymer, 12 parts of KH550 and 10 parts of KH560 and mix them in the reactor, React for 60 minutes under stirring at a speed of 200-500 rev / min, and discharge the material to obtain a silicone hybrid polyurethane elastomer.

[0070] 2. The preparation method of medium temperature curing high toughness epoxy adhesive:

[0071] 1) Preparation of component A: 50 parts of E-51 resin, 50 parts of E-44 resin, 8 parts of 636 reactive diluent, 20 parts of siloxane hybrid polyurethane elastomer, 10 parts of talcum powder, and microsilica powder Put 45 parts and 6 parts of hydrophobic fumed silica into a planetary stirring tank, control the rotation speed at 200-500 rpm for stirring and mixing, and the mixing time is 2 hours. After vacuum defoaming, filter, dis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shear strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a medium-temperature curing high-toughness epoxy adhesive, which comprises A component and B component, and the proportion of A component and B component is 0.9-1.1:1.1-0.9 according to the mass ratio; in A component, In terms of parts by mass, it includes: 80-120 parts of epoxy resin; 6-20 parts of reactive diluent; 20-40 parts of toughening agent; 30-60 parts of filler; 2-10 parts of thixotropic agent; , in parts by mass, including: 10-50 parts of low molecular weight polyamide curing agent; 20-60 parts of modified amine curing agent; 1-5 parts of accelerator; 40-80 parts of filler; 1-5 parts of thixotropic agent . The invention also discloses its preparation method. The entangled interlocking interpenetrating network structure formed by the medium-temperature curing high-toughness epoxy adhesive of the present invention is conducive to the rapid transmission and dispersion of stress, and can realize the bonding of various lightweight materials for automobiles, including aluminum plates, honeycomb aluminum interlayers, and carbon fibers. Composite.

Description

technical field [0001] The invention belongs to the technical field of epoxy adhesives, and in particular relates to a medium-temperature curing high-toughness epoxy adhesive and a preparation method thereof. Background technique [0002] In recent years, the automobile industry has begun to develop in the direction of new energy, lightweight, intelligence and networking. While ensuring safety, better experience and comfort are increasingly favored by consumers. Among them, lightweight is an important way to achieve energy saving and emission reduction in the automotive industry. The concept of "replacing steel with aluminum and steel with plastic" is quietly entering the automobile industry under the guidance of my country's policies and industrial transformation and development. These emerging materials can reduce weight, reduce energy consumption, and replace traditional welding and riveting with adhesive bonding. , Improving the quality effect of automobile products. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J163/00C09J11/04C09J11/08C08G77/458C08G18/48C08G18/28C08G18/83C08G59/60
CPCC09J163/00C09J11/04C09J11/08C08G77/458C08G18/4804C08G18/289C08G18/837C08G59/60C08L63/00C08L75/08C08K3/34C08K3/36
Inventor 吴杰李达
Owner 康达新材料(集团)股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com