Antibacterial composite fabric and preparation method thereof
A composite fabric and composite technology, applied in the field of fabric antibacterial, can solve the problems of poor performance, antibacterial performance, light stability, insufficient high temperature stability, weak antibacterial performance, etc., to improve breaking strength and tear strength, antibacterial performance. Remarkable performance and improved antibacterial properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0045] S1: weigh by weight 2 parts of 5-tert-butylisophthalic acid, 30 parts of N,N-dimethylacetamide, 3 parts of hydrated copper acetate, 30 parts of methanol, 1.3 parts of leucine, PAA 1.3 parts, 5 parts magnesium borate, 0.7 parts manganese dioxide and 0.7 parts iron oxide;
[0046] S2: Dissolve 5-tert-butylisophthalic acid in N,N-dimethylacetamide to obtain A solution, dissolve N,N-dimethylacetamide with hydrated copper acetate to obtain B solution, then mix A and N-dimethylacetamide Mix B evenly to obtain solution C;
[0047] S3: dissolve PAA with ethanol, then add the dissolved PAA solution in the C solution prepared by S2 to obtain D solution;
[0048] S4: mix the D solution, magnesium borate, manganese dioxide and leucine evenly, pour it into the emulsifying machine, the emulsifying machine rotating speed is 2000r / min, the temperature is 80 ℃, and the reaction time is 1h to obtain the E solution;
[0049] S5: pour the iron oxide into the E solution in the emulsifying...
Embodiment 2
[0057] S1: weigh 0.2 part of 5-tert-butylisophthalic acid, 10 parts of N,N-dimethylacetamide, 0.2 part of hydrated copper acetate, 2 parts of methanol, 0.8 part of leucine, 0.8 part of PAA, 2 parts of magnesium borate, 0.5 part of manganese dioxide and 0.5 part of iron oxide;
[0058] S2: Dissolve 5-tert-butylisophthalic acid in N,N-dimethylacetamide to obtain solution A, dissolve N,N-dimethylacetamide with hydrated copper acetate to obtain solution B, then mix A and N-dimethylacetamide Mix B evenly to obtain solution C;
[0059] S3: dissolve PAA with ethanol, then add the dissolved PAA solution in the C solution prepared by S2 to obtain D solution;
[0060] S4: mix the D solution, magnesium borate, manganese dioxide and leucine evenly, pour it into the emulsifying machine, the emulsifying machine rotating speed is 500r / min, the temperature is 50 ℃, and the reaction time is 0.1h to obtain the E solution;
[0061] S5: pour the iron oxide into the E solution in the emulsifying...
Embodiment 3
[0069] S1: weigh 5 parts by weight of 5-tert-butylisophthalic acid, 50 parts of N,N-dimethylacetamide, 5 parts of hydrated copper acetate, 50 parts of methanol, 2 parts of leucine, PAA2 parts, 10 parts magnesium borate, 1 part manganese dioxide and 3 parts iron oxide;
[0070] S2: Dissolve 5-tert-butylisophthalic acid in N,N-dimethylacetamide to obtain solution A, dissolve N,N-dimethylacetamide with hydrated copper acetate to obtain solution B, then mix A and N-dimethylacetamide Mix B evenly to obtain solution C;
[0071] S3: dissolve PAA with ethanol, then add the dissolved PAA solution in the C solution prepared by S2 to obtain D solution;
[0072] S4: mix the D solution, magnesium borate, manganese dioxide and leucine evenly, pour it into the emulsifying machine, the emulsifying machine rotating speed is 5000r / min, the temperature is 100 ℃, the reaction time is 2h, obtains the E solution;
[0073] S5: pour the iron oxide into the E solution in the emulsifying machine, the...