Grinding aid as well as production process and application thereof

A production process and technology of grinding aids, applied in the field of cement additives, can solve the problems of rising costs of grinding aids, affecting popularization and use, and high prices, and achieve the effects of improving grinding aiding effects, promoting hydration reaction process, and reducing usage

Active Publication Date: 2020-12-08
北京金隅水泥节能科技有限公司 +3
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above-mentioned existing technical solutions have the following defects: the amount of triethanolamine in the above-mentioned cement grinding aid accounts for more than 30%. Since tri

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] A kind of production technology of grinding aid, comprises the following steps:

[0058] S1: Mix 3g of triethanolamine and 9g of acetic acid evenly, stir and react at 60°C for 3h, then cool to 20°C, adjust the pH value to 6, wash away the acetic acid to obtain triethanolamine acetate; mix 1g of butyl Mix triphenylphosphine bromide with 30g of water, then add 2g of sodium dodecylbenzenesulfonate, stir for 4h, let it stand for liquid separation, and remove the viscous liquid in the lower layer to obtain butyltriphenyl dodecylbenzenesulfonate phosphorus;

[0059] S2: Mix triethanolamine acetate, 7g p-aminophenol, butyltriphenylphosphine dodecylbenzenesulfonate and 75g water evenly;

[0060] S3: Add 3g of acid-type sophorolipid, 13g of sodium alginate, 1g of aminophenol, 14g of biosurfactant, 4.375g of acrylic acid and 2.25g of propylene alcohol to the mixture obtained in step S2, and mix well to obtain a grinding aid agent.

[0061] Wherein, the preparation method of bi...

Embodiment 2

[0069] A kind of production technology of grinding aid, comprises the following steps:

[0070] S1: Mix 7g of triethanolamine and 1g of acetic acid evenly, stir and react at 60°C for 3h, then cool to 20°C, adjust the pH value to 6, wash away the acetic acid to obtain triethanolamine acetate; mix 5g of butyl Triphenylphosphine bromide is mixed with 15g of water, then 8g of sodium dodecylbenzenesulfonate is added, stirred for 4h, left to stand for liquid separation, and the lower layer of viscous liquid is removed to obtain butyltriphenyl dodecylbenzenesulfonate phosphorus;

[0071] S2: Mix triethanolamine acetate, 3g p-aminophenol, butyltriphenylphosphine dodecylbenzenesulfonate and 70g water evenly;

[0072] S3: Add 9g of acid-type sophorolipid, 7g of sodium alginate, 7g of aminophenol, 6g of biosurfactant, 6.125g of acrylic acid and 7.875g of acrylic alcohol to the mixture obtained in step S2, and mix well to obtain grinding aid agent.

[0073] Wherein, the preparation met...

Embodiment 3

[0081] A kind of production technology of grinding aid, comprises the following steps:

[0082] S1: Mix 5g of triethanolamine and 5g of acetic acid evenly, stir and react at 62.5°C for 3.25h, then cool to 21°C, adjust the pH value to 7, wash away the acetic acid to obtain triethanolamine acetate; Base triphenylphosphine bromide mixed with 22.5g of water, then add 5g of sodium dodecylbenzenesulfonate, stir for 4.25h, let stand for liquid separation, take off the viscous liquid in the lower layer to obtain butyl dodecylbenzenesulfonate Triphenylphosphine;

[0083] S2: Mix triethanolamine acetate, 5g p-aminophenol, butyltriphenylphosphine dodecylbenzenesulfonate and 72.5g water evenly;

[0084] S3: Add 6g of acid-type sophorolipid, 10g of sodium alginate, 4g of aminophenol, 10g of biosurfactant, 5.4g of acrylic acid and 6.6g of propylene alcohol to the mixture obtained in step S2, and mix well to obtain grinding aids agent.

[0085] Wherein, the preparation method of biosurfac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a grinding aid as well as a production process and application thereof, and belongs to the technical field of cement additives. The grinding aid is prepared from the followingraw materials, by weight: 3-7 parts of triethanolamine, 1-9 parts of acetic acid, 1-5 parts of butyltriphenylphosphonium bromide, 85-105 parts of water, 2-8 parts of sodium dodecyl benzene sulfonate,3-7 parts of p-aminophenol, 3-9 parts of acid sophorolipid, 7-13 parts of sodium alginate, 1-7 parts of aminophenol, 6-14 parts of biosurfactant and 10-14 parts of hyperdispersant. The mixing amountof the grinding aid in the cement clinker grinding process is 0.03%-0.05%, and the grinding aid has the effect of improving the cement clinker grinding efficiency so as to reduce the energy consumption in the cement clinker grinding process.

Description

technical field [0001] The invention relates to the technical field of cement additives, in particular to a grinding aid and its production process and application. Background technique [0002] After sending cement clinker and other materials into the ball mill, during the grinding process, due to the gradual refinement of the material particles, the specific surface area increases, and the particles adsorb each other, which is prone to agglomeration, which reduces the grinding efficiency and increases The energy consumption of the grinding process is reduced, so grinding aids are usually added during the grinding process. The grinding aids can prevent particle agglomeration and improve the fluidity of the material, thereby increasing the efficiency of grinding and reducing the energy consumption of the grinding process. [0003] Existing reference number is the Chinese patent of CN103819118A, which discloses a cement grinding aid, the addition of each component is triethan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/38C04B103/52
CPCC04B40/0039C04B2103/52C04B24/003C04B24/02C04B24/122C04B24/14C04B24/38C04B2103/40C04B2103/408C04B24/20C04B24/04
Inventor 任建波张露瑶苏鹏举张三丰田静陈志明唐哲马军民路海峰
Owner 北京金隅水泥节能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap