Water-based single-component white surface material as well as preparation method and application thereof

A single-component, white surface technology, applied in antifouling/underwater coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems such as poor adhesion, poor water resistance, and low fullness, and achieve good compactness , good water resistance and excellent adhesion

Inactive Publication Date: 2020-06-16
CHENGDU ZHANCHEN PAINT +2
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims to provide a water-based single-component white flour material and its preparation method and application, so as to solve the problems of poor water resistance, low fullness and poor adhesion of the existing water-based white flour materials; spraying), yellowing properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based single-component white surface material as well as preparation method and application thereof
  • Water-based single-component white surface material as well as preparation method and application thereof
  • Water-based single-component white surface material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) Preparation of 80% titanium dioxide slurry:

[0032] It is not easy to disperse when titanium white pulp is added directly to the wood lacquer system. Because the stable nano-alumina pulp is prepared in advance, it is added to the wood lacquer system during the let-down stage.

[0033] A. Titanium dioxide paste is prepared from the following raw materials in parts by weight:

[0034]

[0035] Mix and stir deionized water, defoamer, dispersant, and bactericide according to parts by weight, disperse at medium and low speed for 5-10 minutes, add titanium dioxide, disperse at high speed for 20-30 minutes, fineness ≤ 15um, and obtain titanium dioxide pulp.

[0036] The titanium dioxide content in the titanium dioxide slurry is 80%, and there is no delamination and coarsening phenomenon at 50°C / 7d.

[0037] Preparation of water-based one-component white flour material:

[0038]

[0039] Preparation:

[0040]Mix polyacrylic acid emulsion, polyurethane emulsion, d...

Embodiment 2

[0044] The preparation process is the same as in Example 1, except that the polyurethane emulsion in this example uses NEOREZ-986. Simultaneously present embodiment each component specific gravity is also different:

[0045]

[0046]

Embodiment 3

[0048] The preparation process is the same as in Example 1, except that the water-based single-component white flour material polyacrylic acid emulsion of this example uses AC2524 as follows:

[0049]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a water-based single-component white surface material as well as a preparation method and application thereof. The water-based single-component white surface material is prepared from 30-40 parts of polyacrylic emulsion, 10-20 parts of polyurethane emulsion, 0.1-0.5 parts of an antifoaming agent, 1-5 parts of a wetting dispersant, 0.5-1.5 parts of a thickening agent, 25-30parts of titanium dioxide slurry, 1-3 parts of organic extinction powder, 3-5 parts of Fischer-Tropsch wax, 5-10 parts of a coalescing agent, 0.1-0.2 parts of a pH regulator, 0.1-0.2 part of a bactericide and 5-10 parts of water. The water-based single-component white surface material is high in paint film compactness, excellent in water resistance, high in fullness, good in construction performance and high in adhesive force, overcomes the defect that an existing water-based single-component white surface material is low in fullness, poor in compactness, poor in adhesive force, common in water resistance and the like, has a certain yellowing resistance effect and is a novel composite water-based environment-friendly product.

Description

technical field [0001] The invention belongs to the technical field of water-based wood lacquer, and in particular relates to a water-based single-component white surface material and its preparation method and application. Background technique [0002] With the further improvement of environmental protection regulations, in order to reduce the load on the earth, new low-VOC or zero-VOC emission coatings have become the focus of research and development. The research, development, promotion and application of water-based wood coatings have attracted more and more attention. In recent years, the research and development of water-based wood paint has achieved unprecedented development in our country. [0003] Water-based wood paint has been successfully applied in home decoration and ordinary furniture, and is expanding its market share. However, in some mid-to-high-end fields, such as bathrooms and cabinets, based on cost requirements, it is difficult for water-based one-com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D175/08C09D5/14C09D7/61C09D7/42C09D7/65
CPCC09D133/04C09D5/14C09D7/61C09D7/42C09D7/65C08L2205/035C08K2003/2241C08L75/08C08L91/06C08K13/02C08K3/22
Inventor 麦毅
Owner CHENGDU ZHANCHEN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap