R-T-B magnet material, preparation method and application thereof
A R-T-B, magnet technology, applied in the direction of magnetic materials, magnetic objects, inductance/transformer/magnet manufacturing, etc., can solve the problems of poor magnetic properties and small diffusion of magnet materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0089] Example 1
[0090] The raw material formula of the R-T-B magnet material in this embodiment is shown in Table 1 below:
[0091] Table 1
[0092]
[0093] (1) According to the raw material formula in Table 1, a blank is prepared by smelting, casting, hydrogen crushing, compression molding and sintering. The size of the blank is 65 (length) × 50 (pressing direction) × 40 mm (orientation direction).
[0094] Among them, smelting and casting: Place the raw material formula for smelting in Table 1 in a medium-frequency vacuum induction quick-setting belt spinning furnace for smelting and casting, with a frequency of 1500-2500 Hz. The melting temperature is 1450-1550°C, and the casting temperature is 1350-1500°C. After melting and casting, 0.2-0.4mm alloy flakes are obtained.
[0095] Hydrogen crushing and pulverizing: pass hydrogen with a purity of 99.9% into the hydrogen crushing furnace and maintain the hydrogen pressure at 0.15Mpa. After fully absorbing hydrogen, increase the tem...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap