Manufacturing process of fishing net thread with low cost and good flame retardance

A production process and technology for fishing net threads, which are applied in the manufacture of fire-retardant and flame-retardant filaments, rayon manufacturing, and single-component polyamide rayon filaments, etc. Raw material composition and other issues, to achieve the effect of strong compatibility and binding ability and stability, environmental protection and cost reduction

Inactive Publication Date: 2020-12-04
巢湖市方太渔具有限责任公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing amount of nylon 66 fishing net line is relatively large, and long-term production, processing and use will produce a large amount of waste, and these wastes are mostly disposed of by incineration and landfill, which is not conducive to e

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0025] Example 1

[0026] Low-cost production process of twine good flame retardancy, comprising the steps of:

[0027] (1) Extraction of waste material:

[0028] . A The scrap nylon twine 66 into the sulfuric acid solution, and then acetic anhydride was added, sonicated well and then stirred, followed by cooling and crystallization, and finally filtered to obtain filtrate A standby;

[0029] . B was added to the filtrate obtained operating a barium sulfate A, mix well before addition of calcium hydroxide and nanofiller, the reaction process after 3h was filtered to obtain the filtrate B backup;

[0030] . C operation b B obtained filtrate by distillation under reduced pressure, to give waste material after the completion of use;

[0031] (2) Nylon 66 wet resin prepared:

[0032] a. The step (1) of waste material obtained with adipic acid, blended with an ethanol solution, after neutralization and a salt precipitated was then filtered, washed alcohol, after the drying process, is ...

Example Embodiment

[0044] Example 2

[0045] Low-cost production process of twine good flame retardancy, comprising the steps of:

[0046] (1) Extraction of waste material:

[0047] . A The scrap nylon twine 66 into the sulfuric acid solution, and then acetic anhydride was added, sonicated well and then stirred, followed by cooling and crystallization, and finally filtered to obtain filtrate A standby;

[0048] . B was added to the filtrate obtained operating a barium sulfate A, mix well before addition of calcium hydroxide and nanofiller, treatment 3.3h the reaction was filtered to obtain the filtrate B backup;

[0049] . C operation b B obtained filtrate by distillation under reduced pressure, to give waste material after the completion of use;

[0050] (2) Nylon 66 wet resin prepared:

[0051] a. The step (1) of waste material obtained with adipic acid, blended with an ethanol solution, after neutralization and a salt precipitated was then filtered, washed alcohol, after the drying process, is co...

Example Embodiment

[0063] Example 3

[0064] Low-cost production process of twine good flame retardancy, comprising the steps of:

[0065] (1) Extraction of waste material:

[0066] . A The scrap nylon twine 66 into the sulfuric acid solution, and then acetic anhydride was added, sonicated well and then stirred, followed by cooling and crystallization, and finally filtered to obtain filtrate A standby;

[0067] . B was added to the filtrate obtained operating a barium sulfate A, mix well before addition of calcium hydroxide and nanofiller, the reaction process after 3.5h was filtered to obtain the filtrate B backup;

[0068] . C operation b B obtained filtrate by distillation under reduced pressure, to give waste material after the completion of use;

[0069] (2) Nylon 66 wet resin prepared:

[0070] a. The step (1) of waste material obtained with adipic acid, blended with an ethanol solution, after neutralization and a salt precipitated was then filtered, washed alcohol, after the drying process, i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing process of a fishing net thread with low cost and good flame retardance, which belongs to the technical field of fishing net thread manufacturing, and comprisesthe steps of (1) waste material extraction, (2) nylon 66 wet resin preparation, and (3) finished fishing net thread manufacturing. The invention provides a fishing net thread manufacturing process which is low in overall cost and beneficial to application and popularization. The fishing net thread prepared through the manufacturing process has the characteristics of being good in temperature resistance and flame retardance and high in strength and weather resistance.

Description

Technical field [0001] The present invention belongs to the technical field of manufacturing fishing nets, particularly relates to a low-cost flame retardant twine good production process. Background technique [0002] Since my country fishnet material since the early sixties and gradually try synthetic material, after decades of application, basically instead of the original cotton material, fishnet material from the current domestic and international use of the situation, there are sub-species of polyamide (PA ), polyester (PES), polyethylene (PE), polypropylene (PP), polyvinyl chloride (PVC), polyvinyl alcohol (PVA), polyvinylidene chloride (PVD) seven categories of points from the fiber form : there monofilament, multifilament, split fibers, etc., its varieties and specifications are more complete, the fiber strength index compared with similar foreign products, are relatively close. The existing amount of nylon fishing nets line 66 is larger, long-term production, processing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/06C08L83/04C08L85/02C08K5/098C08K3/32D01F6/90D01F1/10D01F1/07C08G69/28
CPCC08G69/28C08K2003/3045C08K2201/011C08L77/06C08L2201/02C08L2201/08C08L2207/20D01F1/07D01F1/10D01F6/90C08L83/04C08L85/02C08K5/098C08K3/32
Inventor 徐宏伟徐宏涛
Owner 巢湖市方太渔具有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap