A kind of injection molding permanent ferrite magnet and preparation method thereof

A permanent magnet ferrite and magnet technology, which is applied in the manufacture of inductors/transformers/magnets, magnetic objects, magnetic materials, etc., can solve the problems of easy cracking of magnets, overheating of engines, failure of coolant pumps, etc., and achieve good fluidity and injection molding The effect of low temperature and low mold requirements

Active Publication Date: 2021-06-18
HENGDIAN GRP DMEGC MAGNETICS CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] In order to overcome the problems that the existing water pump rotor magnets are easy to crack and lead to the failure of the coolant pump and the overheating of the engine, the present invention provides an injection molding machine with high mechanical strength, long working life, high temperature resistance, acid and alkali resistance, solvent resistance and excellent magnetic properties. Permanent ferrite magnet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of injection molding permanent ferrite magnet and preparation method thereof
  • A kind of injection molding permanent ferrite magnet and preparation method thereof
  • A kind of injection molding permanent ferrite magnet and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] An injection-molded permanent ferrite magnet, made according to the formula shown in Table 1: 500kg of Sr permanent ferrite magnetic powder A, 110kg of polyphenylene sulfide I powder, 3kg of KH550 silane coupling agent, 2kg of polyphenylene sulfide Dispersant for sulfide, 4kg of mixed toughening agent P2#. Among them, the average particle size of Sr permanent ferrite magnetic powder A (Fischer gas permeability method) is 1.53 μm, and the melt viscosity of polyphenylene sulfide I powder (310°C, 1200S -1 ) is 33Pa.S.

[0068] Its preparation method is as follows:

[0069] (1) Magnetic powder surface coupling treatment: 500kg of Sr permanent magnet ferrite magnetic powder A is placed in a high-speed powder mixing tank, and 3kg of KH550 silane coupling agent (1:10 dissolved in isopropanol) is added, mixed at 100°C powder for 50 minutes, and the moisture content of the magnetic powder is controlled within 1000ppm;

[0070] (2) Add 110kg of polyphenylene sulfide I powder a...

Embodiment 2

[0075] An injection-molded permanent ferrite magnet, made according to the formula shown in Table 1: 500kg of Sr permanent ferrite magnetic powder B, 100kg of polyphenylene sulfide II powder, 3kg of KH560 silane coupling agent, 3kg of polyphenylene sulfide II powder Dispersant for sulfide, 3.5kg of mixed toughening agent P3#. Among them, the average particle size of Sr permanent ferrite magnetic powder B (Fischer gas permeability method) is 1.76 μm, and the melt viscosity (310°C, 1200S-1) of polyphenylene sulfide II powder is 47Pa.S.

[0076] Its preparation method is as follows:

[0077] (1) Magnetic powder surface coupling treatment: 500kg of Sr permanent magnet ferrite magnetic powder B is placed in a high-speed powder mixing tank, and 3kg of KH560 silane coupling agent (1:10 ratio is dissolved in isopropanol) is added. Mix the powder at temperature for 50 minutes, and control the moisture content of the magnetic powder within 1000ppm;

[0078] (2) Add 100kg of polyphenyl...

Embodiment 3

[0083] An injection-molded permanent ferrite magnet, made according to the formula shown in Table 1: 500kg of Sr permanent ferrite magnetic powder B, 105kg of polyphenylene sulfide III powder, 4kg of KH550 silane coupling agent, 3kg of polyphenylene sulfide III powder Dispersant for sulfide, 3kg of silicon-based toughening agent. Among them, the average particle size of Sr permanent ferrite magnetic powder B (Fischer gas permeability method) is 1.76 μm, and the melt viscosity (310°C, 1200S-1) of polyphenylene sulfide III powder is 25Pa.S.

[0084] Its preparation method is as follows:

[0085] (1) Magnetic powder surface coupling treatment: 500kg of Sr permanent magnet ferrite magnetic powder B is placed in a high-speed powder mixing tank, and 4kg of KH550 silane coupling agent (1:10 ratio is dissolved in isopropanol) is added. Mix the powder at temperature for 50 minutes, and control the moisture content of the magnetic powder within 1000ppm;

[0086](2) Add 105kg of polyph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of injection molding permanent magnet materials, and provides an injection molding permanent ferrite magnet and a preparation method thereof in order to solve the problems that existing water pump rotor magnets are easy to crack and cause coolant pump failure and engine overheating. The permanent ferrite magnet is made of the following components by weight percentage: permanent ferrite magnetic powder 75-90%, polyphenylene sulfide 9-22%, coupling agent 0.2-2.0%, toughening enhancer 0.2-1.5% %, the dispersant is 0.2-1.0%, and the melt viscosity of the polyphenylene sulfide is controlled at 22-75 Pa.S. The injection molded permanent ferrite magnet of the present invention has high tensile strength and high bending strength, and can be widely used in the fields of electronic water pump rotors, automobile motor rotors, high-end home appliance motor rotors, induction magnetic rings, etc.; the magnetic powder fluidity in the preparation process Good, low injection temperature, low energy consumption, low requirements for molds, good product appearance, and low production costs.

Description

technical field [0001] The invention relates to the technical field of injection molding permanent magnet material production, in particular to an injection molding permanent ferrite magnet and a preparation method thereof. Background technique [0002] In recent years, with the vigorous development of turbocharged vehicles and the continuous popularization of new energy vehicles, micro electronic water pumps used as turbochargers and battery pack liquid cooling systems have developed rapidly. At present, the micro electronic water pump mainly adopts a permanent magnet DC motor, and the motor rotor adopts an injection-molded magnet with high dimensional accuracy, high mechanical strength, long working life, and high temperature resistance (above 180°C). [0003] Injection molding magnet is a polymer-based composite permanent magnet material made by uniformly mixing magnetic powder (ferrite, NdFeB, SmFeN, SmCo, etc.) with nylon, polyphenylene sulfide and other binders, granul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/113H01F41/02
CPCH01F1/113H01F41/0266
Inventor 金志洪胡江平何国栋李军华丁卫卫
Owner HENGDIAN GRP DMEGC MAGNETICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com