Negative ion functional chip, preparation method and negative ion sanitary napkin

A negative ion and chip technology, applied in sanitary napkins, medical science, bandages, etc., can solve the problems of antibacterial performance, negative ion release performance, and durability to be improved.

Pending Publication Date: 2021-03-12
何志方
View PDF13 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problems in the prior art, the antibacterial performance, negative ion relea

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Negative ion functional chip, preparation method and negative ion sanitary napkin
  • Negative ion functional chip, preparation method and negative ion sanitary napkin
  • Negative ion functional chip, preparation method and negative ion sanitary napkin

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0059] The preparation method of carboxylated calcium lignosulfonate in the embodiment is the same as the preparation method of carboxylated calcium lignosulfonate in Example 1 of patent application CN201711381045.8. The raw material calcium lignosulfonate is calcium lignosulfonate of model MG-3 provided by Shanghai Yunzhe New Material Technology Co., Ltd.

[0060] In the examples, sharp-state nano-titanium dioxide, CAS number: 1317-80-2. Provided by Xuancheng Jingrui New Material Co., Ltd., model: VK-TA18, purity > 99.8%, particle size: 20nm, specific surface area: 80m 2 / g.

[0061] In the embodiment, the reduced graphene oxide is provided by Shanghai Heditong Nano Technology Co., Ltd., the manufacturer: Graphene Supermarket, the product number: HDT0345, the purity is 98%, and the specific surface area is 400m 2 / g.

[0062] Bismuth tungstate in the examples, CAS number: 13595-87-4.

[0063] Lead acetate (trihydrate) in the examples, CAS number: 6080-56-4.

[0064] Hydr...

Embodiment 1

[0067] (1) Ultrasonic dispersion of anatase nano-titanium dioxide and reduced graphene oxide in deionized water at a mass ratio of 100:6, with a solid-to-liquid mass ratio of 1:80, stirred evenly, and heated at 100°C for 5 hours for water Thermal reaction, natural cooling after the reaction, vacuum filtration, washing to neutrality, drying, grinding, titanium dioxide composite material can be obtained.

[0068] (2) 5 parts of tourmaline powder, 4 parts of medical stone powder, 1 part of Carbomer 940, 10 parts of calcium carboxylated lignosulfonate, 0.07 part of copper citrate, 0.03 part of silver citrate, 0.4 Add 90 parts of titanium dioxide composite material to 90 parts of deionized water and stir for 10 minutes at a speed of 300 r / min, and mix evenly to obtain a negative ion finishing solution.

[0069] (3) Dip the chip in an anion finishing solution at 45°C, the mass ratio of the chip to the anion finishing solution is 1:5, the dipping time is 30min, and dry at 50°C for 3h...

Embodiment 2

[0072] (1) Ultrasonic dispersion of anatase nano-sized titanium dioxide and bismuth tungstate in deionized water with a mass ratio of 100:6, with a solid-to-liquid mass ratio of 1:80, stirred evenly, and heated at 100°C for 5 hours for hydrothermal After the reaction is completed, cool naturally, vacuum filter, wash until neutral, dry, and grind to obtain a titanium dioxide composite material.

[0073](2) 5 parts of tourmaline powder, 4 parts of medical stone powder, 1 part of Carbomer 940, 10 parts of calcium carboxylated lignosulfonate, 0.07 part of copper citrate, 0.03 part of silver citrate, 0.4 Add 90 parts of titanium dioxide composite material to 90 parts of deionized water and stir for 10 minutes at a speed of 300 r / min, and mix evenly to obtain a negative ion finishing solution.

[0074] (3) Dip the chip in an anion finishing solution at 45°C, the mass ratio of the chip to the anion finishing solution is 1:5, the dipping time is 30min, and dry at 50°C for 3h to obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to a negative ion functional chip, a preparation method and a negative ion sanitary napkin. The preparation method of the negative ion functional chip comprises the following steps: uniformly adding 1-10 parts by weight of tourmaline powder, 1-10 parts by weight of medical stone powder, 0.5-1.5 parts by weight of carbomer or safflower seed gum, 5-15 parts by weight of carboxylated calcium lignosulphonate, 0.02-0.1 part by weight of copper citrate and 0.01-0.05 part by weight of silver citrate, 0.2-0.5 part of a nanometer titanium dioxide composite material into 50-120 parts of deionized water, performing stirring for 5-15 min at the rotating speed of 100-400 r/min, performing even mixing to obtain negative ion finishing liquid; putting a chip in the negative ion finishing liquid at the temperature of 40-50 DEG C to be soaked, the mass ratio of the chip to the negative ion finishing liquid being 1: (310), and the soaking time being 20-50 min; and then performing drying at a temperature of 40-60 DEG C for 1-5h to obtain the negative ion functional chip. The negative ion functional chip and the sanitary napkin prepared by the invention have the functions of instant absorption and softening, also have the effects of lasting bacteriostasis and anion release, and can dredge qi and blood, resist bacteria, diminish inflammation and relieve menstrual discomfort symptoms.

Description

technical field [0001] The invention relates to the technical field of disposable sanitary products, in particular to an anion functional chip, a preparation method and an anion sanitary napkin. Background technique [0002] Sanitary napkins, also known as sanitary napkins, are absorbent materials whose main materials are polymers and polymer composite paper formed from cotton, non-woven fabrics, pulp or composites of the above materials. Modern sanitary napkins are gradually developing towards multifunctionality, for example, by adding multiple functions to sanitary napkin chips to prepare functional sanitary napkin products. [0003] Chinese patent application CN108066808A discloses a negative ion sanitary napkin and its preparation method, including negative ion functional chip, the negative ion functional chip and the surface layer, absorber, bottom film, release paper, coating and quick and easy stickers according to the conventional sanitary napkin preparation process ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L15/18A61L15/46A61L15/42A61L15/40A61L15/44A61F13/472A61F13/84
CPCA61L15/18A61L15/46A61L15/42A61L15/40A61L15/44A61F13/472A61F13/8405A61L2300/104A61L2300/102A61L2300/404A61L2300/45A61L2300/602A61L2300/30A61L2300/402A61L2300/41A61F2013/8414A61F2013/8435
Inventor 何志方
Owner 何志方
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap