Low-emission low-warpage long glass fiber reinforced polypropylene composite material suitable for automobile skylight guide rail and preparation method and application of composite material

A composite material and a technology for automobile sunroof, which is applied in the field of low emission and low warpage long glass fiber reinforced polypropylene composite material and its preparation, can solve the problems of unfavorable automobile lightweight, complicated preparation process, heavy metal sunroof guide rail, etc. Achieve the effect of reducing the anisotropic orientation gap, reducing the difference, and reducing the degree of warpage

Active Publication Date: 2020-12-04
中广核俊尔(浙江)新材料有限公司 +1
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The manufacturing process of traditional metal sunroof guide rails is complicated, and many pollution sources are produced along with the product manufacturing, such as waste cutting fluid, metal scraps, noise, etc. At the same time, the weight of metal sunroof guide rails is relatively large, which is not conducive to the promotion of automobile lightweight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-emission low-warpage long glass fiber reinforced polypropylene composite material suitable for automobile skylight guide rail and preparation method and application of composite material
  • Low-emission low-warpage long glass fiber reinforced polypropylene composite material suitable for automobile skylight guide rail and preparation method and application of composite material
  • Low-emission low-warpage long glass fiber reinforced polypropylene composite material suitable for automobile skylight guide rail and preparation method and application of composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036]Below in conjunction with specific embodiment, further illustrate the present invention. It should be understood that these examples are only used to illustrate the present invention and are not intended to limit the scope of the present invention. The operating methods not indicated in the following examples are generally in accordance with conventional conditions, or in accordance with the conditions suggested by the manufacturer.

[0037] The raw material proportions of Examples 1-3 and Comparative Examples 1-4 are shown in Table 1 and Table 2 respectively. Unless otherwise specified, the units or parts are parts by weight, and the length of the tetraacicular zinc oxide whisker needles is 10-50 μm, 0.5-5μm at the root of the needle, 20-50 aspect ratio, and 0.2±0.1g / cm apparent density 3 , real density 5.4±0.2g / cm 3 , heat resistance greater than 800 ℃.

[0038] The preparation method of embodiment 1~3 and comparative example 1~4 comprises the following steps:

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-emission low-warpage long glass fiber reinforced polypropylene composite material suitable for an automobile skylight guide rail, a preparation method of the composite material and an application of the composite material in preparation of the automobile skylight guide rail. The low-emission low-warpage long glass fiber reinforced polypropylene composite material comprises the following raw materials in parts by weight: 30-60 parts of polypropylene, 40-70 parts of continuous glass fibers, 3-10 parts of a compatilizer, 0.1-1.5 parts of an antioxidant, 0-1 parts ofa lubricant, 8-20 parts of a thermoplastic elastomer, 0.2-2 part of a nucleating agent, 0.5-10 part of tetrapod-like zinc oxide whiskers and 0.2-3 part of a deodorant. The deodorant comprises a porousaluminum-silicon compound, and the pore diameter of the deodorant is 0.05-20 [mu]m. The preparation method comprises the following steps: uniformly mixing polypropylene, a compatilizer, an antioxidant, a nucleating agent, dried tetrapod-like zinc oxide whiskers and a selectively added lubricant to prepare master batch, blending the master batch with a thermoplastic elastomer and a deodorant, carrying out melt extrusion, and finally, carrying out continuous glass fiber impregnation and coating.

Description

technical field [0001] The invention relates to the technical field of polypropylene composite materials, in particular to a low emission and low warpage long glass fiber reinforced polypropylene composite material suitable for automobile sunroof guide rails and its preparation method and application. Background technique [0002] With the rapid development of the national economy, high-performance, low-cost thermoplastic resin-based composite materials have been widely used. It is an effective shortcut for the development of new materials to prepare fiber-reinforced thermoplastic resin-based composites (new structural composites, functional composites, etc.) by adding reinforcing fibers to thermoplastic resins and modifying the resins. This has become the consensus of the scientific and technological circles and the industry circles, and it is also the best technical route to realize the engineering of general-purpose plastics, the functionalization of engineering plastics,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/14C08L23/08C08L53/02C08L75/04C08L51/06C08K13/04C08K7/14C08K7/08C08K7/26C08J5/04
CPCC08J5/043C08J2323/12C08J2323/14C08J2423/08C08J2453/02C08J2475/04C08J2451/06C08K13/04C08K7/14C08K7/08C08K7/26
Inventor 郑云磊陈永波周琴恩孙心克安孝善周云国李俊郑京连陈晓敏
Owner 中广核俊尔(浙江)新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap