Purple glaze for insulator processing and its processing method

A processing method and technology for insulators, which are applied to the purple glaze for insulator processing and its processing field, can solve the problem that the glazing strength, the porcelain bending strength, the insulator breakdown rate fail to meet the requirements, and the color glaze and the electric porcelain body cannot be combined. To solve the problems of good quality and so on, to achieve the effect of shortening the time of ball milling

Active Publication Date: 2022-02-11
CHONGQING PIGEON ELECTRIC PORCELAIN CO LTD
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention intends to provide purple glaze for processing insulators and its processing method to solve the problem that existing color glazes are not well bonded to electric porcelain bodies, and the indicators such as glazing strength, porcelain bending strength, and insulator breakdown rate cannot meet the requirements. asked questions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Purple glaze for insulator processing and its processing method
  • Purple glaze for insulator processing and its processing method
  • Purple glaze for insulator processing and its processing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0117] The present embodiment discloses a glazed insulator violet processing, comprising feed mass parts: 28 parts of potassium feldspar, albite 8 parts, 6 parts of ball clay, 21 parts hard kaolin, calcined talc 12 parts, 7 parts limestone , 24 parts of quartz powder, 2 parts of barium carbonate, 7 parts of purple color group.

[0118] Purple enamel present embodiment comprises the following chemical composition:

[0119] SiO 2

Al 2 O 3

FE 2 O 3

Cao MGO K 2 O

NA 2 O

Bao LL 65.4％ 15.1％ 0.5％ 3.2％ 3.5％ 2.8％ 1.3％ 1.8％ 6.4％

[0120] Processing this embodiment the insulator glaze violet processing method, comprising the steps of:

[0121](1) Prepare the following material: 28 copies of potassium, 8 sodium stones, 6 ball clay, 21 hard kaolins, 12 calcined talones, 7 limestone, 24 pieces of quartz powder, bicarbonate 2 copies of purple color foundation.

[0122] (2) Ball milling: Ball mills using a ball mill; ball mills in the ball: Spherical:...

Embodiment 2

[0138] This example discloses a purple glaze for insulator processing, including the following mass parts: 26 potassium waith, 5 sodium stones, 4 copper clay, 20 hard kaolins, 9 calcined talc, 5 limestone 22 copies of quartz powder, 1.2 parts of bicarbonate, 7 purple raw groups.

[0139] The purple glaze in this embodiment includes the following chemical components:

[0140] SiO 2

Al 2 O 3

FE 2 O 3

Cao MGO K 2 O

NA 2 O

Bao LL 65.7％ 14.8％ 0.4％ 3.5％ 3.7％ 2.8％ 1.6％ 0.8％ 6.7％

[0141] The processing method of the purple glaze for the insulator processing, including the steps of:

[0142] (1) Prepare the following material: 26 potassium wax, 5 sodium stones, 4 copper clants, 20 hard kaolins, 9 calcined talones, 5 limestone, 22 quartz powder, bicarbonate 1.2 parts, 7 copies of purple raw group.

[0143] (2) Ball mill: Ball mills using a ball mill; ball mills in the raw material: Spherical: The mass ratio of water is 1: 2.4-2.6: 0.7-0.9. The ...

Embodiment 3

[0147] This example discloses a purple glaze for insulator processing, a raw material of the following mass parts: 31 potassium waith, 9 sodium stones, 7 copper clay, 22 hard kaolins, 13 calcined talc, 9 pieces of limestone 26 pieces of quartz powder, 3 copies of bicarbonate, 8 purple chromosomes.

[0148] The purple glaze in this embodiment includes the following chemical components:

[0149] SiO 2

Al 2 O 3

FE 2 O 3

Cao MGO K 2 O

NA 2 O

Bao LL 65.1％ 14.7％ 0.6％ 3.4％ 3.5％ 2.6％ 1.4％ 2.1％ 6.6％

[0150] The processing method of the purple glaze for the insulator processing, including the steps of:

[0151] (1) Prepare the number of raw materials of the following mass: 31 potassium waith, 9 sodium stones, 7 ball clay, 22 hard kaolins, 3 calcined talones, 9 limestone, 26 quartz powder, bicarbonate 3 copies of purple raw groups.

[0152] (2) Ball mill: Ball mills using a ball mill; ball mills in the raw material: Spherical: The mass ratio of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of electric porcelain glazes, in particular to purple glaze for insulator processing and a processing method thereof, purple glaze for insulator processing, 26-31 parts of potassium feldspar, 5-10 parts of albite, 3-7 parts of ball clay, 19-23 parts of hard kaolin, 9-13 parts of calcined talc, 5-9 parts of limestone, 22-26 parts of quartz powder, 1-3 parts of barium carbonate, 6-10 parts of purple color base. After the insulator is made into porcelain with the purple glaze and the green body, the surface of the porcelain body is bright purple, smooth and bright, delicate and moist, which can well meet the customer's demand for purple electric porcelain. Moreover, the purple glaze of this program can be well combined with the green body. After the porcelain is formed, an excellent intermediate layer can be produced between the glaze and the green body, which can greatly improve the performance of the porcelain (improving the strength of the porcelain by more than 22%). The development of the glaze achieves the design purpose and meets the company's technology and industry standards.

Description

Technical field [0001] The present invention belongs to the technical field of electric porcelain glaze, and is specifically related to the purple glaze and its processing method thereof for insulator processing. Background technique [0002] Electric porcelain refers to an aluminum aluminum aluminous, kaolin, and long-standing natural minerals such as high-temperature fire-fired, including a type of porcelain insulator, including various line insulators and electricity electrical appliances, and other tapers Isolation or support for insulation components. Electric porcelain is an important foundation device for the power industry, and the electric porcelain manufacturing is a national "Eleventh Five-Year" period, which is the foundation industry of the national economy. [0003] The electric porcelain surface is usually coated with electric ceramic glaze, and the electric porcelain glaze means the glaze of the electric chip-containing blank, and the glaze can improve the electri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/86C04B41/5022
Inventor 姚绍明
Owner CHONGQING PIGEON ELECTRIC PORCELAIN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More