High-toughness and high-cohesiveness C130-strength high-strength fiber concrete and preparation method thereof

A high cohesive, high-strength fiber technology, used in clay preparation devices, chemical instruments and methods, climate sustainability, etc., can solve problems such as the inability to achieve toughening effects, reduce costs, increase cohesion, reduce Effects of CO2 Emissions

Active Publication Date: 2021-06-25
XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, due to the presence of cracks of different sizes in conc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness and high-cohesiveness C130-strength high-strength fiber concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0091] 1) Add 12 parts by mass of water reducer to two-thirds of the total water, which is recorded as mixed solution 1; add 10 parts of shrinkage reducer and 1.9 parts of defoamer to the total water of three One-third of the water is recorded as mixed solution 2, and 22 parts of carboxyl-modified polyvinyl alcohol polymers are prepared for later use, with a total water content of 120 parts; wherein, carboxyl-modified polyvinyl alcohol polymers are prepared according to the mass percentage of raw materials Formation: carboxy-modified polyvinyl alcohol 38.6%, water 60.4%, polyacrylate defoamer 1%;

[0092] 2) 5.4 parts of ramie fiber, 985 parts of gravel, 718 parts of sand, 425 parts of cement, 80 parts of fly ash, 65 parts of straw ash, 30 parts of silica fume, 3.5 parts of nano silicon, 9 parts of basalt fiber, 17.8 parts of CaCO 3 Whiskers were divided into three parts, and then a part of ramie fiber, basalt fiber, CaCO 3 Sprinkle the whiskers evenly in the disc mixer, then...

Embodiment 2

[0101] 1) Add 12.5 parts by mass of water reducer to two-thirds of the total water, which is recorded as mixed solution 1; add 10.5 parts of shrinkage reducer and 2.3 parts of defoamer to the total water of three One-third of the water is recorded as mixed solution 2, and 21 parts of carboxyl-modified polyvinyl alcohol polymers are prepared for later use, with a total water content of 125 parts; wherein, carboxyl-modified polyvinyl alcohol polymers are prepared according to the mass percentage of raw materials Made: carboxy-modified polyvinyl alcohol 38.5%, water 60%, polyacrylate defoamer 1.5%;

[0102] 2) 5.5 parts of ramie fiber, 985 parts of gravel, 718 parts of sand, 430 parts of cement, 84 parts of fly ash, 65 parts of straw ash, 35 parts of silica fume, 3.9 parts of nano silicon, 9.3 parts of basalt fiber, 18.1 parts of CaCO 3 Whiskers were divided into three parts, and then a part of ramie fiber, basalt fiber, CaCO 3 Sprinkle the whiskers evenly in the disc mixer, the...

Embodiment 3

[0110] 1) Add 12 parts by mass of water reducing agent to two-thirds of the total water volume, which is recorded as mixed solution 1; add 10 parts of shrinkage reducer and 2.2 parts of defoamer to the total water volume of three One-third of the water is recorded as mixed solution 2, and 21 parts of carboxyl-modified polyvinyl alcohol polymers are prepared for later use, with a total water content of 125 parts; wherein, carboxyl-modified polyvinyl alcohol polymers are prepared according to the mass percentage of raw materials Made: carboxy-modified polyvinyl alcohol 37%, water 61.5%, polyacrylate defoamer 1.5%;

[0111] 2) 5.5 parts of ramie fiber, 985 parts of gravel, 718 parts of sand, 425 parts of cement, 85 parts of fly ash, 63 parts of straw ash, 30 parts of silica fume, 3.5 parts of nano silicon, 9.3 parts of basalt fiber, 17.8 parts of CaCO 3 Whiskers were divided into three parts, and then a part of ramie fiber, basalt fiber, CaCO 3 Sprinkle the whiskers evenly in th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Flexural strengthaaaaaaaaaa
Splitting tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses high-toughness and high-cohesiveness C130-strength high-strength fiber concrete and a preparation method thereof. The concrete is prepared from cement, sand, gravel, fly ash, straw ash, silica fume, nano silicon, water, a water reducing agent, an exciting agent, a defoaming agent, a shrinkage reducing agent, ramie fibers, basalt fibers, CaCO3 whiskers and a carboxyl modified polyvinyl alcohol polymer according to the mixing ratio of (425-430): 718: 985: (80-85): (60-65): (30-35): (3.5-4.2): (120- 125): (12-13): (13-14): (1.9-2.3): (10-11): (5.4-5.6): (9-9.4): (17.8- 18.1): (20-22). The materials are evenly mixed at intervals through a layered stirring method, and discharging, forming and curing are conducted. The fracture resistance, the compression resistance, the bonding strength with the profile steel and the impermeability of the concrete are remarkably enhanced, and the cooperative work capacity with the profile steel is further improved.

Description

technical field [0001] The invention belongs to the field of building materials, and is a kind of ramie fiber, basalt fiber, CaCO 3 Whiskers, carboxyl-modified polyvinyl alcohol polymers, straw ash, fly ash, silica fume, and nano-silicon concrete with high toughness, high cohesion, high durability, and high volume stability, specifically related to a High-strength fiber concrete with high toughness and high cohesiveness C130 strength and a preparation method thereof. Background technique [0002] In structural design, considering the requirements of use function, component stiffness and convenient construction, it is usually necessary to use different grades of concrete for different stress situations to meet the required compressive, flexural and splitting tensile strength of the component when it is loaded. And to ensure the bond strength of concrete and steel working together. Concrete materials with different grades have different modulus of elasticity and different de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/14C04B20/02C04B40/02C04B18/24C04B14/46C04B14/38C04B24/26C04B18/10C04B18/08C04B18/14C04B14/06C04B22/12C04B24/12B28C5/00
CPCC04B28/141C04B20/023C04B40/0254C04B18/248C04B14/4643C04B14/383C04B24/2623C04B18/101C04B18/08C04B18/146C04B14/06C04B24/122C04B22/124B28C5/003C04B2111/00008C04B2201/50C04B7/02C04B14/068C04B18/12C04B22/002C04B2103/302C04B2103/50C04B2103/0068Y02W30/91
Inventor 贺金川郑山锁阮升明铭董立国郑捷段培亮杨路周炎曹琛王斌尚志刚郑跃姬金铭
Owner XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap