A self-adhesive single-layer high-magnification expansion rubber strip and its preparation method

A high-magnification, self-adhesive technology, applied in the direction of adhesive types, adhesives, natural rubber adhesives, etc., can solve the problems of poor sound insulation and noise reduction effects of automobiles, inability to seal, and reduce the noise reduction function of products.

Active Publication Date: 2021-08-20
科建高分子材料(上海)股份有限公司
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the adhesive layer cannot be foamed, it cannot seal some small gaps. The foamed layer has no bonding ability with the substrate, so the product often cannot completely seal the cavity, which reduces the noise reduction function of the product.
[0003] Moreover, the expansion ratio of the existing expansion strips is only 30%-200%, which often makes the product unable to completely seal the cavity, resulting in relatively poor sound insulation and noise reduction effects for automobiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A self-adhesive single-layer high-magnification expansion rubber strip and its preparation method
  • A self-adhesive single-layer high-magnification expansion rubber strip and its preparation method
  • A self-adhesive single-layer high-magnification expansion rubber strip and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A new type of self-adhesive single-layer high-magnification expansion rubber strip for automobiles, the raw materials of the expansion rubber strip are calculated by weight percentage, including the following components: 20% of natural rubber, 6% of terpene phenol resin, and 7% of petroleum resin , modified urea 1%, AC foaming agent 8%, PTSH foaming agent 5%, calcium carbonate 45%, sulfur 0.4%, antioxidant 0.3%, paraffin oil 5%, naphthenic oil 2%, accelerator 0.3 %.

Embodiment 2

[0027] A new type of self-adhesive single-layer high-magnification expansion rubber strip for automobiles, the raw materials of the expansion rubber strip are calculated by weight percentage, including the following components: 16% of natural rubber, 6% of butyl rubber, 6% of terpene phenol resin %, petroleum resin 7%, modified urea 1%, AC foaming agent 8%, PTSH foaming agent 5%, calcium carbonate 43%, sulfur 0.4%, antioxidant 0.3%, paraffin oil 5%, naphthenic oil 2%, Accelerator 0.3%.

Embodiment 3

[0029] A new type of self-adhesive single-layer high-magnification expansion rubber strip for automobiles, the raw materials of the expansion rubber strip are calculated by weight percentage, including the following components: 16% of natural rubber, 6% of butyl rubber, 6% of terpene phenol resin %, petroleum resin 7%, modified urea 1%, AC foaming agent 10%, calcium carbonate 46%, sulfur 0.4%, antioxidant 0.3%, paraffin oil 5%, naphthenic oil 2%, accelerator 0.3% .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a self-adhesive single-layer high-magnification expansion rubber strip, which comprises the following components in parts by weight: 14-20 parts by weight of natural rubber; 4-9 parts by weight of butyl rubber; 0-4 parts by weight of modified urea Parts by weight; 40-50 parts by weight of filler; 9-20 parts by weight of tackifying resin; 9-17 parts by weight of blowing agent; 0.2-0.6 parts by weight of sulfur; 0.1-0.5 parts by weight of antioxidant; 0.2-0.6 parts by weight of accelerator Part; Solvent 4-14 parts by weight. The self-adhesive single-layer high-magnification expansion rubber strip of the present invention uses natural rubber and butyl rubber in combination as raw materials, so that the expansion rubber strip can not only ensure a certain crosslinking density, but also ensure a certain airtightness. AC foaming agent and PTSH foaming agent are used together to better improve and ensure the foaming ratio. The foaming ratio is increased to 500%-600%, and it is a single-layer structure, which improves the sound insulation and noise reduction effect of the product on the car.

Description

technical field [0001] The invention belongs to the technical field of foamed expansion rubber strips for automobiles, and in particular relates to a self-adhesive single-layer high-magnification expansion rubber strip and a preparation method thereof. Background technique [0002] The existing foam-type expansion rubber strip is a double-layer product, which is divided into a foam layer and a bonding layer. The bonding layer mainly plays a bonding role, and the foaming layer plays a sealing role. However, because the adhesive layer cannot be foamed, it cannot seal some small gaps. The foamed layer has no bonding ability with the substrate, so the product often cannot completely seal the cavity, which reduces the noise reduction function of the product. . [0003] Moreover, the expansion ratio of the existing expansion rubber strip is only 30%-200%, which often makes the product unable to completely seal the cavity, resulting in a relatively poor sound insulation and noise ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J107/00C09J123/22C08J9/10
CPCC08J9/103C08J9/105C08J2203/04C08J2307/00C08J2423/22C08L2205/035C09J107/00C08L23/22
Inventor 秦安康邹明选吴海涛
Owner 科建高分子材料(上海)股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com