Preparation method and application of bio-based deodorant

A deodorant and bio-based technology, applied in building structures, building components, building insulation materials, etc., can solve the problems of operators and natural environment hazards, reduce toxic gas overflow, reduce use pollution, and relieve discomfort Effect

Active Publication Date: 2021-09-21
山东高速集团有限公司创新研究院 +2
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When asphalt is modified by adding a modifier containing sulfur, it will generate hydrogen sulfide, mercaptan and other odorous gases at high temperatures, which will also cause great harm to operators and the natural environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of bio-based deodorant
  • Preparation method and application of bio-based deodorant

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] A preparation method of a bio-based deodorant, comprising the following steps:

[0031] Step 1, adding toluene solvent, 1mol3,4-dihydroxybenzaldehyde, 2mol linoleic acid, 2.2mol diethyl azodicarboxylate and 2.2mol triphenylphosphine into a three-necked flask for stirring reaction; After vacuuming and nitrogen replacement, continue to stir and react at 120°C for 12h; cool the reactant to 0°C in an ice-water bath and add ice water to quench; the organic phase is separated and washed with water, dried, filtered, and then concentrated to light yellow Crude product; the crude product is separated and purified by column chromatography to obtain the white product 4-formyl-catechol dilinoleate;

[0032] Step 2, under the protection of nitrogen, dissolve 1.1 mol of n-propionaldehyde and 1 mol of 4-formyl-catechol dilinoleate prepared in step 1 in ethanol solution, stir evenly and cool to -10°C; Slowly add saturated sodium bicarbonate solution dropwise and react at -10°C for 12 ...

Embodiment 1

[0035] In the above step three, 40 parts of 3,4-dilinoleoyloxy-a-methylphenylacrylaldehyde obtained in step two, 56.7 parts of nano-silica, and 0.3 parts of antioxidant 1010 were added to the mixing tank , mixed for 1 hour under the test conditions of temperature 30°C and rotational speed 500 rpm, then added 3.0 parts of polyethylene wax and continued mixing for 30 minutes to obtain a bio-based deodorant.

Embodiment 2

[0037] In the above step three, 58 parts of 3,4-dilinoleoyloxy-a-methylphenylacrylaldehyde obtained in step two, 40 parts of nano-silica, and 0.5 parts of antioxidant BHT were added to the mixture In the tank, mix for 1 hour under the test conditions of temperature 30°C and rotation speed 500rpm, then add 1.5 parts of erucamide and continue mixing for 30 minutes to obtain a bio-based deodorant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
penetrationaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of road asphalt, in particular to a bio-based deodorant as well as a preparation method and application thereof. The bio-based deodorant is prepared from 40-60 parts of 3, 4-dilinoleyloxy-a-methyl benzene acrolein, 40-60 parts of nano white carbon black, 0.3-0.5 part of an antioxidant and 1-3 parts of polyethylene wax. In the use process, the bio-based deodorant can form a ficus base substance with amino in asphalt; and hydrogen sulfide, mercaptan and the like generated in a stabilizer development process form stable thioacetal, so that toxic gas does not overflow any more, and the use pollution is reduced. The synthesis raw materials are all from natural substances, for example, 3, 4-dihydroxybenzaldehyde is extracted from roots of labiatae plant salvia miltiorrhiza, and linoleic acid can be extracted from various oil crops. The synthesis method is green, environment-friendly and pollution-free; and the synthetic product is degradable and can be degraded by bacterial microorganisms after the pavement reaches the service life. The synthetic raw materials have special plant fragrance, and can relieve the discomfort of operators caused by peculiar smell generated in the asphalt mixing process.

Description

technical field [0001] The invention relates to the technical field of road asphalt, in particular to a bio-based deodorant and its preparation method and application. Background technique [0002] A small amount of aromatic amino and other components contained in asphalt are the main source of base asphalt odor. When asphalt is modified by adding a modifier containing sulfur, it will generate hydrogen sulfide, mercaptan and other odorous gases at high temperatures, which will also cause great harm to operators and the natural environment. Asphalt, especially coal tar pitch, will volatilize some polyaromatic compounds when preparing asphalt mixture or paving roads during hot mixing. Studies have shown that such compounds have the risk of carcinogenicity. Therefore, reducing or eliminating the volatilization and overflow of odorous substances in asphalt during high temperature treatment is very important for protecting the environment and creating a safe production environme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L23/06C08K7/26C08K5/107
CPCC08L95/00C08K7/26C08K5/107C08K2201/011C08L23/06
Inventor 穆明浩王福海王峥韩立斌张哲郑君杨茂君陈秀秀刘占斌赵景原李朝旭李明杰郑捷元王进勇青光焱赖思静
Owner 山东高速集团有限公司创新研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap