Vibrating diaphragm material and preparation process thereof

A film material and film glue technology, applied in the field of diaphragm materials, can solve the problems of heavy metal diaphragm, poor damping characteristics, difficult unit drive and control, etc., to achieve maximum improvement, improve frequency response, and increase driving volume Effect

Pending Publication Date: 2022-04-15
CYBRID TECHNOLOGIES INC
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The metal diaphragm is relatively heavy, and the damping characteri

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vibrating diaphragm material and preparation process thereof
  • Vibrating diaphragm material and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～4

[0023] Embodiments 1 to 4: A vibrating membrane material, including a vibrating membrane coating and a substrate layer, the vibrating membrane coating is formed by coating the vibrating membrane glue, and the vibrating membrane glue consists of the following components in parts by weight Composition, as shown in Table 1:

[0024] Table 1

[0025]

[0026] In Example 1, the antioxidant is selected from antioxidant 1010, the above-mentioned lubricant is selected from castor oil, the thickness of the above-mentioned substrate layer is 15 μm, and the thickness of the diaphragm coating is 15 μm.

[0027] In Example 2, the antioxidant is selected from antioxidant 2246, the above-mentioned lubricant is selected from stearic acid amide, the thickness of the above-mentioned substrate layer is 50 μm, and the thickness of the diaphragm coating is 25 μm.

[0028] In Example 3, the antioxidant is selected from antioxidant 2246, the above-mentioned lubricant is selected from diethyltolu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The vibrating diaphragm material comprises a vibrating diaphragm coating and a base material layer, and the vibrating diaphragm coating is formed by coating a vibrating diaphragm glue solution. The vibrating diaphragm glue solution is prepared from the following components in parts by weight: 50 to 80 parts of acrylic resin, 25 to 35 parts of polyethylene resin, 10 to 15 parts of ethylene propylene rubber, 3 to 5 parts of diethylene glycol monohexyl ether, 3 to 8 parts of isopropyl triphenyl phosphate, 15 to 20 parts of glass fiber, 1 to 3 parts of antioxidant, 1 to 5 parts of lubricant, 1 to 5 parts of 2-methyl-5-amino-N-ethyl benzenesulfonyl aniline and 100 parts of solvent. According to the diaphragm material disclosed by the invention, the diethylene glycol monohexyl ether and the isopropyl triphenyl phosphate are added into the acrylic resin, the polyethylene resin and the ethylene propylene rubber, so that the maximum pushing volume of a loudspeaker is increased and can be increased by 39% to the maximum; and the frequency response of the loudspeaker is improved and can be increased by 10dB at most.

Description

technical field [0001] The invention belongs to the technical field of diaphragm materials, and in particular relates to a diaphragm material and a preparation process thereof. Background technique [0002] The properties of the loudspeaker diaphragm material affect the sound quality. Common materials for diaphragms are: paper cones, synthetic plastics, and high-cost titanium diaphragms. [0003] At present, the paper cone manufacturing method is to pour the pulp into the designed mold, and then perform a series of subsequent processing after drying to form our common speaker unit diaphragm. The plastic diaphragm involves the electroplating process, and there is a certain amount of environmental pollution. The smelted alloy metal used in the metal diaphragm has certain toxicity and is difficult to recycle, which is harmful to the human body. [0004] Due to the characteristics of the material, the cone diaphragm is sensitive to changes in temperature and humidity. Changes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H04R7/02H04R31/00
Inventor 王少星张英泉
Owner CYBRID TECHNOLOGIES INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap