A kind of aluminum foil with graphene for lithium battery and preparation method thereof

A technology of graphene and lithium batteries, which is applied in the direction of lithium batteries, battery electrodes, non-aqueous electrolyte batteries, etc., can solve the problems of reducing the charging and discharging efficiency of lithium-ion batteries, the active material is easy to fall off, and the interaction force is weak, etc., to achieve improved Corrosion effect, avoid excessive corrosion, increase the effect of bonding area

Active Publication Date: 2021-05-28
NOZO GRP CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The positive current collector of lithium-ion batteries is usually aluminum foil, and active materials are attached to the aluminum foil. Most of the current active materials are adhered to the surface of the aluminum foil through adhesives. Due to the weak interaction between the active materials and the aluminum foil, the active materials It is easy to fall off during use, which will not only reduce the charging and discharging efficiency of the lithium-ion battery, but also lead to a lower battery life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] An embodiment of the present invention provides a method for preparing an aluminum foil with graphene for a lithium battery, comprising the following steps:

[0026] S1. Preparation of porous aluminum foil substrate

[0027] Clean the surface of the aluminum foil with a detergent to remove the lubricating film on the surface of the aluminum foil, and then clean it with deionized water.

[0028] Immerse the cleaned aluminum foil in an etchant and energize it for corrosion. The etchant includes 0.2-0.5mol / L HCl, 0.1-0.5mol / L H2O2, 0.1-0.3mol / L acetic alcohol, and the corrosion time is 1-3min. Then add triethanolamine phosphate to a concentration of 1-1.2 mol / L for passivation for 2-5 minutes to obtain an aluminum foil substrate with a porous structure on the surface, that is, a porous aluminum foil substrate.

[0029] Chloride ions have a strong corrosive effect on aluminum foil under acidic conditions, and acetic alcohol can be used as a catalyst to accelerate the react...

Embodiment 1

[0042] S101. Use a cleaning agent to clean the surface of the aluminum foil, remove the lubricating film on the surface of the aluminum foil, and then clean it with deionized water.

[0043] Immerse the cleaned aluminum foil in an etchant and energize it for corrosion. The etchant includes 0.5mol / L HCl, 0.5mol / L H2O2, and 0.1mol / L acetic alcohol. The corrosion time is 1min, and then triethanolamine phosphate is added to a concentration of 1.2mol / L passivation for 4min to obtain an aluminum foil substrate with a porous structure on the surface, that is, a porous aluminum foil substrate.

[0044] S102, preparing graphene aluminum foil

[0045] Put the porous aluminum foil substrate into the plasma vapor deposition equipment, vacuumize, raise the temperature of the porous aluminum foil substrate to 980°C, introduce inert gas mixed with methane, wherein the content of methane is 3%, the air flow rate is 50 sccm, and hydrogen gas is 500 sccm , the deposition time is 40s, and then ...

Embodiment 2

[0050] S1. Preparation of porous aluminum foil substrate

[0051] Clean the surface of the aluminum foil with a detergent to remove the lubricating film on the surface of the aluminum foil, and then clean it with deionized water. Immerse the cleaned aluminum foil in an etchant and electrify it for corrosion. The etchant includes 0.2mol / L HCl, 0.1mol / L H2O2, and 0.1mol / L acetic alcohol. The corrosion time is 3 minutes, and then triethanolamine phosphate is added to a concentration of 1mol / L passivation for 5min to obtain an aluminum foil substrate with a porous structure on the surface, that is, a porous aluminum foil substrate.

[0052] S2, prepare graphene aluminum foil

[0053] Put the porous aluminum foil substrate into the plasma vapor deposition equipment, vacuumize, raise the temperature of the porous aluminum foil substrate to 980°C, introduce inert gas mixed with methane, wherein the content of methane is 6%, the gas flow rate is 50 sccm, and the hydrogen gas is 500 s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an aluminum foil with graphene used in a lithium battery and a preparation method thereof, and relates to the field of positive electrode materials of a lithium battery. The method comprises the following steps: immersing the aluminum foil in a corrosive agent and electrifying it to carry out corrosion, and putting the porous aluminum foil base into the Put it into the plasma vapor deposition equipment, vacuumize, heat up to the temperature of the porous aluminum foil substrate is 980 ~ 1000 ℃, introduce inert gas mixed with methane to obtain graphene aluminum foil; spray silver ions on the surface of graphene aluminum foil to obtain silver package Graphene aluminum foil; dissolve organic lithium, organic cobalt and organic manganese in chitin solution to obtain a reaction solution, place the reaction solution in an inert gas environment at a temperature of 900-1000°C for 1-2 hours, and cool naturally to obtain carbon Wrapped lithium, cobalt, and manganese oxides, wherein the carbon has a porous structure, and the porous carbon is mixed with a binder and coated on the silver-coated graphene aluminum foil. The invention can prevent the active material from falling off and improve the service life of the battery.

Description

technical field [0001] The invention relates to the field of positive electrode materials for lithium batteries, in particular to an aluminum foil with graphene for lithium batteries and a preparation method thereof. Background technique [0002] Lithium-ion batteries have high energy storage density, fast charging and discharging speed, high safety in use, and are more friendly to the environment. They are widely used in automobiles, medical care, and electronic products. The sheet has a relatively large relationship, and at the same time, the current collector corresponding to the pole sheet also has a relatively large relationship. [0003] The positive current collector of lithium-ion batteries is usually aluminum foil, and active materials are attached to the aluminum foil. Most of the current active materials are adhered to the surface of the aluminum foil through adhesives. Due to the weak interaction between the active materials and the aluminum foil, the active mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/66H01M4/70H01M10/052
CPCH01M4/661H01M4/663H01M4/667H01M4/70H01M10/052Y02E60/10
Inventor 蒙天庆
Owner NOZO GRP CO LTD