Antibacterial plastic master batch, preparation method thereof and antibacterial plastic

An antibacterial plastic and masterbatch technology, applied in the field of plastic materials, can solve the problems of limited photocatalytic ability and inability to exert antibacterial performance of nano-zinc oxide, and achieve improved antibacterial and formaldehyde removal ability, improved photocatalytic efficiency, and high specific surface area Effect

Pending Publication Date: 2021-03-16
中星(广州)纳米材料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this regard, at present, most of them improve the light quantum efficiency, increase the oxidation ability, and expand the spectral absorption range by modifying zinc oxide. However, the photocatalytic ability of nano-zinc oxide obtained by this method is still limited, especially at night when there is no light, because it cannot absorb light. The energy of light prevents it from exerting its antibacterial properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial plastic master batch, preparation method thereof and antibacterial plastic
  • Antibacterial plastic master batch, preparation method thereof and antibacterial plastic
  • Antibacterial plastic master batch, preparation method thereof and antibacterial plastic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of antibacterial plastic masterbatch, by weight, its raw material components include: 15 parts of nano-zinc oxide, 2 parts of nano-silver powder, 3 parts of nano-copper powder, 5 parts of graphene, 10 parts of CaAl 2 o 4 :Eu 2+ ,Nd 3+ , 2 parts of polyethylene wax, 0.3 part of isopropyl tris (dioctyl pyrophosphate acyloxy) titanate, 62.7 parts of PP resin; wherein, the particle diameter of nano-zinc oxide is 22nm, and the particle diameter of nano-silver powder is 30nm, the particle size of nano-copper powder is 30nm, the number of layers of graphene is 2 layers, the purity is 99.5%, the thickness is 0.7nm, the diameter is 3μm, and the specific surface area is 400m 2 / g, CaAl 2 o 4 :Eu 2+ ,Nd 3+ The particle size is 35nm.

[0023] The preparation method of this antibacterial plastic masterbatch is as follows:

[0024] S1, according to the above-mentioned weight ratio, nano-zinc oxide, nano-silver powder, nano-copper powder, graphene and CaAl 2 o 4 :Eu ...

Embodiment 2

[0027] A kind of antibacterial plastic masterbatch, by weight, its raw material components include: 20 parts of nano-zinc oxide, 4 parts of nano-silver powder, 3 parts of nano-copper powder, 4 parts of graphene, 15 parts of SrAl 2 o 4 :Eu 2+ , Dy 3+ , 4 parts of zinc stearate, 0.5 part of two (dioctyloxypyrophosphate) ethylene titanate, 49.5 parts of PE resin; wherein, the particle diameter of nano-zinc oxide is 45nm, and the particle diameter of nano-silver powder is 50nm, the particle size of nano-copper powder is 35nm, the number of layers of graphene is 2 layers, the purity is 99.5%, the thickness is 0.7nm, the diameter is 3μm, and the specific surface area is 420m 2 / g, SrAl 2 o 4 :Eu 2+ , Dy 3+ The particle size is 40nm;

[0028] The preparation method of this antibacterial plastic masterbatch is as follows:

[0029]S1, according to the above-mentioned weight ratio, nano-zinc oxide, nano-silver powder, nano-copper powder, graphene and SrAl 2 o 4 :Eu 2 + , Dy ...

Embodiment 3

[0032] A kind of antibacterial plastic masterbatch, by weight, its raw material components include: 40 parts of nano-zinc oxide, 1 part of nano-silver powder, 2 parts of nano-copper powder, 0.5 part of graphene, 7 parts of ZnS:Cu, 3 parts of paraffin, 0.2 parts of isopropyl dioleic acid acyloxy (dioctyl phosphate acyloxy) titanate, 46.3 parts of PVC resin; wherein, the particle diameter of nano-zinc oxide is 60nm, the particle diameter of nano-silver powder is 30nm, and the particle diameter of nano-copper powder The particle size of the graphene is 45nm, the number of layers of graphene is 5 layers, the purity is 99.5%, the thickness is 1.7nm, the diameter is 3μm, and the specific surface area is 450m 2 / g, the particle diameter of ZnS:Cu is 35nm.

[0033] The preparation method of this antibacterial plastic masterbatch is as follows:

[0034] S1. Mix nano-zinc oxide, nano-silver powder, nano-copper powder, graphene and ZnS:Cu according to the above weight ratio; then add is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antibacterial plastic master batch, a preparation method thereof and antibacterial plastic. The antibacterial plastic master batch comprises the following raw material components in parts by weight: 15-40 parts of nano zinc oxide, 1-15 parts of nano silver powder, 1-15 parts of nano copper powder, 0.5-5 parts of graphene, 5-25 parts of a long afterglow luminescent material, 1-6 parts of a dispersing agent, 0.1-5 parts of a coupling agent and 30-70 parts of carrier resin. The antibacterial component in the antibacterial plastic master batch takes the nano zinc oxide as a substrate, and the nano silver powder, the nano copper powder, the graphene and the long afterglow luminescent material are added in an auxiliary manner, so that the antibacterial plastic master batch can play an antibacterial role in a relatively wide wavelength range, and also can play an antibacterial role in the absence of illumination.

Description

technical field [0001] The invention relates to the technical field of plastic materials, in particular to an antibacterial plastic masterbatch, a preparation method thereof, and an antibacterial plastic. Background technique [0002] Today, with the rapid economic development, plastics are widely used in various fields such as agriculture, industry, construction, packaging, defense cutting-edge industries and people's daily life, such as raincoats, toothbrushes, plastic bags, plastic wrap, etc. in daily life, and household appliances industry. Plastics are widely used in televisions, electric fans, refrigerators, etc. However, people's living environment is full of a large number of bacteria, fungi, viruses and other pathogenic microorganisms. Some microorganisms have become one of the killers of human health, and people pay more attention to environmental hygiene, and more and more products with antibacterial functions Be loved by people. [0003] Antibacterial plastic i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J3/22C08L23/12C08K13/02C08K3/22C08K3/08C08K3/04C08K3/24C08L23/06C08K3/30C08L27/06
CPCC08J3/226C08J2423/06C08J2423/12C08J2427/06C08K3/24C08K13/02C08K2003/0806C08K2003/085C08K2003/2296C08K2003/3036C08K2201/005C08K2201/006C08K2201/011C08L23/06C08L23/12C08L27/06C08K3/042C08K3/22C08K3/08C08K3/04C08K3/30
Inventor 沈海华余力曾和平
Owner 中星(广州)纳米材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com