A kind of environment-friendly release agent for refractory materials and its preparation and use method

A refractory material and release agent technology, applied in the field of refractory materials, can solve the problems of release agent failure, easy damage to the protective interface of the release agent, and the temperature resistance of the release agent cannot meet the requirements, so as to avoid waste, Good emulsification and mold release properties, and the effect of improving heat resistance

Active Publication Date: 2022-04-22
武汉善达化工有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the existing release agents will fail when used in some special and harsh environments. For example, in a high-temperature steam environment, the sample needs to be baked at 110°C. During this process, a large amount of water will evaporate and overflow. General release agents The protective interface is easily damaged, and the temperature resistance of the release agent cannot meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of environment-friendly release agent for refractory materials and its preparation and use method
  • A kind of environment-friendly release agent for refractory materials and its preparation and use method
  • A kind of environment-friendly release agent for refractory materials and its preparation and use method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The environmentally friendly release agent for refractory materials provided in this example is prepared by the following method:

[0021] 150 parts of hydrogen-containing silicone monomer (1% hydrogen content, hydrogen-containing silicone oil with a viscosity of 0.3 Pa·s), 50 parts of polyether monomer (hydroxyl-terminated polyether with molecular weight between 2000 and 10000), plasticized Add 20 parts of agent (tri-n-butyl citrate and epoxidized soybean oil with molecular weight between 200 and 1000 1:10) into the reaction kettle, raise the temperature to 100°C, start stirring, set the stirring rate to 35r / min, and stir for 15min Finally, add 0.02 part of catalyst (chloroplatinic acid) and stir for 45 minutes, raise the temperature to 150°C, then add 2 parts of siliphenyne monomer (n-dodecyltriphenylethynylsilane) and keep it for 5h, cool down to 50°C, add 1 part of coupling agent and keep it out for 10 minutes to get an environmentally friendly release agent.

[00...

Embodiment 2

[0029] The environmentally friendly release agent for refractory materials provided in this example is prepared by the following method:

[0030] Mix 150 parts of hydrogen-containing silicone monomer (hydrogen-containing silicone oil with a hydrogen content of 1.2% and a viscosity of 0.4 Pa·s), 50 parts of polyether monomer (hydroxyl-terminated polyether with molecular weight between 2000 and 10000), plasticize Add 50 parts of agent (tri-n-butyl citrate and epoxidized soybean oil with a molecular weight between 200 and 1000 10:1) into the reaction kettle, heat up to 100°C, start stirring, set the stirring rate to 30r / min, and stir for 20min Finally, add 0.02 parts of catalyst (Castel catalyst) and stir for 45 minutes, heat up to 150°C, then add 5 parts of siliphenyne monomer (n-octadecyltriphenylethynylsilane) and keep it warm for 5h, then cool down to 50°C. Add 2 parts of coupling agent and keep discharging for 15 minutes to obtain an environmentally friendly release agent. ...

Embodiment 3

[0038] The environmentally friendly release agent for refractory materials provided in this example is prepared by the following method:

[0039] 100 parts of hydrogen-containing silicone monomer (hydrogen-containing silicone oil with hydrogen content of 0.8%, viscosity of 0.35 Pa·s), 55 parts of polyether monomer (hydroxyl-terminated polyether with molecular weight between 2000 and 10000), plasticizer (Tri-n-butyl citrate and epoxidized soybean oil with a molecular weight between 200 and 1000 1:1) 25 parts were added to the reaction kettle, the temperature was raised to 100°C, and the stirring was started, and the stirring rate was set at 30r / min. After stirring for 25 minutes, , add 0.03 parts of catalyst (selenocrown ether platinum complex) and stir for 45 minutes, heat up to 150 ° C, then add 3 parts of siliphenyne monomer (n-hexyltriphenylethynyl silane) and keep warm for 5 hours, cool down to 50 ° C, add 1.5 parts of coupling agent and kept for 15 minutes to discharge, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an environmentally friendly release agent for refractory materials. The components and mass ratio of the release agent are: 80-150 parts of hydrogen-containing organosilicon monomer, 50-70 parts of polyether monomer, 2-5 parts of silphenyne monomer, 0.02-0.04 part of catalyst, 20-50 parts of plasticizer, 1-2 parts of coupling agent; the silphenyne monomer is n-dodecyltriphenylethynylsilane , n-octadecyltriphenylethynylsilane, n-tetradecyltriphenylethynylsilane, n-hexyltriphenylethynylsilane, or a mixture of two or more. The release agent has good temperature resistance, and is applicable to construction environments with relatively low temperatures in winter and relatively high temperatures in summer, and can also be applied to special environments such as high-temperature steam. Mixing environment-friendly mold release agent with waste engine oil can not only save resources, protect the environment, and reduce costs, but also has excellent mold release performance, smooth mold surface, and smooth sample surface.

Description

technical field [0001] The invention belongs to the technical field of refractory materials and relates to a release agent, in particular to an environment-friendly release agent for refractory materials. Background technique [0002] Coating the release agent on the contact surface between the slurry and the mold can make the molded product and the mold free of adhesion and easy to separate, so as to obtain a smooth and flat product, and ensure that the mold is not polluted and can be reused. Moreover, the release agent has stable chemical properties, does not react chemically with molded products and molds, and will not affect its performance. The release agent can be divided into pure oil, emulsified oil, paraffin, paint and resin. Pure oils include various vegetable oils, animal oils, and mineral oils. Among them, industrial waste oil is the most widely used, but there are many impurities in waste oil, which is easy to contaminate the concrete surface. Most emulsified ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M169/04C10M177/00C10N30/04C10N30/08C10N30/06C10N40/36
CPCC10M169/04C10M177/00C10M2209/103C10M2207/289C10M2207/24C10M2229/02C10M2229/042
Inventor 黄凯黄異张意陈娜
Owner 武汉善达化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com