NiTe2/MXene composite material and preparation method and application thereof
A composite material and mixed solution technology, applied in the field of nanomaterials, can solve the problems of poor electrochemical performance, electrode material crushing, falling off, etc., and achieve the effects of improving electrical conductivity, low cost, and increasing active sites.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0039] The invention provides a NiTe 2 The preparation method of / MXene composite material, wherein, NiTe 2 For the synthesis method, please refer to:
[0040] "Lei Yuxi. Hydrothermal Synthesis, Modification and Properties of Various Transition Metal Telluride Nanostructures [D]. Shaanxi Normal University, 2018.".
Embodiment 1
[0042] A kind of NiTe 2 The preparation method of / MXene composite material, comprises the following steps:
[0043] (1) Take 0.1mmol MXene (Ti 3 C 2 T x ) into ethanol, magnetically stirred for 1 hour, and configured into a 1 mg / ml dispersion;
[0044] (2) 0.1mmol NiCl 2 ·6H 2 O and 0.2mmol sodium tellurite were added to the dispersion described in step (1), and stirred for 5 hours to obtain a mixed solution;
[0045] (3) Transfer the mixed solution into a reaction kettle with a capacity of 100ml, seal it, place it in an oven, heat it to 100°C, keep it warm for 10h, and then cool it to room temperature;
[0046] (4) The product obtained in step (3) was centrifuged for 4 minutes under the condition of 4000r / min with a centrifuge, the supernatant was discarded, and the filter residue was washed alternately with deionized water and absolute ethanol for 3 times, and then carried out in a vacuum oven. Drying, drying temperature 60 ° C, drying time 9 hours, collected to obtai...
Embodiment 2
[0050] A kind of NiTe 2 The preparation method of / MXene composite material, comprises the following steps:
[0051] (1) Take 0.2mmol MXene (Ti 3 C 2 T x ) into ethanol, magnetically stirred for 3 hours, and configured into a 50 mg / ml dispersion;
[0052] (2) 0.2mmol NiCl 2 ·6H 2 O and 0.25mmol sodium tellurite were added to the dispersion described in step (1), and stirred for 10 hours to obtain a mixed solution;
[0053] (3) Transfer the mixed solution into a 50ml reaction kettle, seal it, place it in an oven, heat it to 150°C, keep it warm for 16h, and then cool it down to room temperature;
[0054] (4) The product obtained in step (3) was centrifuged for 7 minutes under the condition of 6000r / min with a centrifuge, the supernatant was discarded, and the filter residue was washed alternately with deionized water and absolute ethanol for 3 times, and then carried out in a vacuum oven. Drying, drying temperature 60 ° C, drying time 12 hours, collected to obtain NiTe 2 ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap