Preparation method of hard particle reinforced impact-resistant and wear-resistant coating for machine-made sand
A hard particle, impact-resistant technology, used in coatings, metal material coating processes, liquid chemical plating, etc., can solve the problems of erosion wear, shortened life, and large coating brittleness, and achieve enhanced erosion resistance. Wear performance, improved service life, high bonding strength effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0021] Example 1
[0022] Step 1: Will Al 2 O 3 The raw powder is ball mill with anhydrous ethanol to get the ball after milling. 2 O 3 Slurry, and make the ball after Al 2 O 3 Slurry alone 2 O 3 The particle diameter is less than 50 nm; the ball is used as the medium ball when the ball mill is used as the medium ball, the medium ball is 1 mm, 3 mm, 5 mm, and 10 mm, the ball milling time is 10 hours, the ball mill speed is 250 rpm, the ball ratio 6: 1;
[0023] Step 2: Will step 1 get the ball mill after 2 O 3 Slurry drying, sieving, to get the ball milling nano Al 2 O 3 Powder spare;
[0024] Step 3: The TiC powder is cleaned at 6 mol / L dilute HCl solution and 8 mol / L dilute NaOH solution, and then removes the powder by deionized water, the powder is coarsed in the roughening liquid; the coarseization The composition of the liquid is from Hf20mol / L, HNO 3 50mol / L and NH 4 F 1g / L mixed composition;
[0025] Step 4: Wash the roughened TiC powder with deionized water, then...
Example Embodiment
[0029] Example 2
[0030] Step 1: Will Al 2 O 3 The raw powder is ball mill with anhydrous ethanol to get the ball after milling. 2 O 3 Slurry, and make the ball after Al 2 O 3 Slurry alone 2 O 3 The particle diameter is less than 50 nm; the ball is used as the medium ball when the ball mill is used as a medium ball, and the medium ball is 1 mm, 3 mm, 5 mm, and 10 mm. The ball mill is 8 hours, the ball mill rotation is 180 rpm, the ball ratio 7: 1;
[0031] Step 2: Will step 1 get the ball mill after 2 O 3 Slurry drying, sieving, to get the ball milling nano Al 2 O 3 Powder spare;
[0032] Step 3: The TiC powder is cleaned at a dilute HCl solution of 8 mol / L and a dilute NaOH solution of 7 mol / L, which is then cleaned with deionized water, and the powder is coarsed into the roughening liquid; the coarseization The composition of the liquid is from HF40 mol / L, HNO 3 70mol / L and NH 4 F 2g / L mixing composition;
[0033] Step 4: Wash the roughenous TiC powder with deionized ...
Example Embodiment
[0037] Example 3
[0038] Step 1: Will Al 2 O 3 The raw powder is ball mill with anhydrous ethanol to get the ball after milling. 2 O 3 Slurry, and make the ball after Al 2 O 3 Slurry alone 2 O 3 The particle diameter is less than 50 nm; the ball is used as a medium ball when the ball mill is used as the medium ball, and the medium ball is 1 mm, 3 mm, 5 mm, and 10 mm. The ball mill is 6 hours, the ball mill speed is 100 rpm, the ball ratio 8: 1;
[0039] Step 2: Will step 1 get the ball mill after 2 O 3 Slurry drying, sieving, to get the ball milling nano Al 2 O 3 Powder spare;
[0040] Step 3: The TiC powder is cleaned at 9 mol / L of the dilute HCl solution and 6 mol / L of the dilute NaOH solution, which is then cleaned with deionized water, and the powder is coarsed in the roughening liquid; the coarseization The composition of the liquid is from HF60mol / L, HNO 3 80mol / L and NH 4 F 3g / L mixed composition;
[0041] Step 4: Wash the TiC powder after the roughening water, t...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap