Composite material with matte effect and preparation method thereof
A composite material and matte powder technology, applied in the field of composite material and its preparation, can solve the problems of uneven gloss distribution, performance deterioration, high energy consumption, achieve uniform and fine matte, reduce processing temperature, and simple preparation process. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0029] The preparation method of the composite material with matte effect comprises the following steps:
[0030] Weigh the PC resin, the ABS resin, the matte powder and the antioxidant according to the formula and premix them in a high-speed mixer for 5-10min to obtain the premix;
[0031] The premix is added into a twin-screw extruder for extrusion granulation to obtain the composite material.
[0032] Further, the temperature of the twin-screw extruder is set as: 200-210 ℃ in zone 1, 210-220 ℃ in zone 2, 210-220 ℃ in zone 3, 210-220 ℃ in zone 4, 210-220 ℃ in zone 5, 210-220 ℃ in zone 6, 210-220 ℃ in zone 7, 210-220 ℃ in Zone 8, 210-220 ℃ in zone 9, 210-220 ℃ in zone 10 and 220-230 ℃ in head.
[0033] Further, the screw speed is 300-400r / min, and the screw length diameter ratio of the twin-screw extruder is 40-50.
[0034] Further, during the later sample preparation, the temperature of the injection molding machine is set as: 220-230 ℃ in zone I, 230-240 ℃ in zone II, 230-240...
Example
[0035] Examples 1-9 and comparative examples 1-4:
Example Embodiment
[0036] Example 1:
[0037] In this embodiment, the formula of the composite material (unit:%) is shown in Table 1. The preparation method of the composite material includes the following steps:
[0038] Weigh 67.8% of the PC resin, 30% of the ABS resin, 2% of the matte powder and 0.2% of the antioxidant, and premix in a high-speed mixer for 5 minutes to obtain the premix;
[0039] The composite material is obtained by adding the premix to the twin-screw extruder for extrusion granulation.
[0040] The temperature of the twin-screw extruder is set as: 210 ℃ in the first zone, 220 ℃ in the second zone, 220 ℃ in the third zone, 220 ℃ in the fourth zone, 220 ℃ in the fifth zone, 220 ℃ in the sixth zone, 220 ℃ in the seventh zone, 220 ℃ in the eighth Zone, 220 ℃ in the ninth zone, 220 ℃ in the tenth zone and 230 ℃ in the head. The screw speed is 350r / min, and the screw length diameter ratio of twin-screw extruder is 1:44. During sample preparation, the temperature of the injection mo...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap