Method for preparing MOF-based nano material based on waste lithium ion battery leachate

A technology for lithium-ion batteries and nanomaterials, which is applied in the field of preparing MOF-based nanomaterials based on the leaching solution of waste lithium-ion batteries, can solve the problems that the purity cannot meet the requirements of commercial applications, the separation and extraction of leaching solution is difficult, and the utilization rate of leaching solution is low. Low cost, good crystallinity and complete crystal form

Active Publication Date: 2021-03-16
北京理工大学前沿技术研究院 +1
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to the coexistence of various metal ions, it is difficult to separate and extract the leachate of waste lithium-ion batteries, and the process is long, the utilization rate of the leachate is low, the added value of the product is low, its purity cannot meet the requirements of commercial applications, and its shape is uncontrollable.
At present, MOF materials have shown good application prospects in lithium-ion batteries, supercapacitors, electrocatalysis, and adsorbents, but their large-scale application is limited due to the expensive raw materials required for their preparation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing MOF-based nano material based on waste lithium ion battery leachate
  • Method for preparing MOF-based nano material based on waste lithium ion battery leachate
  • Method for preparing MOF-based nano material based on waste lithium ion battery leachate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] This embodiment provides a method for preparing MOF-based nanomaterials based on the leaching solution of waste lithium-ion batteries. The lithium-ion batteries are waste lithium cobalt oxide batteries. The method includes the following steps:

[0036] (1) Mix the waste and old lithium-ion battery positive electrode material with the acetic acid solution of 2mol / L, add the H that the volume is 3% of acidic solution volume 2 o 2 , stirred at 70°C for 60min to obtain Li + ,Co 2+ A solution of metal ions; wherein, the solid-to-liquid ratio of the waste lithium-ion battery positive electrode material to the acidic solution is 30g / L, and the stirring speed is 400rpm.

[0037] (2) Control the concentration of cobalt ions to 0.75mol / L by evaporating the leaching solution; add an appropriate amount of ammonia water to adjust the pH of the leaching solution to 6; add ethanol so that the volume ratio of the leaching solution and ethanol is 0.5:1; The molar ratio of imidazole t...

Embodiment 2

[0041] This embodiment provides a method for preparing MOF-based nanomaterials based on the leaching solution of waste lithium-ion batteries. The lithium-ion batteries are waste lithium cobalt oxide batteries. The method includes the following steps:

[0042] (1) Mix waste and old lithium-ion battery cathode material with 1mol / L nitric acid solution, add volume is 0.5% H of acidic solution volume 2 o 2 , stirred at 50°C for 30min to obtain Li + ,Co 2+A solution of metal ions; wherein, the solid-to-liquid ratio of the waste lithium-ion battery cathode material to the acidic solution is 50g / L, and the stirring speed is 300rpm.

[0043] (2) Control the concentration of cobalt ions to 0.5mol / L by evaporating the leaching solution; add an appropriate amount of ammonia water to adjust the pH of the leaching solution to 7; add ethanol so that the volume ratio of the leaching solution and ethanol is 3:1; The molar ratio of imidazole to cobalt ion concentration was 4:1, and 2-methyl...

Embodiment 3

[0047] This embodiment provides a method for preparing MOF-based nanomaterials based on the leaching solution of waste lithium-ion batteries. The lithium-ion batteries are waste lithium cobalt oxide batteries. The method includes the following steps:

[0048] (1) Mix waste and old lithium-ion battery positive electrode material with 1.5mol / L lactic acid solution, add volume and be the H of 0.5% of acidic solution volume 2 o 2 , stirred at 60°C for 30min to obtain Li + ,Co 2+ A solution of metal ions; wherein, the solid-to-liquid ratio of the waste lithium-ion battery positive electrode material to the acidic solution is 20g / L, and the stirring speed is 400rpm.

[0049] (2) Control the concentration of cobalt ions to 0.25mol / L by evaporating the leaching solution; add an appropriate amount of ammonia water to adjust the pH of the leaching solution to 10; add ethanol so that the volume ratio of the leaching solution and ethanol is 1:1; The molar ratio of imidazole to cobalt i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for preparing an MOF-based nano material based on a waste lithium ion battery leachate. The method comprises the following steps: (1) dissolving a waste lithium ion battery positive electrode material in an acidic reagent to obtain a leachate containing Co<2+> and Li<+>; (2) dispersing a certain amount of 2methylimidazole into the leachate, and centrifuging to obtain an MOF nano material; and (3) carrying out roasting treatment on the MOF nano material to obtain an MOF-based derivative nano material. According to the method provided by the invention, raw materials are cheap and easily available, the preparation steps are simple, reaction conditions are mild and easy to control, the prepared product is regular in morphology and high in purity, and the methodhas a wide application prospect, and has important significance for high-valued utilization of waste lithium ion batteries.

Description

technical field [0001] The invention relates to the field of resource recycling technology and preparation of chemical materials, in particular to the field of a method for preparing MOF-based nanomaterials based on the leaching solution of waste lithium-ion batteries. Background technique [0002] Lithium-ion batteries have the advantages of high energy density, small self-discharge, light pollution, and long cycle life. They are widely used in consumer electronics, new energy vehicles, and large-scale energy storage equipment, which leads to the consumption and disposal of lithium-ion batteries. The amount of lithium-ion batteries is increasing rapidly around the world, and after the service of lithium-ion batteries is over, its subsequent reasonable treatment is an urgent problem to be solved. Improper disposal of used lithium-ion batteries will result in a waste of resources and pose a greater threat to the environment and human health. Under such circumstances, the rec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/54H01M10/0525B82Y30/00B82Y40/00
CPCH01M10/54H01M10/0525B82Y30/00B82Y40/00Y02W30/84Y02E60/10
Inventor 范二莎李丽陈人杰林娇吴锋
Owner 北京理工大学前沿技术研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products