Manufacturing process for titanium alloy Huck rivet

A production process, titanium alloy technology, applied in the field of titanium alloy Huck rivet production process, can solve the problems of corrosion resistance, structural strength, surface hardness and low uniformity of structure, heavy product weight, reduced utilization rate, etc., to achieve improved structure Effects of strength and surface hardness, weight reduction, and performance improvement

Pending Publication Date: 2020-07-17
王丽
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, Huck rivets mostly use steel materials as raw materials for production, and the performance of the product such as corrosion resistance, structural strength, surface hardness and tissue uniformity is relatively low due to the limitation of raw materials, and the weight of the product is heavy, which reduces its utilization rate.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A manufacturing process of a titanium alloy Hack rivet, including the manufacture of a nail body and the manufacture of a bushing;

[0040] Nail body production includes the following steps:

[0041] Step 1, nail body blank preparation: select TC4 raw materials with appropriate specifications and quality;

[0042] Step 2, upsetting molding: the selected TC4 raw material is subjected to molds of corresponding specifications in a hot pier machine with an upsetting temperature of 350°C, and the head of the nail body, the screw rod, and the lower R of the head are upset 3 times Forming to obtain semi-finished nail body;

[0043] Step 3, cleaning: Put the semi-finished nail body into the corresponding cleaning line and pickling line to remove the surface dirt and raw material coating caused by upsetting;

[0044] Step 4, heat treatment: a. Solution heat treatment, put the cleaned nail body semi-finished product into a vacuum water quenching furnace at 900 °C for production...

Embodiment 2

[0061] A manufacturing process of a titanium alloy Hack rivet, including the manufacture of a nail body and the manufacture of a bushing;

[0062]Nail body production includes the following steps:

[0063] Step 1, nail body blank preparation: select TC4 raw materials with appropriate specifications and quality;

[0064] Step 2, upsetting molding: the selected TC4 raw material is upsetting the head of the nail body, the screw rod, and the lower head R three times through the mold of the corresponding specification in the hot pier machine with the upsetting temperature of 400°C Forming to obtain semi-finished nail body;

[0065] Step 3, cleaning: Put the semi-finished nail body into the corresponding cleaning line and pickling line to remove the surface dirt and raw material coating caused by upsetting;

[0066] Step 4, heat treatment: a. Solution heat treatment, put the cleaned nail body semi-finished product into a vacuum water quenching furnace at 900°C for production and h...

Embodiment 3

[0083] A manufacturing process of a titanium alloy Hack rivet, including the manufacture of a nail body and the manufacture of a bushing;

[0084] Nail body production includes the following steps:

[0085] Step 1, nail body blank preparation: select TC4 raw materials with appropriate specifications and quality;

[0086] Step 2, upsetting molding: the selected TC4 raw material is upsetting the head of the nail body, the screw rod, and the lower head R three times through the mold of the corresponding specification in the hot pier machine with the upsetting temperature of 500°C Forming to obtain semi-finished nail body;

[0087] Step 3, cleaning: Put the semi-finished nail body into the corresponding cleaning line and pickling line to remove the surface dirt and raw material coating caused by upsetting;

[0088] Step 4, heat treatment: a. Solution heat treatment, put the cleaned nail body semi-finished product into a vacuum water quenching furnace at 950°C for production and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing process for a titanium alloy Huck rivet. The manufacturing process is characterized by comprising the steps of rivet body manufacturing and lining manufacturing, wherein rivet body manufacturing comprises the following steps that 1, a rivet body blank is prepared; 2, upsetting forming is carried out; 3, washing is carried out; 4, heat treatment is carried out, specifically, a, solid solution heat treatment is carried out, specifically, a washed rivet body semi-finished product is put into a vacuum water quenching furnace at the temperature of 800 DEG C -950 DEG C to be subjected to production heat preservation for 1.5 h - 2 h, and then water-cooled; b, aging heat treatment is carried out, specifically, the water-cooled rivet body semi-finished product is put into a vacuum furnace at the temperature of 550 DEG C - 600 DEG C to be subjected to heat preservation for 8 h -10 h, and then air-cooled; 5, turning is carried out, specifically, the headouter diameter and the tail end thread bottom diameter of the rivet body semi-finished product subjected to heat treatment are turned; 6, centerless grinding is carried out, specifically, the turned rivet body semi-finished product is put into a centerless grinding machine to grind the rod diameter, the head R angle and the head lower supporting surface; 7, thread rolling is carried out; and 8, surface treatment is carried out to obtain a rivet body finished product. The manufacturing process is high in machining efficiency and qualified rate, and the product is excellent in corrosion resistance, structural strength, surface hardness, structure uniformity and the like.

Description

technical field [0001] The invention relates to the field of production technology of new material rivets, in particular to a production technology of titanium alloy Huck rivets. Background technique [0002] At present, Huck rivets mostly use steel materials as raw materials for production, and the performance of products such as corrosion resistance, structural strength, surface hardness and tissue uniformity is relatively low due to the limitation of raw materials, and the weight of products is relatively heavy, which reduces its utilization rate. Contents of the invention [0003] Aiming at the defects in the prior art, the present invention provides a titanium alloy with high processing efficiency and qualified rate, excellent performances such as product corrosion resistance, structural strength, surface hardness and structure uniformity, light weight and improved product utilization rate. Gram rivet manufacturing process. [0004] The technical scheme that the pres...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23P15/00C22F1/18
CPCB23P15/00C22F1/002C22F1/183
Inventor 王丽
Owner 王丽
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com