Moisture-absorption quick-dry antibacterial fabric and preparation method thereof

An antibacterial fabric, moisture-absorbing and quick-drying technology, applied in the field of textiles, can solve problems such as poor moisture absorption and air permeability

Active Publication Date: 2022-03-29
PEAK CHINA CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Solved the disadvantages of poor moisture absorption and air permeability of existing polyester fiber materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Moisture-absorption quick-dry antibacterial fabric and preparation method thereof
  • Moisture-absorption quick-dry antibacterial fabric and preparation method thereof
  • Moisture-absorption quick-dry antibacterial fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] TiO 2 The preparation method of modified polyester comprises the steps:

[0027] (1) Preparation of porous nano-TiO 2 : Add 50g of titanium isopropoxide and 12.5g of dodecyl dimethyl tertiary amine into the reaction flask, mechanically stir evenly, add 1000mL of deionized water, ultrasonically stir, add 7.5g of 30% hydrochloric acid aqueous solution, mechanically stir evenly, heat up to 55°C, keep it warm for 30h, place the filtered residue in an oven, raise the temperature of the oven to 110°C, age for 36h, wash with methanol, and dry in an oven to obtain porous nano TiO 2 ;

[0028] (2) Preparation of TiO 2 Modified polyester: 6g porous nano-TiO 2 , 300g of hydroxyl-terminated polyester, 13.5g of 1,2,3,4-butane tetracarboxylic acid, 9g of acetylacetone, and 2400mL of deionized water were added to the reaction kettle, and mechanically stirred evenly. Continue to heat up to 150°C, keep the temperature for 6 minutes, and get TiO 2 Modified polyester.

Embodiment 2

[0030] TiO 2 The preparation method of modified polyester comprises the steps:

[0031] (1) Preparation of porous nano-TiO 2 : Add 50g of titanium isopropoxide and 18g of dodecyl dimethyl tertiary amine into the reaction flask, mechanically stir evenly, add 1500mL of deionized water, ultrasonically stir, add 15g of 40% hydrochloric acid aqueous solution, mechanically stir evenly, heat up to 60 ℃, heat preservation and rest for 32h, the filter residue obtained by filtration is placed in an oven, the oven is heated to 120°C, aged for 39h, washed with methanol, and dried in an oven to obtain porous nano TiO 2 ;

[0032] (2) Preparation of TiO 2 Modified polyester: 10g porous nano-TiO 2 , 200g of hydroxyl-terminated polyester, 20g of 1,2,3,4-butanetetracarboxylic acid, 12g of acetylacetone, and 2500mL of deionized water were added to the reaction kettle, and mechanically stirred evenly. Continue to heat up to 160°C, keep the temperature for 10 minutes, and get TiO 2 Modified...

Embodiment 3

[0034] TiO 2 The preparation method of modified polyester comprises the steps:

[0035] (1) Preparation of porous nano-TiO 2: Add 50g of titanium isopropoxide and 22.5g of dodecyl dimethyl tertiary amine into the reaction flask, mechanically stir evenly, add 2000mL of deionized water, ultrasonically stir, add 17.5g of 45% hydrochloric acid aqueous solution, mechanically stir evenly, heat up to 65°C, keep it warm for 33h, place the filtered residue in an oven, raise the temperature of the oven to 130°C, age for 42h, wash with methanol, and dry in an oven to obtain porous nano TiO 2 ;

[0036] (2) Preparation of TiO 2 Modified polyester: 12g porous nano-TiO 2 , 200g of hydroxyl-terminated polyester, 28g of 1,2,3,4-butanetetracarboxylic acid, 16g of acetylacetone, and 3000mL of deionized water were added to the reaction kettle, and mechanically stirred evenly. Continue to heat up to 170°C, keep the temperature for 15 minutes, and get TiO 2 Modified polyester.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a moisture-absorption quick-dry antibacterial fabric and a preparation method thereof, and relates to the technical field of textiles. The preparation method comprises the following steps: firstly, preparing porous nano titanium dioxide, crosslinking the porous nano titanium dioxide and polyester by using 1, 2, 3, 4-butanetetracarboxylic acid as a crosslinking agent to obtain TiO2 modified polyester, performing electrostatic spinning on the TiO2 modified polyester to obtain TiO2 modified polyester fibers, and performing double-layer weaving on the TiO2 modified polyester fibers and natural fiber blended yarns to obtain the moisture-absorbing quick-drying antibacterial fabric. According to the invention, porous nano titanium dioxide is grafted with hydroxyl-terminated polyester, so that the fabric has the characteristics of excellent moisture absorption, quick drying and antibacterial property.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a moisture-absorbing and quick-drying antibacterial fabric and a preparation method thereof. Background technique [0002] The human body will secrete a lot of sweat when exercising. Natural fibers (cotton, hemp) have good moisture absorption and air permeability, and provide good thermal and humidity comfort for the wearer when the human body sweats. However, when the human body sweats a lot or When in contact with liquid, the natural fibers absorb moisture and expand, the gaps between the fibers are reduced, and the water transfer rate is reduced, resulting in a decrease in the air permeability of the clothes and adhesion to the skin surface, causing the human body to feel cold and wet. Synthetic fibers have excellent moisture-wicking and quick-drying properties, but synthetic fiber clothing has poor moisture absorption and water absorption properties. The sweat on the surface...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D11/00D03D15/47D03D15/283D03D15/217D03D15/50D03D15/527D01F6/92D01F1/10
CPCD03D11/00D03D15/47D03D15/283D03D15/217D03D15/50D03D15/527D01F6/92D01F1/103D10B2331/04D10B2201/02D10B2201/01D10B2401/13D10B2401/021D10B2501/00Y02A50/30
Inventor 刘文勇
Owner PEAK CHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com