High-temperature-resistant and flame-retardant co-extruded polystyrene foam material and preparation method thereof

A polystyrene foaming and polystyrene technology, which is applied in chemical instruments and methods, layered products, synthetic resin layered products, etc. It is used for problems such as high temperature environment and difficult market promotion, and achieves the effect of low cost, excellent water vapor and low cost

Active Publication Date: 2022-04-12
HUANGSHAN MEISEN NEW MATERIAL TECH
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, due to the lack of high temperature resistance of all-plastic polystyrene foam materials, its surface cannot be used in environments with high temperatures, generally below 100°C. If it is used for outdoor countertops, it will cause traces on the countertop due to focusing in the sun. , seriously affecting performance and appearance
In order to overcome this problem, CN108084625A is made of specially synthesized high-temperature-resistant materials, which can meet the needs of high-temperature resistance, but this product needs to use a large amount of high-temperature-resistant materials, resulting in high costs and difficulty in market promotion
At the same time, since all-plastic foam products are easy to burn, they must meet the requirements of flame retardancy in the process of downstream promotion. Although CN108084588A can meet the requirements of flame retardancy, the cost is too high. and lower cost products is an urgent need for the industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant and flame-retardant co-extruded polystyrene foam material and preparation method thereof
  • High-temperature-resistant and flame-retardant co-extruded polystyrene foam material and preparation method thereof
  • High-temperature-resistant and flame-retardant co-extruded polystyrene foam material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The composition of the core material in parts by mass of the core material of the high temperature resistant and flame retardant co-extruded polystyrene foam material is as follows:

[0029] General purpose polystyrene (GPPS) 60;

[0030] High Impact Polystyrene (HIPS) 16;

[0031] Enhancement aid 5;

[0032] Foaming agent 0.5;

[0033] Antioxidant 0.5;

[0034] UV absorber 0.5;

[0035] Wherein, foaming agent is sodium carbonate; UV absorber is UVP-327; Antioxidant is antioxidant 1010; Strengthening aid is to adopt rock wool fiber, glass fiber, general-purpose polystyrene according to mass ratio 0.15:0.1: 1 Obtained through high-temperature melt extrusion and granulation by twin-screw extruder.

[0036] The surface layer is divided into A material and B material, wherein A material is a composite of polysulfone resin, high impact polystyrene (HIPS), and high molecular weight brominated epoxy resin modification, and the mass parts of the three are respectively It ...

Embodiment 2

[0044] The raw material mass parts composition of described core material is as follows:

[0045] General purpose polystyrene (GPPS) 70;

[0046] High Impact Polystyrene (HIPS) 19;

[0047] Enhancement aid 8;

[0048] Blowing agent 1;

[0049] Antioxidant 0.9;

[0050] UV absorber 1;

[0051] The surface layer is divided into A material and B material, wherein A material is a composite of polysulfone resin, high impact polystyrene (HIPS), and high molecular weight brominated epoxy resin modification, and the mass parts of the three are respectively It is 79 parts of polysulfone resin; 9 parts of high impact polystyrene (HIPS); 15 parts of high molecular weight brominated epoxy resin modification; consumption is 5% of core material; B material is pure polysulfone resin, The dosage is 8% of material A.

[0052] Other conditions are identical with embodiment 1.

Embodiment 3

[0054] The raw material mass parts composition of described core material is as follows:

[0055] General purpose polystyrene (GPPS) 64;

[0056] High Impact Polystyrene (HIPS) 17;

[0057] Enhancement aid 7;

[0058] Foaming agent 0.8;

[0059] Antioxidant 0.8;

[0060] UV absorber 0.8;

[0061] The surface layer is divided into A material and B material, wherein A material is a composite of polysulfone resin, high impact polystyrene (HIPS), and high molecular weight brominated epoxy resin modification, and the mass parts of the three are respectively It is 75 parts of polysulfone resin; 8 parts of high impact polystyrene (HIPS); 15 parts of high molecular weight brominated epoxy resin modification; consumption is 5% of core material; B material is pure polysulfone resin, The dosage is 10% of material A.

[0062] Other conditions are identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-temperature-resistant and flame-retardant co-extruded polystyrene foam material, which is divided into a surface layer and a core material, the core material is mainly prepared by carrying out extrusion granulation on general polystyrene (GPPS), high impact polystyrene (HIPS), an antioxidant, a foaming agent and the like as raw materials and finally carrying out co-extrusion molding with the surface layer, the surface layer is divided into a material A and a material B, the material A is obtained by compounding polysulfone, high impact polystyrene (HIPS) and a brominated epoxy resin modifier, and the material B is pure polysulfone resin. The bonding capacity of the surface layer and the core material of the obtained material is extremely high, and the stripping phenomenon is avoided; the finally obtained composite material has excellent high-temperature resistance, can be used in an environment of 150 DEG C without obvious change, and the surface layer has a relatively strong flame-retardant function.

Description

technical field [0001] The invention belongs to the technical field of polystyrene foamed materials, and in particular relates to a high-temperature-resistant, flame-retardant co-extruded polystyrene foamed material and a preparation method thereof. Background technique [0002] Imitation wood materials refer to building materials that can achieve imitation wood effects, aiming to replace real wood in order to save forest resources. Imitation wood materials can be divided into traditional imitation wood materials and advanced wood imitation materials: traditional imitation wood materials are mostly made of cement, and the imitation wood effect is formed by sealing or carving on its surface, but usually only imitates the external effect; The wood material is made by modern plastic processing technology, which can not only imitate the external decorative effect of real wood, but also simulate its performance, texture and even smell. Among the commonly used advanced wood-like ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B5/18B32B27/28B32B27/06B32B27/30B32B27/18C08L25/06C08L51/04C08K7/12C08K7/14C08J9/08C08L81/06C08L63/00B29C48/18B29C48/92
Inventor 盛岳金赵小亮焦采之
Owner HUANGSHAN MEISEN NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com