MAB phase ceramic-metal layered composite material as well as preparation method and application thereof

A technology of composite materials and metal layers, applied in the field of materials, can solve the problems of electrical conductivity, thermal conductivity and strength, etc., and achieve excellent oxidation resistance

Active Publication Date: 2020-11-03
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] CN 102703850 A discloses a ternary boron nitride ceramic coating containing cerium oxide and a preparation method thereof. The coating uses Mo powder, Fe powder and FeB powder as raw materials to prepare Mo on a Q235 steel substrate. 2 FeB 2 Ternary nitride ceramic coating improves the wear resistance of the coating, but its electrical conductivity, thermal conductivity and strength still need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • MAB phase ceramic-metal layered composite material as well as preparation method and application thereof
  • MAB phase ceramic-metal layered composite material as well as preparation method and application thereof
  • MAB phase ceramic-metal layered composite material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0083] This embodiment provides a preparation method of MAB phase ceramic-metal layered composite material, the preparation method comprising the following steps:

[0084] (1) Preparation of MAB phase slurry:

[0085] (a) Dissolving PMMA in anisole, stirring at 450r / min for 3h to clarification, obtaining an anisole solution of PMMA with a concentration of 12wt%;

[0086] (b) mixing the MoAlB powder with a particle diameter D50 of 12 μm and the anisole solution of PMMA obtained in step (a), stirring at 450 r / min for 3 h to disperse evenly, and obtaining a MAB phase slurry with a volume fraction of 15%;

[0087] (2) Spray the MAB phase slurry obtained in step (1) on the surface of aluminum foil with an average thickness of 18 μm, and the spray thickness is 10 μm;

[0088] (3) drying and solidifying the aluminum foil sprayed with the MAB phase slurry in step (2), and then laminating to obtain a laminated blank, the number of laminated layers is n≥2, and n is a positive integer; ...

Embodiment 2

[0093] This embodiment provides a preparation method of a MAB phase ceramic-metal layered composite material, except that the volume fraction of the MAB phase slurry in step (b) is 10%, the rest are the same as in Embodiment 1.

Embodiment 3

[0095] This embodiment provides a method for preparing a MAB phase ceramic-metal layered composite material, except that the volume fraction of the MAB phase slurry in step (b) is 20%, the rest are the same as in Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average thicknessaaaaaaaaaa
The average thicknessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides an MAB phase ceramic metal layered composite material and a preparation method and application thereof. The composite material comprises metal layers and MAB phase layers whichare alternately stacked, wherein the MAB phase layers are attached to the metal layers; the preparation method of the composite material comprises the following steps: preparing MAB phase slurry; coating the MAB phase slurry on the surface of a metal substrate; drying and curing the metal base material coated with the MAB phase slurry, and then performing lamination to obtain a laminated blank; preprocessing the laminated blank to obtain a pre-product; and sintering the pre-product, and cooling the sintered product along with the furnace to obtain the MAB-phase ceramic metal layered compositematerial. The composite material has the advantages of high interface strength, light weight, high strength, wear resistance and corrosion resistance, and can meet the application requirements in thefields of carrying tools, power transmission and transformation or military materials.

Description

technical field [0001] The invention belongs to the technical field of materials and relates to a composite material, in particular to a MAB phase ceramic-metal layered composite material and a preparation method and application thereof. Background technique [0002] Aluminum matrix composite material is a material with strong vitality that emerges in response to the needs of modern scientific development. It is composed of two or more materials with different properties through various technological means. [0003] Aluminum has many characteristics in making composite materials, such as light weight, low density, good plasticity, and aluminum matrix composite technology is easy to master and easy to process. In addition, aluminum matrix composite materials have high specific strength and specific stiffness, good high temperature performance, and are more durable Fatigue and more wear-resistant, good damping performance, low thermal expansion coefficient, can meet specific m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B15/01B32B15/20B32B33/00B32B37/06B32B37/10
CPCB32B15/01B32B15/20B32B33/00B32B37/06B32B37/10B32B2307/202B32B2307/302B32B2307/558B32B2307/536B32B2307/554B32B2255/20B32B2255/06
Inventor 王钰赵栋王秦欢
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com