Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of preparation method of rosin resin and its processing equipment

A technology of rosin resin and reaction kettle, which is applied in the field of rosin processing, can solve the problems of poor thermal stability, unfavorable use of rosin resin, deep color, etc., and achieve the effect of improving thermal stability, reducing heat emission, and preventing oxidation

Active Publication Date: 2021-08-03
广西上林县林发松香有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing rosin resins are generally difficult to meet the needs of use. Existing rosin resins have a darker color and poor thermal stability, which is not conducive to the widespread use of rosin resins.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of rosin resin and its processing equipment
  • A kind of preparation method of rosin resin and its processing equipment
  • A kind of preparation method of rosin resin and its processing equipment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A processing equipment used in the preparation method of rosin resin, comprising a reactor shell 1, a stirrer 2, a feed pipe 3 and a discharge pipe 5, and the agitator 2 is located above the reactor shell 1 , and the stirring shaft 14 of the agitator 2 is inserted into the reactor shell 1, and the left and right sides of the stirring shaft 14 in the reactor shell 1 are provided with a number of stirring blades-15. The left and right sides of the bottom end of the stirring shaft 14 are respectively fixed with stirring blades 2 16, the feed pipe 3 is located on the upper side of the reactor shell 1, and the upper side of the reactor shell 1 is also provided with Auxiliary material pipe 1 4, the middle of the bottom end of the reaction kettle shell 1 is provided with a discharge pipe 5, the bottom end of the reaction kettle shell 1 is also provided with auxiliary material pipe 2 6, and the bottom end of the reaction kettle shell 1 is provided with a discharge pipe 5. A sup...

Embodiment 2

[0027] A preparation method of rosin resin, specifically comprises the following steps:

[0028] 1) Modified catalyst carrier: first make NH with a concentration of 2 mol / L 4 HCO 3 solution and 2mol / L of Al(OH) 3 The solution is reacted, adjusted so that the pH value of the reaction is between 9, the reaction is filtered to obtain a precipitate, and the obtained precipitate is cleaned, so that the washed precipitate and the mass concentration of 8% TiO 2 reaction, adding ethanol and sodium pyrophosphate at the same time, under the condition of heating in a water bath, so that the reaction temperature is 75 ° C, after the reaction, suction filtration, washing, dipping, drying, and calcination are performed to obtain modified nano-alumina;

[0029] 2) Preparation of catalyst: firstly add 30 parts of nano-silica and 0.2 part of emulsifier into 60 parts of deionized water, and the emulsifier includes polyoxyethylene 20 sorbitan monooleate and glyceryl monostearate, and The mass...

Embodiment 3

[0032] A preparation method for rosin resin, specifically comprising the following steps:

[0033] 1) Modified catalyst carrier: first make the concentration of 2mol / L NH 4 HCO 3 solution and 2mol / L Al(OH) 3 Solution reaction, adjustment makes the pH value of reaction between 10, reacts and filters and obtains precipitate, the precipitate obtained is cleaned, makes the precipitate after cleaning and mass concentration be 8% TiO 2 Reaction, adding ethanol and sodium pyrophosphate at the same time, under the condition of heating in a water bath, the reaction temperature is 85°C, after the reaction, perform suction filtration, washing, impregnation, drying, and calcination to obtain modified nano-alumina;

[0034] 2) prepare catalyst: first make 50 parts of nano silicon dioxide and 0.4 part of emulsifier add 80 parts of deionized water, described emulsifier comprises polyoxyethylene 20 sorbitan monooleate and glyceryl monostearate, and The mass ratio between the polyoxyethylen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is applicable to the technical field of rosin processing. The present invention provides a preparation method of rosin resin and its processing equipment. In the preparation method of rosin resin in the present invention, nano alumina is modified as a carrier, so that the nano Alumina has a good carrying capacity, which is conducive to carrying silica. By using silica as a carrier, the catalytic reaction can be carried out well, and at the same time, it can absorb impurities in rosin resin, which is beneficial to lighten the color of rosin resin; In the preparation process of the rosin resin in the invention, by adding an antioxidant, the rosin resin can be effectively prevented from being oxidized, the color of the rosin resin can be further lightened, and the thermal stability of the rosin resin in the present invention can be effectively improved at the same time; the present invention The processing equipment of rosin resin has good thermal insulation effect, which is beneficial to the reaction.

Description

technical field [0001] The invention belongs to the technical field of rosin processing, and in particular relates to a preparation method of rosin resin and processing equipment thereof. Background technique [0002] Rosin, also known as rosin, is a substance obtained by distillation of the resin contained in pine trees. It is solid and transparent in appearance, light yellow or brown in color, hard and brittle, insoluble in water and soluble in alcohol. It can be used in industrial, Flux, Chinese medicinal materials, stringed musical instruments, etc. Rosin is divided into three types: gum rosin, wood rosin and tall oil rosin according to its source. Gum rosin is also called relaxing fragrance, with light color, high acid value and high softening point; wood rosin, also known as leaching rosin, is not as good as gum rosin, dark in color, low in acid value, and easy to crystallize from certain solvents; tall oil rosin Also known as tall oil rosin. Rosin is a transparent,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09F1/02B01J21/12B01J19/18B01J19/00B01J20/10B01J20/30
CPCB01J19/0053B01J19/0066B01J19/18B01J20/103B01J21/12C09F1/02
Inventor 陈秉煌
Owner 广西上林县林发松香有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products