Blended yarn woven fabric and manufacturing process thereof

A technology of blended fabrics and production processes, applied in textile, textile and papermaking, fabrics and other directions, can solve the problems of easy to wrinkle, not strong enough, easy to absorb body and so on

Inactive Publication Date: 2021-07-06
梁燕萍
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its disadvantage is that it is easy to wrinkle, easy to absorb, not strong enough, and fades quickly
Chemical fibers are textiles made of fibers made of polymer compounds. The advantages are bright colors, soft texture, drape, smooth and comfortable, and the disadvantages are poor wear resistance, heat resistance, moisture absorption and air permeability. , easy to deform when exposed to heat, easy to generate static electricity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blended yarn woven fabric and manufacturing process thereof
  • Blended yarn woven fabric and manufacturing process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Because of the blended fabric and its manufacturing process, the biggest difference between the present invention and the prior art is that in step S1, the polyester fiber is soaked in the soaking liquid. Therefore, the present invention focuses on the experimental steps related to the immersion solution, as other steps can be easily understood by those skilled in the art, and will not be repeated here.

[0045] In the present invention, the ratio of the stock solution of the treatment agent is preferably prepared. Because in terms of treatment effect, its main function is to effectively stabilize the coloring of blended fabrics, improve air permeability and toughness without deformation. The coloring performance and air permeability were used as indicators for measurement.

[0046] An infiltration manufacturing process for blended fabrics. The various components are produced according to the above steps. In order to ensure a single variable, the ratio of the stock sol...

Embodiment 2

[0064]The present invention secondly optimizes the proportion of modified aqueous solution ingredients. Because the inventor suspects that it can enhance the effect of the treatment agent, improve the stability of the treatment agent on the fabric, and improve the toughness and oxidation resistance of the fiber at the same time, the tensile breaking strength test is used as an index to measure.

[0065] Tensile breaking strength test: the experimental instrument is YG065 electronic fabric strength tester, referring to the standard ISO9073-3-1989 "Test methods for textiles and nonwovens Part III: Determination of tensile strength and elongation"

[0066] A kind of blended fabric manufacturing process, each component is made according to the above steps, in order to ensure a single variable, the modified aqueous solution is extracted according to the following test in order to ensure a single variable, and the modified aqueous solution is extracted according to the following test...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses blended yarn woven fabric that is formed by interweaving warp yarn and weft yarn, wherein the warp yarn is blended warp yarn, the blended warp yarn takes silk fibers and modal fibers as spinning raw materials. The invention further provides a manufacturing process of the blended yarn woven fabric, and the manufacturing process comprises the following steps: S1, respectively putting silk fibers, modal fibers and polyester fibers in water for cleaning, taking out the fibers and draining, naturally air-drying the drained silk fibers, modal fibers and polyester fibers at room temperature, and then soaking the polyester fibers in a soaking solution; S2, respectively drying the silk fibers, the modal fibers and the polyester fibers, and respectively carrying out a cotton opening process, a cotton carding process and a drawing process; and S3, after the silk fibers, the modal fibers and the polyester fibers are respectively drawn, performing a mixing and drawing process, a roving process, a spinning process and a spooling process on the silk fibers, the modal fibers and the polyester fibers after drawing, and finally forming the required fabric woven from cotton and wool blended yarn.

Description

technical field [0001] The invention relates to the technical field of blended fabric and its preparation, in particular to a blended fabric and its manufacturing process. Background technique [0002] At present, blended or blended chemical fiber fabrics are textile products made of chemical fibers and other cotton wool, silk, hemp and other natural fibers. Blended fabrics often combine the characteristics of a variety of single fabrics. The main component is a textile made of 65%-67% polyester and 33%-35% cotton blended yarn. Polyester-cotton cloth is commonly known as cotton Dacron, which not only highlights the style of polyester but also has the advantages of cotton fabric. The advantages of hemp are its high strength, moisture absorption, heat conduction, and excellent air permeability. The disadvantages are that it is not very comfortable to wear, and its appearance is rough and stiff. The advantages of silk textiles are lightness, fit, softness, smoothness, breathab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M13/513D06M15/53D06M15/285D06M13/355D03D15/47D03D15/233D03D15/225D03D15/283D06M101/06D06M101/10D06M101/32
CPCD06M13/513D06M15/53D06M15/285D06M13/355D10B2211/04D10B2201/22D10B2331/04D06M2101/10D06M2101/06D06M2101/32
Inventor 梁燕萍
Owner 梁燕萍