High-temperature-resistant inorganic hole sealing agent for thermal spraying coating and preparation method of high-temperature-resistant inorganic hole sealing agent
A thermal spraying, high temperature resistant technology, used in coatings, anti-corrosion coatings, fire-resistant coatings, etc., can solve the problems of poor penetration of the sealing agent, insufficient sealing depth, and poor adhesion, and achieve good UV resistance and resistance. High temperature performance, avoidance of brittle failure, effect of excellent permeability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0036]The present invention also provides a method for preparing a high temperature-resistant inorganic sealing agent for thermal spray coating, including the following steps:
[0037]Take the equivalent inorganic functional sol and rare earth sol, heated to 50 to 80 ° C, after this temperature is completely dissolved, the inorganic film forming agent is added, stirred and uniform, and then add the stabilizer, fully mixed, adjust the pH To 2.5 ~ 5, the hot spray coating was obtained with high temperature inorganic sealing agents.
[0038]The present invention also provides a method of using a high temperature-resistant inorganic sealing agent for a thermal spray coating, including the following steps:
[0039]A. The workpiece of the heat spray coating is 30 to 60 min at 50 to 60 ° C, and the mixed inorganic sealing agent is uniformly applied to the surface of the workpiece, the coating method is atmospheric spray, brush or impregnation;
[0040]B, stand for 30 ~ 60min, so that the sealing agent...
Example Embodiment
[0044]EXAMPLES Preparation of Heat Temperature Inorganic Sealing Dissipings for the thermal spray coating of the present invention
[0045]The specific steps are as follows:
[0046](1) Preparation of inorganic film films, 300 g of phosphoric acid, 80 g of aluminum hydroxide, 3GB2O3, Magnesium oxide 200g, 465GH2O, the reaction generates 1000 g colorless transparent solution A;
[0047](2) Add 500 g of Al Sol, 500 g of Zr sol, 250g TiO in order to the container2Sol, 125 g of a phosphate sol, 125 g of a phosphate sol, heated to 50 ° C, uniformly stirred, and slowly add solution A to solution B, and 125 g of chromic anhydride, stir until the solution is uniform.
[0048]The plasma sprayed Al2O3 ceramic coating is performed by the above-described sealing agent, the steps are as follows:
[0049]Step 1, the workpiece of the heat spray coating is preheated at 60 ° C for 30 min, and the mixing of the inorganic sealing agent is uniformly applied to the surface of the workpiece surface, the coating method ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap