A kind of warm and antibacterial school uniform fabric and preparation method thereof

A technology for fabrics and school uniforms, applied in the field of warming and antibacterial school uniform fabrics and its preparation, can solve the problem of poor comprehensive performance such as moisture absorption and perspiration performance, elastic wear resistance and mechanical strength, lack of comprehensive performance, warming and antibacterial school uniform fabrics, and easy mold Odor and other problems, to achieve the effect of good moisture absorption and perspiration performance, not easy to breed bacteria, and high antibacterial rate

Active Publication Date: 2022-04-05
润克(集团)股份有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 1. The thermal performance is poor, the antibacterial effect is poor, and it is easy to mold and smell after sweating during exercise;
[0006] 2. The overall performance of moisture absorption and perspiration performance, elasticity, wear resistance and mechanical strength is poor, and there is a lack of a warm and antibacterial school uniform fabric with excellent comprehensive performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of warm and antibacterial school uniform fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0079] A warming and antibacterial school uniform fabric, the warming and antibacterial school uniform fabric is made of warming and antibacterial composite fiber through knitting or weaving process;

[0080] The warm-keeping and antibacterial composite fiber includes an inner layer and an outer layer;

[0081] The outer layer is coated on the outer surface of the inner layer, and the cross-sectional profile of the outer layer is circular;

[0082] The ratio of the cross-sectional area of ​​the inner layer to the outer layer is 1:1.35-1.55;

[0083] The inner layer is made of raw materials comprising the following parts by weight:

[0084] Polyhexamethylene adipamide: 88-98 parts,

[0085] Polyurethane elastomer: 5-9 parts;

[0086] The outer layer is made of raw materials comprising the following parts by weight:

[0087] Nylon 56: 65-75 parts,

[0088] Polyhexamethylene adipamide: 15-20 parts,

[0089] Polyurethane elastomer: 20-28 parts,

[0090] 5-7 parts of airgel ...

Embodiment 2

[0133] A warming and antibacterial school uniform fabric, the warming and antibacterial school uniform fabric is made of warming and antibacterial composite fiber through knitting or weaving process;

[0134] The warm-keeping and antibacterial composite fiber includes an inner layer and an outer layer;

[0135] The outer layer is coated on the outer surface of the inner layer, and the cross-sectional profile of the outer layer is circular;

[0136] The ratio of the cross-sectional area of ​​the inner layer to the outer layer is 1:1.35;

[0137] The inner layer is made of raw materials comprising the following parts by weight:

[0138] Polyhexamethylene adipamide: 88 parts,

[0139] Polyurethane elastomer: 5 parts;

[0140] The outer layer is made of raw materials comprising the following parts by weight:

[0141] Nylon 56: 65 parts,

[0142] Polyhexamethylene adipamide: 15 parts,

[0143]Polyurethane elastomer: 20 parts,

[0144] Airgel silica 5 parts,

[0145] 3 parts...

Embodiment 3

[0170] A warming and antibacterial school uniform fabric, the warming and antibacterial school uniform fabric is made of warming and antibacterial composite fiber through knitting or weaving process;

[0171] The warm-keeping and antibacterial composite fiber includes an inner layer and an outer layer;

[0172] The outer layer is coated on the outer surface of the inner layer, and the cross-sectional profile of the outer layer is circular;

[0173] The ratio of the cross-sectional area of ​​the inner layer to the outer layer is 1:1.55;

[0174] The inner layer is made of raw materials comprising the following parts by weight:

[0175] Polyhexamethylene adipamide: 98 parts,

[0176] Polyurethane elastomer: 9 parts;

[0177] The outer layer is made of raw materials comprising the following parts by weight:

[0178] Nylon 56: 75 parts,

[0179] Polyhexamethylene adipamide: 20 parts,

[0180] Polyurethane elastomer: 28 parts,

[0181] Airgel silica 7 parts,

[0182] 4 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a warm-keeping and antibacterial school uniform fabric and a preparation method thereof. The warm-keeping and antibacterial school uniform fabric is prepared from a warm-keeping and antibacterial composite fiber through a knitting or weaving process; the warm-keeping and antibacterial composite fiber includes an inner layer and an outer layer. layer; the outer layer is coated on the outer surface of the inner layer, and the cross-sectional profile of the outer layer is circular; the ratio of the cross-sectional area of ​​the inner layer to the outer layer is 1:1.35 to 1.55; the The inner layer is made of the following raw materials in parts by weight: polyhexamethylene adipamide: 88-98 parts, polyurethane elastomer: 5-9 parts. The special warm-keeping and antibacterial composite fiber adopted in the warm-keeping and antibacterial school uniform fabric of the present invention has an inner layer and an outer layer structure, has a high antibacterial rate, and has a good antibacterial effect. Good performance, good resilience, soft hand feeling, comfortable to wear; good moisture absorption and perspiration performance, high tensile strength, good mechanical properties; suitable as school uniform fabric.

Description

technical field [0001] The invention relates to the technical field of textile fabrics, in particular to a warm-keeping and antibacterial school uniform fabric and a preparation method thereof. Background technique [0002] Fabric is the material used to make clothing. As one of the three elements of clothing, fabrics can not only interpret the style and characteristics of clothing, but also directly affect the color and shape of clothing. Among them, functional fabrics refer to fabrics with certain special properties and uses, such as waterproof, windproof, breathable, moisture-permeable, warm, oil-proof, easy to decontaminate, anti-bacterial and deodorizing, anti-ultraviolet, anti-static, anti-radiation, Anti-flame retardant, high temperature resistance, acid and alkali resistance and other functions. The functional fabrics on the market are mainly clothing fabrics, which are mostly used in outdoor sportswear and high-end casual wear. [0003] Students, especially prima...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04B1/18D04B21/18D03D15/292D03D15/50D03D15/56D03D15/573D01D5/34D01F8/16D01F8/12D01F1/10A41D31/30A41D31/24A41D31/18A41D31/12A41D31/06C08G18/32C08G18/42C08G18/48C08G18/61C08G18/73
CPCD04B1/18D04B21/18D01D5/34A41D31/06A41D31/18A41D31/30A41D31/12A41D31/24D01F8/12D01F8/16D01F1/103D01F1/10C08G18/4238C08G18/61C08G18/73C08G18/4825C08G18/3206A41D2400/10A41D2500/10A41D2500/20D10B2401/061D10B2401/062D10B2401/063D10B2401/13D10B2501/04D03D15/56D03D15/292D03D15/50D03D15/58D03D15/52D03D15/573
Inventor 钟志娥
Owner 润克(集团)股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com