Coal mine roadway spraying material and preparation method thereof
A spraying material and roadway technology, applied in the direction of cement coating, anti-corrosion coating, fire-proof coating, etc., can solve the problems of easy water absorption and deliquescence or expansion, gas gushing out of the goaf, and great influence of coating dust, etc., to achieve high toughness and elasticity , good support and high support strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0025] Example 1
[0026] A coal mine mine lane spray material comprising two layers of a base layer and a surface layer, the base layer is made of a material of the following weight parts: 42.5 silicate cement, 35 pieces of fly ash, 8 clay, 4 deposition of latex powder 15 parts of the fiber reinforcement material, 0.2 cophenthraneum emulsions, 0.2 parts of polyvinyl alcohol, 1 part of water glass and 35 parts of water, the surface layer as a polyurethane foam layer.
[0027] The polyurethane layer is made of a raw material having a number of parts by weight of the polyether polyol (17.5 parts of polyether polyol, 17.5 serial toluocyanates, 3 parts of phenol resin, 8 dimethylsilicone oil, 1 part of diethylene glycol, catalyst 1 serving, 1.5 parts of trihydroxypropane, 10 hollow glass micro-balls, 12 parts of fiber reinforced material, 5 water glass and 3 deionized water.
[0028] The catalyst is bilateral di-dika titanate and triamine is mixed by weight ratio of 2: 1.
[0029] The...
Example Embodiment
[0035] Example 2
[0036] A coal mine mine road spray material comprising two layers of the base layer and the surface layer, the base layer is made of raw material of the following weight parts: 2,000 silicate cement, 32 pieces of fly ash, 9 copies, 5 depolar powder, The fiber reinforcing material was 14 parts of the phenylatoxide, 0.18 parts of polyvinyl alcohol, 1.2 parts of water glass and 38 water, and the surface layer is a polyurethane layer.
[0037] The polyurethane layer is made of a raw material of the following weight parts: 1000 polyether polyols (17.5 parts of toluene, 4 parts of toluene, 4 parts of phenol resin, 8.5 parts of dimethylsilicone oil, 1.2 parts of diethylene glycol, catalyst 1.2 parts, 1.4 parts of trihydroxypropane, 11 hollow glass microads, 11 parts of fiber reinforced material, 6 parts of water glass and 3.5 parts of deionized water.
[0038] The catalyst is bilateral di-dika titanate and triamine is mixed by weight ratio of 2: 1.
[0039] The fiber r...
Example Embodiment
[0042] Example 3
[0043] A coal mine mine lane spray material comprising two layers of the base layer and the surface layer, the base layer is made of a raw material of the following weight parts: 30 parts of silicate cement, 30 drums, 10 clay, 6 depolar powder, 13 parts of the fiber reinforcement material, 0.25 cophenthral emulsions, 0.15 parts of polyvinyl alcohol, 1.5 parts of water glass and 30 parts of water, the surface layer as a polyurethane layer.
[0044] The polyurethane layer is made of a raw material of the following weight parts: 100 parts by polyether polyol (2000), a toluene diisocyanate, 5 parts of the phenol resin, 9 dimethylsilicilicizine oil, 1.5 parts of diethylene glycol, catalyst 1.5 parts, 1.2 parts of trihydroxymethyl propylene, 12 of the microbeads of the hollow glass, 10 parts of fiber reinforced material, 6.5 parts of water glass and 4 deionized water.
[0045] The catalyst is bilateral di-dika titanate and triamine is mixed by weight ratio of 2: 1.
...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Length | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap