Fireproof energy-storage luminescent coating and preparation process thereof

An energy-storage luminescence and coating technology, which is applied in luminescent coatings, fireproof coatings, coatings, etc., can solve the problems of difficult to meet the needs of changing environments and poor weather resistance, and achieve good light resistance, high weather resistance, and adsorption capacity. strong effect

Inactive Publication Date: 2021-10-12
HEBEI JUNHUI SECURITY TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the comprehensive performance of most products on the market is difficult to meet the needs of changing environments, especially the poor weather resistance, which determines the service life and performance of the coating, so enhancing the weather resistance is the top priority of energy storage luminous coatings. Therefore, we propose a fire-resistant energy-storing luminous coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present invention proposes a fire-proof energy-storing luminous paint, the formula of which is as follows by weight of raw materials: 280 parts of water, 1 part of hydroxyethyl cellulose, 3 parts of dispersant, 3 parts of water quality stabilizer, 1 part of defoamer, bactericidal 1 part of ethylene glycol, 1 part of water quality pH regulator, 180 parts of styrene-acrylic emulsion, 40 parts of elastic emulsion, 0.3 parts of defoamer, 8 parts of film-forming aid, 350 parts of flame-retardant coated luminescent powder, Thickener 1 part.

[0022] The present invention also provides a preparation process of a fire-proof energy-storing luminous coating, comprising the following steps:

[0023] S1. Select the agitator as an auxiliary tool, and carry out disinfection and sterilization treatment on it under the condition of 80-100 degrees Celsius, and add water to it after completion;

[0024] S2. Slowly put the hydroxyethyl cellulose into the mixer according to the propor...

Embodiment 2

[0029] The present invention proposes a fire-proof energy-storing luminous coating, the formula of which is as follows by weight of raw materials: 290 parts of water, 1.5 parts of hydroxyethyl cellulose, 3.5 parts of dispersant, 3.5 parts of water quality stabilizer, 1.5 parts of defoamer, bactericidal 1.5 parts of agent, 1.5 parts of ethylene glycol, 1.5 parts of water quality pH regulator, 190 parts of styrene-acrylic emulsion, 45 parts of elastic emulsion, 0.4 parts of defoamer, 9 parts of film-forming aid, 375 parts of flame-retardant coated luminescent powder, Thickener 2 parts.

[0030] The present invention also provides a preparation process of a fire-proof energy-storing luminous coating, comprising the following steps:

[0031] S1. Select the agitator as an auxiliary tool, and carry out disinfection and sterilization treatment on it under the condition of 80-100 degrees Celsius, and add water to it after completion;

[0032] S2. Slowly put the hydroxyethyl cellulose...

Embodiment 3

[0037] The present invention proposes a fire-proof energy-storing luminous coating, the formula of which is as follows by weight of raw materials: 300 parts of water, 2 parts of hydroxyethyl cellulose, 4 parts of dispersant, 4 parts of water quality stabilizer, 2 parts of defoamer, bactericidal 2 parts of agent, 2 parts of ethylene glycol, 2 parts of water quality pH regulator, 200 parts of styrene-acrylic emulsion, 50 parts of elastic emulsion, 0.5 parts of defoamer, 10 parts of film-forming aid, 400 parts of flame-retardant coated luminescent powder, Thickener 3 parts.

[0038] The present invention also provides a preparation process of a fire-proof energy-storing luminous coating, comprising the following steps:

[0039] S1. Select the agitator as an auxiliary tool, and carry out disinfection and sterilization treatment on it under the condition of 80-100 degrees Celsius, and add water to it after completion;

[0040] S2. Slowly put the hydroxyethyl cellulose into the mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fireproof energy-storage luminescent coating. The formula comprises the following raw materials in parts by weight: 280-320 parts of water, 1-3 parts of hydroxyethyl cellulose, 3-5 parts of a dispersing agent, 3-5 parts of a water quality stabilizer, 1-3 parts of a defoaming agent, 1-3 parts of a sterilizing agent, 1-3 parts of ethylene glycol, 1-3 parts of a water quality PH regulator, 180-220 parts of styrene-acrylic emulsion, 40-60 parts of elastic emulsion, 0.3-0.7 part of a defoaming agent, 8-12 parts of a coalescing agent, 350-450 parts of flame-retardant coated luminescent powder and 1-5 parts of a thickening agent. The invention also provides a preparation process of the fireproof energy-storage luminescent coating. According to the luminescent material, the styrene-acrylic emulsion is used as an adhesive, so that the coating has relatively high water resistance, heat and humidity resistance and freeze thawing resistance.

Description

technical field [0001] The invention relates to the technical field of preparation of luminous paints, in particular to a fireproof energy storage luminous paint and a preparation process thereof. Background technique [0002] At present, the comprehensive performance of most products on the market is difficult to meet the needs of changing environments, especially the poor weather resistance, which determines the service life and performance of the coating, so enhancing the weather resistance is the top priority of energy storage luminescent coatings. Therefore, we propose a fire-resistant energy-storing luminescent coating. Contents of the invention [0003] The present invention proposes a fire-proof energy-storage luminescent coating and its preparation process to solve the problems raised in the above-mentioned background technology. [0004] The present invention proposes a fire-proof energy-storing luminescent coating, the formula of which is as follows by weight o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/22C09D5/18
CPCC09D125/14C09D5/22C09D5/18C08L2201/02C08L2205/03C08L101/00C08K13/06C08K9/10
Inventor 李伟东
Owner HEBEI JUNHUI SECURITY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap