Preparation method of hydrophobic white carbon black
A silica and hydrophobic technology, applied in the field of preparation of hydrophobic silica, can solve problems such as poor modification effect, and achieve the effect of improving modification effect and improving hydrophobicity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0023] Example 1
[0024] The vinyl trimethoxysilane and vinyl triethoxysilane are mixed in a ratio of 1: 1 to obtain a silane coupling agent;
[0025] The silane coupling agent, dichloromethane, a concentration of 10% by weight ratio of dilute sulfuric acid, a silane coupling agent, dichloromethane, dilute sulfuric acid at a temperature of 80 ° C for 1 h. Get a modifier;
[0026] According to the following weight parts, each component is referred to: 2 parts of alkylphenol polyoxyethylene ether, 10 modifiers, 2 parts of fatty acid methyl oxyethylene ether, 3 of Tuwhifluoroalkyl triethoxysilane 60 parts of white carbon black; pour alkylphenol polyoxyethylene ether and modifier into a mixed bucket at a high speed of 5000 r / min under a high speed of 5000 r / min; pour white carbon black into the mixed bucket in an environment of 50 ° C Mix 0.5 h in a medium speed of the rotational speed of 4000 R / min; pour the fatty acid methyl eoxyethylene ether and thirteenctone alkyltriethoxy...
Example Embodiment
[0027] Example 2
[0028] The vinyl trimethoxysilane and vinyl triethoxysilane are mixed in a ratio of 1: 1 to obtain a silane coupling agent;
[0029] The silane coupling agent, dichloromethane, a concentration of 25% by weight is weighted; the silane coupling agent, dichloromethane, and dilute sulfuric acid are mixed at a temperature of 95 ° C. 1- 1.5H is obtained after obtaining a modifier;
[0030] According to the weight fraction, each component is referred to: 8 parts of alkylphenol polyoxyethylene ether, 25 parts of the modifier, 5 parts of the fatty acid methyl ethylene ether, and 6 of Tentezoxoalkyl triethoxysilane. 100 copies of white carbon; pour alkylphenol polyoxyethylene ether and modifier into a mixed bucket at a high speed of 6000 r / min under a high speed of 6000 r / min; pour white carbon black into the mixed bucket in an environment of 90 ° C The mixture was stirred at a medium rotational speed of 5000 R / min, and the fatty acid methyl oxyethylene ether and th...
Example Embodiment
[0031] Example 3
[0032] The vinyl trimethoxysilane and vinyl triethoxysilane are mixed in a ratio of 1: 1 to obtain a silane coupling agent;
[0033] According to the weight ratio of 10: 3: 4, the silane coupling agent, dichloromethane, the concentration of 17%; mixed the silane coupling agent, dichloromethane, dilute sulfuric acid mixed at a temperature of 87 ° C 1.75H After obtaining a modifier;
[0034] According to the weight fraction, each component is referred to: 6 parts of alkylphenol polyoxyethylene ether, 17 modifiers, 3.5 parts of fatty acid methyl oxyethylene ether, and 4.5 parts of thirteenctone alkyl tribeoxysilane. 80 copies of white carbon; pour alkylphenol polyoxyethylene ether and modifier into a mixed bucket at a high speed of 5500 r / min under a high speed of 5500 r / min; pour white carbon black into a mixed bucket in an environment of 70 ° C Mix 0.75 h in a medium rotational speed of 4500 r / min; pour the fatty acid methyl oxyethylene ether and thirteenct...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap