Corrosion-resistant glaze for pottery pot and glazing method thereof

A corrosion-resistant ceramic pot technology, which is applied in the field of corrosion-resistant glazes and glazing of pottery pots, can solve the problems of poor acid resistance of the glass phase, and achieve the goal of improving density, acid resistance, and hydrolysis resistance Effect

Pending Publication Date: 2021-08-06
重庆名檀陶瓷有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to provide a corrosion-resistant glaze for pottery pots, which is used to solve the technical problem of poor acid resistance of the glass phase formed after the glaze for pottery pots is sintered in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A corrosion-resistant glaze for pottery pots, comprising the following raw materials in parts by weight: 35 parts of kaolin, 12.5 parts of limestone, 14 parts of potassium feldspar, 16 parts of lepidolite, 3 parts of zirconia, 3 parts of zinc oxide, 2 parts of tin oxide, 15 parts of terpene resin, 22.5 parts of sodium hydroxyethylidene diphosphonate.

[0046] A method for glazing a corrosion-resistant glaze for a pottery pot, comprising the following steps:

[0047] (1) Body pretreatment

[0048] a. Green body soot blowing: put the green body in a fume hood, and blow the green body with compressed air;

[0049] b. Biscuit green body: heat the green body to 100-300°C, enter step (2) when the green body has water absorption and adsorption properties, and the water absorption and adsorption properties of the green body are determined according to the actual situation;

[0050] (2) wet glaze preparation

[0051] a. Limestone, potassium feldspar and lepidolite are mixed e...

Embodiment 2

[0058] A kind of anti-corrosion glaze of pottery pot, comprises following raw material ratio by weight: 20 parts of kaolin, 5 parts of limestone, 21 parts of potassium feldspar, 24 parts of lepidolite, 5 parts of zirconia, 3.4 parts of zinc oxide, 1.3 parts of tin oxide, 20 parts of terpene resin, 30 parts of hydroxyethylidene diphosphonate.

[0059] The glazing method of the corrosion-resistant glaze of embodiment 2 pottery pots is the same as embodiment 1.

Embodiment 3

[0061] A corrosion-resistant glaze for pottery pots, comprising the following raw materials in parts by weight: 50 parts of kaolin, 20 parts of limestone, 7 parts of potassium feldspar, 8 parts of lepidolite, 1 part of zirconia, 2.6 parts of zinc oxide, 2.7 parts of tin oxide, 10 parts of terpene resin, 15 parts of potassium hydroxyethylidene diphosphonate.

[0062] The glazing method of the corrosion-resistant glaze of embodiment 3 pottery pots is the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a corrosion-resistant glaze material for a pottery pot. The corrosion-resistant glaze is prepared from the following raw materials in parts by weight: 20 to 50 parts of kaolin, 5 to 20 parts of limestone, 7 to 21 parts of potassium feldspar, 8 to 24 parts of lepidolite, 1 to 5 parts of zirconium oxide, 2.6 to 3.4 parts of zinc oxide, 1.3 to 2.7 parts of tin oxide, 10 to 20 parts of terpene resin and 15 to 30 parts of 1-hydroxyethylidene-1, 1-diphosphonate. The invention further discloses a glazing method of the corrosion-resistant glaze for the pottery pot, the process is simple, and raw materials are easy to obtain. The pottery pot glaze prepared by the method has the characteristic of excellent corrosion resistance.

Description

technical field [0001] The invention relates to the technical field of production and processing of pottery pots, in particular to a corrosion-resistant glaze for pottery pots and a glaze application method thereof. Background technique [0002] Ceramics is a general term for pottery and porcelain, and pottery and porcelain have different textures and properties. Pottery is made of clay with high viscosity and strong plasticity as the main raw material. It is opaque, has fine pores and weak water absorption, and the sound of hitting is muddy. Porcelain is made of clay, feldspar and quartz, translucent, non-absorbent, anti-corrosion, hard and compact, and crisp when knocked. [0003] Glaze is a kind of silicate. The glaze applied on ceramics is generally made of quartz, feldspar, and clay. After grinding and adding water, it is coated on the surface of the green body and melted by roasting at a certain temperature. The temperature drops When, a glassy thin layer on the cera...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/86C04B41/5022C04B41/4539C04B41/0072
Inventor 张铭
Owner 重庆名檀陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com