A kind of road marking paint based on geopolymer material and preparation method thereof
A technology of road markings and geopolymers, applied in coatings and other directions, can solve problems such as environmental pollution and resource waste, and achieve the effects of reducing environmental pollution, saving costs, and smooth and dense coatings
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0019] Dry, grind, and sieve the steel slag to make it into a powder with a particle size within the range of 300 to 400 mesh; mix 700g of steel slag powder, 400g of 200 mesh ash calcium powder, 200g of white cement with a strength grade of 42.5, and 200g of 100 mesh Glass beads, 380g heavy calcium powder, 100g rutile titanium dioxide, 20g VEA latex powder, 5g polypropylene fiber with a length of 3mm, 4g sodium hexametaphosphate, 2g powder polycarboxylate water reducer, 4g xanthan gum, etc. Put the material into the blender, stir well, and then seal the package, which is the A component.
[0020] Dissolve 100g of sodium hydroxide and 60g of sodium sulfate in 1540g of deionized water, then slowly add 300g of silica sol into the solution, stir well, seal and package to obtain component B.
[0021] When in use, the two components A and B are mixed according to the mass ratio of 1.5:1, and then stirred at a high speed to obtain a road marking paint slurry.
[0022] Apply the slur...
Embodiment 2
[0024] Dry, grind, and sieve the red mud to make it into a powder with a particle size within the range of 300-400 mesh; mix 800g of red mud powder, 300g of high-strength gypsum powder, 300g of 200-mesh ash calcium powder, and 300g of 100-mesh glass micro Beads, 220g heavy calcium powder, 40g rutile titanium dioxide, 40g resin powder, 10g polypropylene fiber with a length of 5mm, 4g sodium tripolyphosphate, 6g powder polycarboxylate water reducer, 2g xanthan gum and other materials are added In a blender, stir well and evenly, and then seal the package, which is the A component.
[0025] Dissolve 100g of potassium hydroxide and 50g of potassium sulfate in 1450g of deionized water, then slowly add 400g of silica sol into the solution, stir well, seal and package to obtain component B.
[0026] When in use, the two components A and B are mixed according to the mass ratio of 2:1, and then stirred at a high speed to obtain a road marking paint slurry.
[0027] Apply the slurry on...
Embodiment 3
[0029] Dry, grind, and sieve fly ash and steel slag to make it a powder with a particle size ranging from 300 to 400 mesh; mix 300g fly ash powder, 400g steel slag powder, 300g 200 mesh quicklime powder, and 100g high-strength Gypsum powder, 400g 100-mesh glass beads, 300g Shuangfei powder, 40g talcum powder, 100g iron oxide yellow, 60g VEA latex powder, 7g polypropylene fiber with a length of 3mm, 5g sodium hexametaphosphate, 1g xanthan gum and other materials Add it into a blender, stir it well, and then seal it and package it as component A.
[0030] Dissolve 50g of sodium hydroxide, 50g of potassium hydroxide, and 30g of sodium sulfate in 1670g of deionized water, then slowly add 200g of silica sol into the solution, stir well, seal and package to obtain component B.
[0031] When in use, the two components A and B are mixed according to the mass ratio of 1:1, and then stirred at a high speed to obtain a road marking paint slurry.
[0032] Apply the slurry on the road sur...