A kind of high-solid single-coat high-gloss black plastic paint and preparation method thereof

A high-gloss, plastic paint technology, applied in the field of paint, can solve the problems of high paint usage, low production efficiency, complex process, etc., and achieve the effects of protecting the environment, improving production efficiency, and reducing pollution

Active Publication Date: 2011-12-14
DONGLAI COATING TECH SHANGHAI
View PDF6 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] These two methods are all carried out with two sprays and two bakes, which have the following defects: (1) the process is complicated, and the primer must be sprayed first, then polished after drying, and then sprayed with a top coat, so that the production efficiency is low; (2) Both are primer and topcoat two coats, the amount of paint used is high, and the cost is high; with the rise of raw material costs and the intensification of market competition, customers urgently need a single-coat product to replace the current double-coat product. This can greatly reduce the cost of raw materials and production costs, improve production efficiency and market competitiveness, and at the same time comply with the national energy conservation and environmental protection policy, and reduce physical injuries to painting workers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A preparation method of high-solid single-coat high-gloss black plastic paint, the method comprises the following processing steps:

[0038] (1) with saturated polyester resin (Setal 173VS-60) 32%, hydroxyl acrylic resin (Hypomer FS-1560) 43%, organic solvent propylene glycol methyl ether acetic acid 5% and 100# solvent naphtha 4% and carbon black dispersant ( Disperbyk 161) 2% was added sequentially under stirring, and stirred at a medium speed for 30 minutes to make it evenly mixed, and to prepare product A;

[0039] (2) Add 2.5% of carbon black pigment (DEGUESS FW-200) evenly in the stirring state of product A. After adding, stir at high speed for 30 minutes to fully mix carbon black and product A; then add 3% butyl acetate , adjust the base material viscosity to 70 ~ 80KU.

[0040] (3) Put the base material above into a sand mill for grinding, adjust the rotation speed, control the flow rate according to the base material temperature ≤ 40°C, grind to a fineness ≤ 1...

Embodiment 2

[0043] A preparation method of high-solid single-coat high-gloss black plastic paint, the method comprises the following processing steps:

[0044] (1) Saturated polyester resin (Desmophen VPLS2388) 38%, hydroxyl acrylic resin (Desmophen A450MPA / X) 37%, organic solvent propylene glycol methyl ether acetic acid 3%, ethylene glycol ethyl ether 3% and xylene 3% and carbon black Dispersant (CIBA EFKA-4050) 2.5% was added sequentially while stirring, and stirred at a medium speed for 30 minutes to make it evenly mixed, and the product A was prepared;

[0045] (2) Add 2.8% of carbon black pigment (DEGUESS FW-200) evenly in the stirring state of product A. After adding, stir at high speed for 30 minutes to fully mix carbon black and product A; then add 4% butyl acetate , adjust the base material viscosity to 70 ~ 80KU.

[0046] (3) Put the base material above into a sand mill for grinding, adjust the rotation speed, control the flow rate according to the base material temperature ≤ ...

Embodiment 3

[0049] A preparation method of high-solid single-coat high-gloss black plastic paint, the method comprises the following processing steps:

[0050] (1) Disperse saturated polyester resin (Uralac SN883) 35%, hydroxyl acrylic resin (ETERAC7305-2-XS-50) 40%, organic solvent propylene glycol monobutyl ether 2% and 150# solvent oil 3% and carbon black Add 3% of the agent (TEGO DISPERS 610S) in a stirring state, stir at a medium speed for 30 minutes, make it evenly mixed, and prepare product A;

[0051] (2) Add 3.5% of carbon black pigment (CABOT M1400) evenly in the stirring state of product A. After adding, stir at high speed for 30 minutes to fully mix carbon black and product A; then add 5% butyl acetate, adjust Base material viscosity to 70 ~ 80KU.

[0052] (3) Put the base material above into a sand mill for grinding, adjust the rotation speed, control the flow rate according to the base material temperature ≤ 40°C, grind to a fineness ≤ 10um, and then stop grinding to make p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-solid volume, single-coating and high-lustre black plastic paint and a preparation method thereof. The plastic paint comprises the following components: 30-40wt% of saturated polyester resin, 35-45wt% of hydroxy acrylic resin, 2-4wt% of high-purity carbon black pigment, 1-3wt% of carbon black dispersing agent, 0.5-1wt% of flatting agent, 0.3-0.6wt% of scratch-resisting agent, 0.2-0.5wt% of defoaming agent, 0.02-0.04wt% of drier and 15-25wt% of organic solvent. Compared with the prior art, the black plastic paint has the advantages of low cost, high efficiency, good effect and the like.

Description

technical field [0001] The invention relates to a coating, in particular to a high-solid single-coat high-gloss black plastic paint and a preparation method thereof. Background technique [0002] Among the low-temperature plastic paints currently used in the automobile, home appliance and 3C industries, there is a kind of high-gloss black plastic paint widely used on ABS and other plastics, because its full appearance is similar to the black paint on the surface of a piano, and the industry also calls it "" "Piano black", the traditional coating process of this kind of paint is two coats, generally there are two methods: [0003] Black primer + clear varnish [0004] Primer + Black Topcoat [0005] These two methods are all carried out with two sprays and two bakes, which have the following defects: (1) the process is complicated, and the primer must be sprayed first, then polished after drying, and then sprayed with a top coat, so that the production efficiency is low; (2...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D167/00C09D7/12
Inventor 朱忠敏叶小明
Owner DONGLAI COATING TECH SHANGHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com