A nanoporous graphene/nitrocellulose membrane for antibacterial and wound healing promotion and preparation method thereof
A nitrocellulose membrane and nitrocellulose technology, applied in the direction of resisting vector-borne diseases, bandages, absorbent pads, etc., can solve the problems that cannot effectively improve the gas-permeable wound healing of nitrocellulose membrane, and achieve the promotion of wound healing Effects of healing, broad-spectrum antimicrobial properties, good toughness and biocompatibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0025] (1) Mix the graphene oxide dispersion with the zinc nitrate solution so that the final concentration of the former is 4 g / L, and the final concentration of the latter is 800 g / L, stir and mix evenly, the mixed solution is filtered with filter paper, and then the filter paper and The intercepted mixture was dried in an oven at 55°C, then ignited in an alcohol lamp and fully incinerated. The incineration product was repeatedly washed with 10% hydrochloric acid, then washed with distilled water until the pH was neutral, and the nanoporous graphene was collected by centrifugation;
[0026] (2) Take 0.003 g of nanoporous graphene prepared in step (1), add it to 250 μL ethanol, and add 750 μL nitrocellulose solution (collodion; content: w / % 4-8%) after ultrasonic dispersion, Continue to sonicate and mix evenly to obtain a mixed solution;
[0027] (3) The mixed solution prepared in step (2) was added dropwise to a 35 mL petri dish, and air-dried to form a film to obtain a nan...
Embodiment 2
[0029] (1) Mix the graphene oxide dispersion with the zinc nitrate solution so that the final concentration of the former is 6 g / L, and the latter is 800 g / L, stir and mix evenly, the mixed solution is filtered with filter paper, and then the filter paper and The intercepted mixture was dried in an oven at 55°C, then ignited in an alcohol lamp and fully incinerated. The incineration product was repeatedly washed with 10% hydrochloric acid, then washed with distilled water until the pH was neutral, and the nanoporous graphene was collected by centrifugation;
[0030] (2) Take 0.001 g of nanoporous graphene prepared in step (1), add it to 250 μL ethanol, and after ultrasonic dispersion, add 750 μL nitrocellulose solution (collodion; content: w / %4-8%) to continue Ultrasound and mix uniformly to obtain a mixed solution;
[0031] (3) The mixed solution prepared in step (2) was added dropwise to a 35mL petri dish, and air-dried naturally to form a nanoporous graphene / nitrocellulose...
Embodiment 3
[0033] (1) Mix the graphene oxide dispersion with the zinc nitrate solution so that the final concentration of the former is 4 g / L, and the latter is 600 g / L, stir and mix evenly, the mixed solution is filtered with filter paper, and then the filter paper and The intercepted mixture was dried in an oven at 55°C, then ignited in an alcohol lamp and fully incinerated. The incineration product was repeatedly washed with 10% hydrochloric acid, then washed with distilled water until the pH was neutral, and the nanoporous graphene was collected by centrifugation;
[0034] (2) Take 0.003 g of nanoporous graphene prepared in step (1), add it to 200 μL ethanol, and after ultrasonic dispersion, add 800 μL nitrocellulose solution (collodion; content: w / %4-8%) to continue Ultrasound and mix uniformly to obtain a mixed solution;
[0035](3) The mixed solution prepared in step (2) was added dropwise to a 35mL petri dish, and air-dried to form a film to obtain a nanoporous graphene / nitrocel...