Health-care mattress and preparation method thereof

A mattress and health care technology, applied in the field of mattresses, can solve the problems of poor air permeability of mattresses, affecting people's sleep, and detrimental to physical health, and achieving appropriate softness and resilience, moderate hardness and extended service life. Effect

Pending Publication Date: 2021-12-10
HEYE HEALTH TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But this EPE foam mattress is too soft, sleep on this mattress for a long time and easily cause symptoms such as lumbar muscle strain, and the air permeability of this mattress is not good, affects people's sleep, is unfavorable for health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Health-care mattress and preparation method thereof
  • Health-care mattress and preparation method thereof
  • Health-care mattress and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Composition of raw materials (parts by weight): 10 parts of modified bamboo charcoal fiber, 100 parts of low-density polyethylene, 5 parts of diatom mud, 2 parts of n-heptane, 0.1 part of triethanolamine, 3 parts of traditional Chinese medicine essential oil, tert-butyl benzoyl peroxide 0.01 part of ester.

[0033] The preparation method of modified bamboo charcoal fiber is as follows:

[0034] S1. Pretreatment: Soak 20g of bamboo charcoal fiber in 0.5wt% NaOH solution for 20min, take it out and wash it;

[0035] S2. The deposition of magnetic nanoparticles: After mixing 100mL 2mol / L ferric chloride and 100mL 1mol / L ferrous chloride solution, add 15g of pretreated bamboo charcoal fiber, stir for 10min, add dropwise 20wt% ammonia solution until the pH is 8. Introduce oxygen, the ventilation rate is 1L / min, control the reaction temperature to 50°C, filter, and after the solid is calcined at 300°C for 3 hours, the bamboo charcoal fiber deposited with magnetic nanoparticle...

Embodiment 2

[0044] Raw material composition (parts by weight): 30 parts of modified bamboo charcoal fiber, 200 parts of low-density polyethylene, 10 parts of diatom mud, 4 parts of n-pentane, 0.2 part of diethanolamine, 5 parts of traditional Chinese medicine essential oil, and 0.02 part of methyl ethyl ketone peroxide.

[0045] The preparation method of modified bamboo charcoal fiber is as follows:

[0046] S1. Pretreatment: Soak 20g of bamboo charcoal fiber in 2wt% NaOH solution for 30min, take it out and wash it;

[0047] S2. Deposition of magnetic nanoparticles: After mixing 100mL 2mol / L ferric chloride and 100mL 1mol / L ferrous chloride solution, add 15g of pretreated bamboo charcoal fiber, stir for 30min, add dropwise 20wt% ammonia solution until the pH is 11. Introduce oxygen, the ventilation rate is 2L / min, control the reaction temperature to 70°C, filter, and after the solid is calcined at 400°C for 4 hours, the bamboo charcoal fiber deposited with magnetic nanoparticles is obtain...

Embodiment 3

[0056] Composition of raw materials (parts by weight): 20 parts of modified bamboo charcoal fiber, 150 parts of low-density polyethylene, 7 parts of diatom mud, 3 parts of petroleum ether, 0.15 parts of polyvinyl alcohol, 4 parts of traditional Chinese medicine essential oil, 0.015 parts of azobisisoheptanonitrile share.

[0057] The preparation method of modified bamboo charcoal fiber is as follows:

[0058] S1. Pretreatment: Soak 20g of bamboo charcoal fiber in 1wt% NaOH solution for 25min, take it out and wash it;

[0059] S2. The deposition of magnetic nanoparticles: After mixing 100mL 2mol / L ferric chloride and 100mL 1mol / L ferrous chloride solution, add 15g of pretreated bamboo charcoal fiber, stir for 20min, add dropwise 20wt% ammonia solution until the pH is 10. Introduce oxygen, the ventilation rate is 1.2L / min, control the reaction temperature to 60°C, filter, and after the solid is calcined at 350°C for 3.5h, the bamboo charcoal fiber deposited with magnetic nanopa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a health-care mattress. The health-care mattress is prepared from the following raw materials in parts by weight: 10-30 parts of modified bamboo charcoal fiber, 100-200 parts of low-density polyethylene, 5-10 parts of diatom ooze, 2-4 parts of a foaming agent, 0.1-0.2 part of a foam stabilizer, 3-5 parts of traditional Chinese medicine essential oil and 0.01-0.02 part of an initiator. The prepared health-care mattress is moderate in hardness, good in bearing performance, excellent in mechanical strength and air permeability, capable of forming a magnetic field beneficial to human health, good in antibacterial, bacteriostatic, anti-mite and deodorant effects and good in health-care effect on a user, and meanwhile the service life of the health-care mattress is prolonged.

Description

technical field [0001] The invention relates to the technical field of mattresses, in particular to a health-care mattress and a preparation method thereof. Background technique [0002] Mattress is an item between the human body and the bed to ensure consumers get a healthy and comfortable sleep. Mattresses are made of various materials, and mattresses made of different materials can bring different sleep effects to people. With the continuous progress of material civilization and technology, the types of mattresses used by modern people are gradually becoming diversified, mainly spring mattresses, palm mattresses, latex mattresses, sponge mattresses and 3D mattresses. Among these mattresses, Spring mattresses account for a larger proportion. [0003] Spring mattresses are mattresses commonly used in modern times with better performance. They have good elasticity, better support and strong air permeability. However, spring mattresses have certain noise during use, and afte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L91/00C08K9/02C08K9/06C08K7/06C08J9/14C08J9/10A61K36/534A61P43/00A47C27/14A47C27/22
CPCC08J9/142C08J9/102C08J9/0061C08J9/0066C08J9/009A61K36/236A61K36/258A61K36/235A61K36/534A61P43/00A47C27/22A47C27/14A61K2236/35A61K2236/51A61K2236/53C08J2203/12C08J2203/04C08J2323/06C08J2491/00A61K2300/00
Inventor 方彦雯方志财
Owner HEYE HEALTH TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap