High-impact-resistance high-fluidity polypropylene material

A polypropylene material and high fluidity technology, applied in the field of polypropylene materials, can solve problems affecting product quality and performance, and achieve the advantages of avoiding rapid oxidative decomposition, high impact strength and elongation at break, and improving fluidity. Effect

Inactive Publication Date: 2021-09-03
厦门永晋鸿塑胶工业有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing PP material pedals require low temperature resistance, high impact resistance and weather resistance requirements, and the embrittlement temperature of the existing PP material products is -30°C, which will

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] This embodiment provides a high-fluidity high-impact polypropylene material, including polypropylene, mixed high-density polyethylene, elastic composite material, linear low-density polyethylene, light stabilizer, food-grade white mineral oil, Prepared by mixing antioxidant and activator, said polypropylene, mixed high-density polyethylene, elastic composite material, linear low-density polyethylene, light stabilizer, food-grade white mineral oil, antioxidant and activator The ratio is 30~35:30~34:15~18:16~19:0.2~0.5:0.1~0.4:0.2~0.6:0.3~0.6.

[0017] The mixing ratio of the polypropylene, mixed high-density polyethylene, elastic composite material, linear low-density polyethylene, light stabilizer, food grade white mineral oil, antioxidant and activator is 33.5:32:16:17:0.4: 0.2:0.4:0.5.

[0018] The light stabilizer is hindered amine light stabilizer and o-hydroxybenzophenone light stabilizer, benzotriazole light stabilizer, salicylic acid lipid light stabilizer and s...

Embodiment 2

[0022] This embodiment provides a high-fluidity high-impact polypropylene material, including polypropylene, mixed high-density polyethylene, elastic composite material, linear low-density polyethylene, light stabilizer, food-grade white mineral oil, Prepared by mixing antioxidant and activator, said polypropylene, mixed high-density polyethylene, elastic composite material, linear low-density polyethylene, light stabilizer, food-grade white mineral oil, antioxidant and activator The ratio is 30~35:30~34:15~18:16~19:0.2~0.5:0.1~0.4:0.2~0.6:0.3~0.6.

[0023] The mixing ratio of the polypropylene, mixed high-density polyethylene, elastic composite material, linear low-density polyethylene, light stabilizer, food grade white mineral oil, antioxidant and activator is 33:31:17:16:0.3: 0.4:0.5:0.4.

[0024] The light stabilizer is hindered amine light stabilizer and o-hydroxybenzophenone light stabilizer, benzotriazole light stabilizer, salicylic acid lipid light stabilizer and sub...

Embodiment 3

[0028] This embodiment provides a high-fluidity high-impact polypropylene material, including polypropylene, mixed high-density polyethylene, elastic composite material, linear low-density polyethylene, light stabilizer, food-grade white mineral oil, Prepared by mixing antioxidant and activator, said polypropylene, mixed high-density polyethylene, elastic composite material, linear low-density polyethylene, light stabilizer, food-grade white mineral oil, antioxidant and activator The ratio is 30~35:30~34:15~18:16~19:0.2~0.5:0.1~0.4:0.2~0.6:0.3~0.6.

[0029] The mixing ratio of the polypropylene, mixed high-density polyethylene, elastic composite material, linear low-density polyethylene, light stabilizer, food grade white mineral oil, antioxidant and activator is 33.5:32:16:17:0.4: 0.2:0.4:0.5.

[0030] The light stabilizer is hindered amine light stabilizer and o-hydroxybenzophenone light stabilizer, benzotriazole light stabilizer, salicylic acid lipid light stabilizer and s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-fluidity high-impact-resistance polypropylene material which is prepared by mixing polypropylene, mixed high-density polyethylene, an elastic composite material, linear low-density polyethylene, a light stabilizer, food-grade white mineral oil, an antioxidant and an activating agent. The mixed high-density polyethylene component is added, so that the elongation at break of the prepared product is increased, high performance can be kept in a low-temperature environment, meanwhile, the low-temperature resistance of the product is improved by adding the linear low-density polyethylene, the low-temperature resistance is close to the low-temperature resistance, the fluidity is improved, and the elastic composite material is matched for mixing and toughening, so that the product can maintain high impact strength and elongation at break in a low-temperature environment, and the addition of the light stabilizer avoids rapid oxygenolysis of tertiary carbon atoms, so that the weather resistance of the product is improved.

Description

technical field [0001] The invention relates to the technical field of polypropylene materials, in particular to a high-fluidity high-impact polypropylene material. Background technique [0002] It is a polymer formed by addition polymerization of propylene. It is a colorless, odorless, non-toxic, translucent solid substance with chemical resistance, heat resistance, electrical insulation, high-strength mechanical properties and good high-strength properties. Wear-resistant processing properties, etc., are widely used in the production of clothing, blankets and other fiber products, medical equipment, automobiles, bicycles, parts, pipelines, chemical containers, etc., and are also used in food and drug packaging; [0003] The existing PP material pedals require low temperature resistance, high impact resistance and weather resistance requirements, and the embrittlement temperature of the existing PP material products is -30°C, which will crack in low temperature environments...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/06C08L23/08
CPCC08L23/12C08L2205/035C08L2205/025C08L2207/062C08L2201/08C08L23/06C08L23/0815
Inventor 汪世平陈志顺
Owner 厦门永晋鸿塑胶工业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap