Alkaline-earth heat-resistant magnesium alloy ingot preparation process

A preparation process and technology for magnesium alloys, applied in the field of magnesium alloy production, can solve the problems of difficult preparation process and high cost of preparation process

Pending Publication Date: 2022-07-01
惠州云海镁业有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Based on this, it is necessary to provide an alkaline earth heat-resistant magnesium alloy ingot preparation process for the technical problems of high cost and difficult preparation process of magnesium alloys in the prior art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alkaline-earth heat-resistant magnesium alloy ingot preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] In order to make the above objects, features and advantages of the present invention more clearly understood, the specific embodiments of the present invention will be described in detail below with reference to the accompanying drawings. In the following description, numerous specific details are set forth in order to provide a thorough understanding of the present invention. However, the present invention can be implemented in many other ways different from those described herein, and those skilled in the art can make similar improvements without departing from the connotation of the present invention. Therefore, the present invention is not limited by the specific embodiments disclosed below.

[0029] In the description of the present invention, it should be understood that the terms "center", "longitudinal", "lateral", "length", "width", "thickness", "upper", "lower", "front", " Back, Left, Right, Vertical, Horizontal, Top, Bottom, Inner, Outer, Clockwise, Countercl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation process of an alkaline earth heat-resistant magnesium alloy ingot, which belongs to the technical field of magnesium alloy production technology, and comprises the following steps: firstly preparing a talcum powder coating, a zinc oxide coating, a covering agent and a refining agent, and then adding the covering agent in the process of smelting a magnesium ingot and an aluminum ingot to control the smelting stability; next, introducing Mn element by using Al-10% Mn intermediate alloy, then adding zinc ingots, next, wrapping Mg-30% Ca by using aluminum foil, then adding the wrapped Mg-30% Ca into alloy liquid, and then adding a refining agent so as to control the refining process; and after refining is completed, pouring is conducted in a mold preheated to 200 DEG C, and a magnesium alloy ingot can be obtained after pouring is completed. The technical problems that in the prior art, a magnesium alloy preparation technology is high in cost and difficult are solved.

Description

technical field [0001] The invention relates to the technical field of magnesium alloy production technology, in particular to a preparation process of an alkaline earth heat-resistant magnesium alloy ingot. Background technique [0002] Magnesium alloys have the advantages of low density, high specific strength and specific stiffness, high electrical and thermal conductivity, excellent damping and shock absorption properties and electromagnetic shielding properties, good casting and machining properties, and easy recycling. Therefore, it has broad application prospects in aerospace, automobile manufacturing, home appliance instruments, electronic communications and other fields, and has become a very important modern industrial material. Mg-Al based alloys are the most widely used magnesium alloys due to their good die casting, machining, mechanical properties, low density, high specific strength and specific stiffness. In recent years, the requirements of energy saving, e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C1/03C22C1/06C22C23/04B22D7/00
CPCC22C1/03C22C1/06C22C23/04B22D7/005
Inventor 巩绪平汪剑袁伟强
Owner 惠州云海镁业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com