Low-shrinkage blended wax material and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A low-shrinkage, paraffin-wax technology, applied in the direction of casting and molding equipment, can solve the problems of unstable shrinkage of the product line, difficult to meet precision casting, non-reusable, etc., and achieve good chemical stability, strong applicability, and low-temperature volatilization The effect of low content
Active Publication Date: 2022-01-04
NANJING TIANSHI NEW MATERIAL TECH +1
View PDF12 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] At present, domestic investment casting wax still has problems such as few developed varieties, low output, and poor strength, especially the problem of unstable shrinkage of the product line and non-reusable problems. The above-mentioned technical products have not been solved, and it is difficult to meet the needs of the development of the precision casting industry.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0030] (1) Natural rosin (50 g, 50%) and paraffin wax No. 64 (40 g, 40%) were melted at 100°C.
[0031] (2) In the melted wax liquid, add microcrystalline wax (2g, 2%), Sichuan wax (3g, 3%), polyethylene wax (5g, 5%) and antioxidant 264 (0.1g, 0.1%) ), mixed uniformly in the reactor at 100°C.
[0032] (3) A new type of special blended wax is prepared by steel belt granulation.
Embodiment 2
[0034] (1) Natural rosin (50 g, 50%) and paraffin wax No. 60 (40 g, 40%) were melted at 100°C.
[0035] (2) In the melted wax liquid, add microcrystalline wax (2g, 2%), Sichuan wax (3g, 3%), polyethylene wax (5g, 5%) and antioxidant 264 (0.1g, 0.1%) ), mixed uniformly in the reactor at 100°C.
[0036] (3) A new type of special blended wax is prepared by steel belt granulation.
Embodiment 3
[0038] (1) Polymerized rosin (50 g, 50%) and paraffin wax No. 60 (40 g, 40%) were melted at 100°C.
[0039] (2) In the melted wax liquid, add microcrystalline wax (2g, 2%), Sichuan wax (3g, 3%), polyethylene wax (5g, 5%) and antioxidant 264 (0.1g, 0.1%) ), mixed uniformly in the reactor at 100°C.
[0040] (3) A new type of special blended wax is prepared by steel belt granulation.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
shrinkage
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a low-shrinkage blended wax material and a preparation method thereof, and relates to the technical field of precision investment casting. The preparation method comprises the steps: heating and melting rosin and paraffin, adding a grain refiner, a viscosity modifier, a flexibilizer and a heat stabilizer into liquid wax, placing in a reaction kettle, and uniformly mixing to prepare the novel reusable special blended wax. The special novel blended wax has the advantages of small linear shrinkage rate, small expansion coefficient within softening temperature, low heat capacity, sufficient strength and hardness, small viscosity in a molten state, small residual ash content, low content of low-temperature volatile matters, good chemical stability, fine grain structure, repeated use and the like. The prepared special novel blended wax can meet the size precision requirements and surface quality requirements of various complex precision castings and has wide market application prospects, and meanwhile, the preparation method is simple, low in cost, high in applicability, capable of being repeatedly used and capable of being used for large-scale production.
Description
technical field [0001] The invention relates to the technical field of investment precision casting, in particular to a low shrinkage compounded wax material and a preparation method thereof. Background technique [0002] In more than half a century after World War II, precision casting has experienced rapid development, from the initial use in the manufacture of false teeth and jewelry, to the application in national defense and industrial civilian products. Today, the products made by precision casting are not only used in military and aviation sectors, but also in industries and other sectors that are closely related to the lives of the masses, such as energy, chemical industry, petroleum, textiles, light industry, electronics, transportation, Medical equipment and other departments. [0003] my country's investment casting industry is a relatively slow-growing industry, and there is still a big gap between the precision casting industry of advanced countries in the worl...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.