Method for preparing carbon monoxide low-shift catalyst by far infrared roasting
A far-infrared and carbon monoxide technology is applied in the field of preparation of carbon monoxide low-change catalysts, which can solve the problems of catalyst sintering, insufficient material decomposition, large temperature fluctuations, etc., and achieve the effects of stable catalyst performance, ideal pore structure, and uniform loss on ignition.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0035] Example 1
[0036] The precipitation method was obtained from copper-zinc aluminum three-membered materials, washing and filtration, wet filter cake, wet filter cake was processed, dried, and crushed. Weigh 400 kg of dry material (consistency of material basic parameters), invested in far red exterior reservoirs, adjust the temperature of each segment temperature zone temperature to 330 ° C, set control speed 550R / min, adjust the amount of material to 100 kg / h, Adjust the lower tank squeegee, uniform speed, so that the thickness mean of the chain plate tape material is 20 mm ± 2㎜, runs 2 h, and sampling.
Example Embodiment
[0037] Example 2
[0038] The precipitation method was obtained from copper-zinc aluminum three-membered materials, washing and filtration, wet filter cake, wet filter cake was processed, dried, and crushed. Weigh 400 kilograms of dry materials (consistency of material basic parameters), invested in far red-exterior reservoirs, adjust the temperature of each segment temperature zone temperature to 350 ° C, set control speed 550R / min, adjust the amount of material to 100 kg / h, Adjust the lower tank squeegee, uniform speed, so that the thickness mean of the chain plate tape material is 20 mm ± 2㎜, runs 2 h, and sampling.
Example Embodiment
[0039] Example 3
[0040] The precipitation method was obtained from copper-zinc aluminum three-membered materials, washing and filtration, wet filter cake, wet filter cake was processed, dried, and crushed. Weigh 400 kg of dry material (consistency of material basic parameters), invested in far red exterior reservoirs, adjust the temperature of each segment temperature zone temperature to 320 ° C, set control speed 600R / min, adjust the amount of material to 100kg / h, Adjust the lower tank squeegee, uniform speed, so that the thickness mean of the chain plate tape material is 20 mm ± 2㎜, runs 2 h, and sampling.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap