A method and system for preparing sulphoaluminate cement from all solid waste pretreated with aluminum ash

A sulphoaluminate cement and pretreatment technology, applied in cement production, etc., can solve problems such as condenser blockage, difficulty in long-term operation, easy ring formation of rotary kiln, etc., and achieve the effect of reducing energy consumption and increasing energy utilization rate

Active Publication Date: 2021-04-06
SHANDONG UNIV +2
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the inventors of the present invention have found that when aluminum ash is used to replace part of the bauxite, the tail of the rotary kiln is more likely to form rings, the condenser is blocked, it is difficult to run for a long time, and it is impossible to completely replace aluminum ash with aluminum ash. Bauxite

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method and system for preparing sulphoaluminate cement from all solid waste pretreated with aluminum ash
  • A method and system for preparing sulphoaluminate cement from all solid waste pretreated with aluminum ash
  • A method and system for preparing sulphoaluminate cement from all solid waste pretreated with aluminum ash

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0057] In order to realize the preparation of sulphoaluminate cement from the above-mentioned aluminum ash pretreatment of all solid waste, the third embodiment of the present invention provides a method for realizing the above-mentioned aluminum ash pretreatment of all solid waste to prepare sulphoaluminate cement System, including indirect rotary drum heating furnace, cyclone condenser, dryer, raw material pulverizer, rotary kiln, the inlet of indirect rotary drum heating furnace is set to connect aluminum ash source, the solid phase outlet of indirect rotary drum heating furnace is connected The material inlet of the dryer, the gas phase outlet of the indirect rotary drum heating furnace is connected to the inlet of the cyclone condenser, the gas phase outlet of the cyclone condenser is connected to the heat exchange gas inlet of the dryer, and the material inlet of the dryer is also set to be used to connect the red mud source , desulfurization gypsum source, calcium carbid...

Embodiment 1

[0066] A system for preparing sulphoaluminate cement from all solid waste pretreated with aluminum ash, such as figure 1 As shown, hopper 1, automatic weighing scale 2, indirect drum heating furnace 3, burner nozzle 5, red mud storage bin 6, desulfurized gypsum storage bin 7, carbide slag storage bin 8, belt conveyor 9, feeding pipe Road 10, air extractor 11, cyclone condenser 12, cooling fan 13, salt storage bin 14, rotary drying cylinder 15, raw material grinding machine 16, dry raw material bin 17, rotary kiln 18, material grinding machine 19.

[0067]The aluminum ash is first fed into the automatic weighing scale 2 through the hopper 1, and sent into the indirect rotary drum heating furnace 3 through the belt conveyor, and the natural gas 4 is heated to the indirect rotary drum heating furnace 3 through the burner nozzle 5 to realize the indirect transfer The aluminum ash in the drum heating furnace 3 is denitrified and desalted by high-temperature calcination, and the alu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method and system for preparing sulphoaluminate cement from all solid waste pretreated with aluminum ash. The mud, desulfurized gypsum, and calcium carbide slag are homogenized and mixed, and the mixed material is dried by the hot gas generated by heat treatment, and then the dried material is grinded with raw powder ratio, and the raw powder ratio grinded material is Carrying out calcination to obtain sulphoaluminate cement clinker; the aluminum ash includes secondary aluminum ash or the aluminum ash is secondary aluminum ash. The invention can make the tail of the rotary kiln not easy to form rings, avoid the clogging of the condenser, ensure long-term operation, and can completely replace the bauxite.

Description

technical field [0001] The invention relates to the fields of aluminum processing, building material technology and comprehensive utilization of bulk industrial solid waste resources and environmental protection treatment, and relates to a method and system for preparing sulphoaluminate cement from all solid waste pretreated with aluminum ash. Background technique [0002] The information disclosed in this background section is only intended to increase the understanding of the general background of the present invention, and is not necessarily taken as an acknowledgment or any form of suggestion that the information constitutes the prior art already known to those skilled in the art. [0003] Industrial solid waste refers to various waste residues, dust and other wastes discharged into the environment during the industrial production process, which can be divided into general industrial wastes (such as blast furnace slag, steel slag, red mud, tailings, fly ash, desulfurizati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B7/32C04B7/147
CPCC04B7/147C04B7/32Y02P40/10
Inventor 王文龙任常在成望海王旭江武双姚永刚刘全勋
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com