Environment-friendly interior wall negative ion formaldehyde removal coating and preparation method thereof

A technology of negative ions and negative ion powder, which is applied in the direction of coating, etc., can solve the problems of the decrease of negative ion induction ability, the decrease of pyroelectric and piezoelectric properties of negative ion materials, the low ability of deodorization and formaldehyde removal, etc., to achieve good cleanness Odor and formaldehyde removal ability, good stability, good dispersion effect

CN112226117AInactive Publication Date: 2021-01-15佛山市净野环保材料有限公司
0 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Current Assignee / Owner
Publication Date
2021-01-15
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
Patent Text Reader

Abstract

The invention discloses an environment-friendly interior wall negative ion formaldehyde removal coating. The coating comprises the following components in parts by weight: 30-35 parts of water, 0.8-1part of a dispersing agent, 0.3-0.6 part of a defoaming agent, 0.1-0.3 part of a wetting agent, 0.2-0.4 part of a preservative, 0.5-0.8 part of a mildew preventive, 1-2 parts of an odor removal coalescing agent, 1.5-2.5 parts of an environment-friendly antifreezing agent, 18-25 parts of R706 titanium dioxide, 5-8 parts of kaolin, 3-5 parts of talcum powder, 10-15 parts of ground calcium carbonate,25-40 parts of odorless emulsion and 3-5 parts of modified negative ion powder. The coating has the following beneficial effects: the water-soluble odorless emulsion is used as a film-forming material, does not contain an organic solvent, and does not release any volatile organic compounds, and the coating is green and environment-friendly; the modified negative ion powder is added so that not only are better dispersion effect and stability achieved, but also the negative ion inducing capability is strong, and better odor removing and formaldehyde removing capabilities are achieved.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the technical field of coatings, in particular to an environment-friendly interior wall negative ion formaldehyde-removing coating and a preparation method thereof. Background technique

[0002] In today's paint market, environmentally friendly and healthy odor-free products have become the main demand of consumers.

[0003] Negative air ions are a kind of ions or ion clusters with floating points in the atmosphere. They have the functions of purifying the air, anti-oxidation, anti-aging, and eliminating free radicals in the body. They are called "air vitamins". Negative ion coatings have the effect of generating negative ions by adding powders with negative ion electric fields to the coatings. Negative ion paint has the function of environmental protection and health, mainly because the added negative ion material has a permanent electric field effect, which can generate negative ions, thereby increasing the concentration of ...

Examples

preparation example Construction

[0023] A method for preparing an environment-friendly interior wall negative ion formaldehyde-removing paint, comprising the following steps: weighing each component according to parts by weight; The antifreeze agent and environmental protection antifreeze are uniformly dispersed in water under the condition of medium-speed stirring, and then R706 titanium dioxide, kaolin, talcum powder, heavy calcium carbonate, modified negative ion powder are added, and high-speed stirring is made for 25-30 minutes to make a coating slurry. Grinding the coating slurry to make the fineness less than 40 μm, adding the deodorizing emulsion to the coating slurry, stirring at a high speed for 20-30 minutes, mixing evenly, adjusting the viscosity, and obtaining the coating.

[0024] The stirring speed of medium-speed stirring is 400-550 r / min, and the stirring speed of high-speed stirring is 1550-1700 r / min.

[0025] Water-soluble deodorizing emulsion is used as the film-forming material, which do...

Embodiment 1

[0027] Embodiment 1, a kind of environment-friendly interior wall negative ion removes formaldehyde coating, comprises the component by following parts by weight: 30 parts of water, 0.8 part of dispersant, 0.3 part of defoamer, 0.1 part of wetting agent, 0.2 part of preservative , 0.5 parts of antifungal agent, 1 part of deodorizing film-forming aid, 1.5 parts of environmental protection antifreeze, 18 parts of R706 titanium dioxide, 5 parts of kaolin, 3 parts of talcum powder, 10 parts of heavy calcium carbonate, 25 parts of deodorizing emulsion, 3 parts of modified negative ion powder.

[0028] The modified negative ion powder includes sodium polyacrylate, sodium polyphosphate, white carbon black, and Mg tourmaline powder.

[0029] Sodium polyacrylate, sodium polyphosphate, white carbon black, and Mg tourmaline powder are compounded into modified anion powder by ball milling, suspending and coating.

[0030] The mass ratio of sodium polyacrylate, sodium polyphosphate, white...

Embodiment 2

[0035] Embodiment 2, a kind of environment-friendly interior wall negative ion removes formaldehyde paint, comprises the component by following parts by weight: 32 parts of water, 0.9 part of dispersant, 0.4 part of defoamer, 0.2 part of wetting agent, 0.3 part of preservative , 0.6 parts of antifungal agent, 1.5 parts of deodorizing film-forming aid, 2 parts of environmental protection antifreeze, 20 parts of R706 titanium dioxide, 6 parts of kaolin, 4 parts of talcum powder, 12 parts of heavy calcium carbonate, 30 parts of deodorizing emulsion, 4 parts of modified negative ion powder.

[0036] The modified negative ion powder includes sodium polyacrylate, sodium polyphosphate, white carbon black, and Mg tourmaline powder.

[0037] Sodium polyacrylate, sodium polyphosphate, white carbon black, and Mg tourmaline powder are compounded into modified anion powder by ball milling, suspending and coating.

[0038] The mass ratio of sodium polyacrylate, sodium polyphosphate, white ca...